Low-linear thermal expansion coefficient, flocking effect polypropylene composite material and preparation method thereof
A technology of thermal expansion coefficient and composite material, which is applied in the field of low linear thermal expansion coefficient, flocking-like polypropylene composite material and its preparation field, can solve the problems of easy warping and deformation of parts, affecting the appearance of parts, cumbersome processing process, etc. Achieve the effect of reducing post shrinkage and linear thermal expansion coefficient, improving comprehensive performance, and simple preparation process
Inactive Publication Date: 2018-06-01
CHONGQNG PRET NEW MATERIAL +4
View PDF6 Cites 9 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the processing process of this kind of method is cumbersome, and the parts are easy to warp and deform. At the same time, the glass fiber is easy to be exposed, which affects the appearance of the part.
There are also patents to reduce the linear thermal expansion coefficient of co
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] The main components of the polypropylene composite material of the present invention include 80.6% polypropylene, 5% talc, 5% acicular wollastonite, 0.5% cellulose, 5% elastomer, 0.5% compatibilizer, 0.1% antioxidant 3314 , 0.1% antioxidant DSTP and 0.2% secondary antioxidant 168 and 2% other additives.
Embodiment 2
[0034] The main components of the polypropylene composite material of the present invention include 72.6% polypropylene, 5% talc, 10% acicular wollastonite, 1.0% cellulose, 8% elastomer, 1.0% compatibilizer, 0.1% antioxidant 3314 , 0.1% antioxidant DSTP and 0.2% secondary antioxidant 168 and 2% other additives.
Embodiment 3
[0036] The main components of the polypropylene composite material of the present invention include 67.6% polypropylene, 5% talc, 15% acicular wollastonite, 1.0% cellulose, 8% elastomer, 1.0% compatibilizer, 0.1% antioxidant 3314 , 0.1% antioxidant DSTP and 0.2% secondary antioxidant 168 and 2% other additives.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more Abstract
The invention discloses a low linear thermal expansion coefficient, a flocking effect polypropylene composite material and a preparation method thereof. The polypropylene composite material is prepared from the following raw materials in percentage by weight: 45 to 90 of polypropylene, 0 to 15 of talc powder, 5 to 15 of acicular wollastonite, 0.2 to 5 of cellulose, 1 to 15 of elastomer, 0.5 to 2 of compatilizer, 0.1 to 1 of antioxidant, 0 to 2 of other additives. According to the low linear thermal expansion coefficient, the flocking effect polypropylene composite material and the preparationmethod thereof, high aspect ratio acicular wollastonite and the cellulose are adopted to replace part or all of the talc powder for compounding and filling, and are added into an extruder through a side feeding method, so that the structures of the acicular wollastonite and the cellulose are maintained farthest, the post-shrinkage and linear thermal expansion coefficient of the composite materialare greatly reduced, a stronger plastic feel of the composite material is improved, and the material has a flocking effect, can be widely used in automotive interior trim parts such as automotive pillars, door panels, and instrument panels.
Description
technical field [0001] The invention relates to a polypropylene composite material, in particular to a polypropylene composite material with low linear thermal expansion coefficient and imitation flocking effect and a preparation method thereof. It is a polypropylene composite material with simple process and low cost, and has a relatively low It has the advantages of linear thermal expansion coefficient and excellent imitation flocking effect, and the comprehensive performance of the composite material is excellent. It can be widely used in the field of automotive interior parts such as odor pillars, door panels and instrument panels, and belongs to the field of polymer modification and processing technology. Background technique [0002] Polypropylene is widely used in industries such as automotive interior and exterior trims, household appliances and electronic components because of its good molding performance, excellent oil resistance and chemical resistance, light weigh...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more IPC IPC(8): C08L23/14C08L1/02C08L23/08C08L51/06C08K13/04C08K7/10C08K3/34B29C47/92B29B9/06B29C48/92
Inventor 付武昌蔡青周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap