Periodontitis gel containing hyaluronic acid and preparation method thereof

A technology of hyaluronic acid and sodium hyaluronate, which is applied in the field of medicine, can solve the problems of short retention time, limited application, and easy biodegradation of natural sodium hyaluronate, and achieve the effect of promoting regeneration, repair and healing

Inactive Publication Date: 2018-06-29
NANJING TZONE BIOLOGICAL SCI & TECH
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Natural sodium hyaluronate is easily biodegradable, has a short residence time in the organism, and its hardness and mechanical strength are not large enough, which limits its clinical application and requires chemical modification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Periodontitis gel containing hyaluronic acid and preparation method thereof
  • Periodontitis gel containing hyaluronic acid and preparation method thereof
  • Periodontitis gel containing hyaluronic acid and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A periodontitis gel containing hyaluronic acid, comprising the following components in mass percentage: sodium hyaluronate derivatives (0.5%), enzyme-cleaved oligomeric hyaluronate sodium (0.5%), glycerin (5%), honeysuckle Water Extract (3%), Recombinant Human Bone Morphogenetic Protein (rhBMP-2) (0.08%), Basic Fibroblast Growth Factor (b-FGF) (0.06%), Pentylene Glycol (0.03%), Caprylyl Glycol (0.02%), methylparaben (0.1%), and purified water were added to 100%.

[0029] The molecular weight of small molecular weight sodium hyaluronate is 9000Da.

[0030] The preparation method of the periodontitis gel containing hyaluronic acid comprises the following steps:

[0031] (1) Preparation of sodium hyaluronate derivatives.

[0032] (2) Mix sodium hyaluronate derivatives and sodium hyaluronate with an appropriate amount of water, soak at room temperature, homogenize for 3 minutes, and stir at a speed of 300 r / min for 30 minutes to fully swell and disperse evenly, as compone...

Embodiment 2

[0038] A periodontitis gel containing hyaluronic acid, comprising the following components in mass percentage: sodium hyaluronate derivatives (0.8%), enzyme-cleaved oligomeric hyaluronate sodium (0.4%), glycerin (10%), honeysuckle Water extract (2%), recombinant human bone morphogenic protein (rhBMP-2) (0.06%), basic fibroblast growth factor (b-FGF) (0.1%), pentanediol (0.03%), octanediol (0.03%), methylparaben (0.2%), and purified water were added to 100%.

[0039] The molecular weight of small molecular weight sodium hyaluronate is 7000Da.

[0040] The preparation method of the periodontitis gel containing hyaluronic acid comprises the following steps:

[0041] (1) Preparation of sodium hyaluronate derivatives.

[0042](2) Mix sodium hyaluronate derivatives and sodium hyaluronate with an appropriate amount of water, soak at room temperature, homogenize for 3 minutes, and stir at a speed of 300 r / min for 30 minutes to fully swell and disperse evenly, as component 1;

[004...

Embodiment 3

[0048] A periodontitis gel containing hyaluronic acid, comprising the following components in mass percentage: sodium hyaluronate derivatives (1.2%), enzyme-cleaved oligomeric hyaluronate sodium (0.3%), glycerin (12%), honeysuckle Water extract (4%), recombinant human bone morphogenic protein (rhBMP-2) (0.15%), basic fibroblast growth factor (b-FGF) (0.1%), pentanediol (0.02%), octanediol (0.04%), methylparaben (0.15%), and purified water were added to 100%.

[0049] The molecular weight of small molecular weight sodium hyaluronate is 5000Da.

[0050] The preparation method of the periodontitis gel containing hyaluronic acid comprises the following steps:

[0051] (1) Preparation of sodium hyaluronate derivatives.

[0052] (2) Mix sodium hyaluronate derivatives and sodium hyaluronate with an appropriate amount of water, soak at room temperature, homogenize for 3 minutes, and stir at a speed of 300 r / min for 30 minutes to fully swell and disperse evenly, as component 1;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to periodontitis gel containing hyaluronic acid and a preparation method thereof. The periodontitis gel is prepared from the following ingredients in mass percent: 0.1% to 1.5% of sodium hyaluronate derivative, 0.05% to 1.0% of enzyme-digested oligomerized sodium hyaluronate, 5% to 15% of glycerinum, 1.5% to 4.5% of honeysuckle flower aqueous extractive, 0.02% to 0.2% of recombinant human bone morphogenetic protein-2 (rhBMP-2), 0.02% to 0.2% of base fibroblast growth factor (b-FGF), 0.02% to 0.04% of pentanediol, 0.02% to 0.04% of octylene glycol, 0.1% to 0.3% of methylparaben and purified water added to 100%. The gel disclosed by the invention can be applied to treating gingivitis and periodonititis and has an obvious treating effect.

Description

technical field [0001] The invention relates to a periodontitis gel containing hyaluronic acid and a preparation method thereof, belonging to the field of medicine. Background technique [0002] Periodontitis refers to chronic inflammation that occurs in the gums, periodontal ligament, cementum, and alveolar bone. Most cases develop from long-standing gingivitis, forming periodontal pockets and alveolar bone absorption symptoms. Due to the slow course of the disease, the early symptoms do not cause obvious pain, and patients often do not seek medical treatment in time. The longer the inflammation, the damage to the supporting tissue will gradually increase, which will eventually lead to the loss of teeth, and at the same time become an important cause of pathological changes in other organs and tissues of the body. potential risk factors. It is listed by the World Health Organization as one of the three major diseases that endanger human health. Periodontitis not only inte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K38/18A61K9/06A61P1/02A61K36/355A61K31/728
CPCA61K9/006A61K9/06A61K31/728A61K36/355A61K38/1825A61K38/1875A61K2236/331A61K2236/39A61K2236/51A61K2300/00
Inventor 金玉
Owner NANJING TZONE BIOLOGICAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com