Incontinence underwear with inner mat
A technology for incontinence trousers and underwear, applied in bandages, absorbent pads, medical science and other directions, can solve the problems of high cost, high consumption of raw materials, inability to be repeatedly washed and reused, etc. The effect of the side leak effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037] Knitted fabrics, woven fabrics, needle-punched fabrics, and membranes are overlocked to form an inner pad and sewn into underwear to form a kind of incontinence pants with an inner pad. The specific process is as follows:
[0038] (1) Preparation of the surface layer: using spinning technology, the Kapron copper ion fiber with a specification of 38mm 2.5D and the polyester fiber with a specification of 51mm 2D are spun into a yarn with a count of 40S at a ratio of 20%:80% After being made into knitted fabric, the surface density is 210g / m 2 ;
[0039] (2) Preparation of the diversion layer: the polyester fiber with a specification of 40mm 5D is spun into yarn by spinning technology, and the warp yarn with a fineness of 75D and the weft yarn with a fineness of 60D are made into a yarn with a warp density of 100 by using a weaving technology. Roots / 10cm, woven fabric with a weft density of 90 threads / 10cm, forming the diversion layer, with an area density of 37g / m 2 . ...
Embodiment 2
[0044] Knitted fabrics, woven fabrics, needle-punched fabrics, and membranes are overlocked to form an inner pad and sewn into underwear to form a kind of incontinence pants with an inner pad. The specific process is as follows:
[0045] (1) Preparation of the surface layer: using spinning technology, the Kapron copper ion fiber with a specification of 38mm 2.5D and the polyester fiber with a specification of 51mm 2D are spun into a yarn with a count of 40S at a ratio of 20%:80% After being made into knitted fabric, the surface density is 210g / m 2 ;
[0046] (2) Preparation of the diversion layer: the polyester fiber with a specification of 40mm 5D is spun into yarn by spinning technology, and the warp yarn with a fineness of 75D and the weft yarn with a fineness of 60D are made into a yarn with a warp density of 100 by using a weaving technology. Roots / 10cm, woven fabric with a weft density of 90 threads / 10cm, forming the diversion layer, with an area density of 37g / m 2 ; ...
Embodiment 3
[0052] Knitted fabrics, woven fabrics, needle-punched fabrics, and films are overlocked to form an inner pad and sewn into underwear to form a kind of incontinence pants with an inner pad. The specific process is as follows:
[0053] (1) Preparation of the surface layer: using spinning technology, the Kapron copper ion fiber with a specification of 38mm 2.5D and the polyester fiber with a specification of 51mm 2D are spun into a yarn with a count of 40S at a ratio of 20%:80% After being made into knitted fabric, the surface density is 210g / m 2 ;
[0054] (2) Preparation of the diversion layer: the polyester fiber with a specification of 40mm 5D is spun into yarn by spinning technology, and the warp yarn with a fineness of 75D and the weft yarn with a fineness of 60D are made into a yarn with a warp density of 100 by using a weaving technology. Roots / 10cm, woven fabric with a weft density of 90 threads / 10cm, forming the diversion layer, with an area density of 37g / m 2 ;
[0...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com