A kind of preparation method of alkoxy-terminated polydimethylsiloxane

A technology of hydroxyl-terminated polydimethylsiloxane and dimethylsiloxane, which is applied in the field of preparation of alkoxy-terminated polydimethylsiloxane, and can solve the problem of harsh conditions, long reaction time, sealant Performance changes and other issues, to achieve the effect of easy operation and control, reduce the yield of reactants, and mild reaction conditions

Active Publication Date: 2019-04-19
HANGZHOU ZHIJIANG SILICONE CHEM +1
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor storage performance of dealcoholized room temperature silicone rubber produced by hydroxyl-terminated polydimethylsiloxane, the general shelf life is only 6 to 9 months, which greatly restricts the circulation and development of dealcoholized room temperature silicone rubber.
In order to improve the storability of dealcoholized room temperature silicone rubber, the effect of formula improvement is not only limited, but also the application is limited due to the change of sealant performance due to the introduction of various active additives
The method of obtaining alkoxy-terminated polydimethylsiloxane through alkoxy-terminated hydroxyl-terminated polydimethylsiloxane can effectively improve the storage period to more than 12 months, but the general reaction process The conditions are harsh, the reaction time is long, the catalyst cannot be reused, and the cost increases and other reasons are also slow.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] According to the molar ratio of 1:2.1:5, respectively weigh the hydroxyl-terminated polydimethylsiloxane and methyl orthosilicate (Si(OCH 3 ) 4 ) and dimethylamine, added to the reactor, and reacted at 35°C for 60 minutes; then depressurized to -0.05 MPa and heated to 90°C, and continued to react for 30 minutes; then depressurized to -0.1 MPa and heated to 110°C , and continue the reaction to remove the low boiling for 60 minutes to obtain the product alkoxy-terminated polydimethylsiloxane.

[0030] Detect the prepared alkoxypolydimethylsiloxane: take a certain amount of the product alkoxy-terminated polydimethylsiloxane, add tetrabutyl titanate with a mass content of 1.5%, and pass through the flow The viscosity change of the polydimethylsiloxane before and after the reaction is measured by a variable instrument is less than 10%, indicating that the capping ratio is greater than 85%, which meets the requirements for the preparation of alcohol-type sealant with a long ...

Embodiment 2

[0033] According to the molar ratio of 1: 2.2: 5, respectively weigh the hydroxyl-terminated polydimethylsiloxane and tetraethyl orthosilicate (Si(OC 2 h 5 ) 4 ) and diethylamine, added to the reactor, and reacted at 50°C for 50 minutes; then depressurized to -0.05 MPa and heated to 90°C, and continued to react for 25 minutes; then depressurized to -0.1 MPa and heated to 110°C , and continue the reaction to remove the low boiling point for 75 minutes to obtain the product alkoxy-terminated polydimethylsiloxane.

[0034] Detect the prepared alkoxypolydimethylsiloxane: take a certain amount of the product alkoxy-terminated polydimethylsiloxane, add tetrabutyl titanate with a mass content of 1.5%, and pass through the flow The viscosity change of the polydimethylsiloxane before and after the reaction is measured by a variable instrument is less than 10%, indicating that the capping ratio is greater than 85%, which meets the requirements for the preparation of alcohol-type seala...

Embodiment 3

[0037] According to the molar ratio of 1:2.3:5, respectively weigh the hydroxyl-terminated polydimethylsiloxane and orthophenylsilicate (Si(OC 5 h 6 ) 4 ) and pyrrolidine were added to the reactor, and reacted at 85°C for 30 minutes; then depressurized to -0.05 MPa and heated to 110°C, and continued to react for 15 minutes; then depressurized to -0.1 MPa and heated to 120°C, Continue the reaction to remove the low boiling point for 90 minutes to obtain the product alkoxy-terminated polydimethylsiloxane.

[0038] Detect the prepared alkoxypolydimethylsiloxane: take a certain amount of the product alkoxy-terminated polydimethylsiloxane, add tetrabutyl titanate with a mass content of 1.5%, and pass through the flow The viscosity change of the polydimethylsiloxane before and after the reaction is measured by a variable instrument is less than 10%, indicating that the capping ratio is greater than 85%, which meets the requirements for the preparation of alcohol-type sealant with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of organic silicon polymers and in particular relates to a preparation method of alkoxy-terminated polydimethylsiloxane. Compared with an existing alkoxy terminationmethod, the preparation method of the alkoxy-terminated polydimethylsiloxane, provided by the invention, has the following technical effects that in step (1), the initial temperature (35 to 85 DEG C)is relatively low, reaction conditions are moderate and pressurizing or decompression operation is not needed; the total reaction time of the provided preparation method is less than 3h and the operation of all steps are simple and moderate to operate, so that safety production is facilitated, and efficient production of an alkoxy-terminated polydimethylsiloxane product is also realized at the same time; one of dimethylamine, diethylamine, dipropylamine, methyl ethylamine and pyrrolidine is used as a catalyst; the termination rate of the prepared alkoxy-terminated polydimethylsiloxane is high; the catalyst can be recycled and repeatedly utilized through a decompression distillation and rectification manner.

Description

technical field [0001] The invention belongs to the field of organosilicon polymers, in particular to a preparation method of alkoxy-terminated polydimethylsiloxane. Background technique [0002] Due to its superior weather resistance, extremely wide elastic temperature range, excellent flame retardancy and high cost performance, room temperature vulcanized silicone rubber is widely used in structural assembly and non-structural assembly joint sealing of exterior walls of construction projects, and Various waterproof seals for interior decoration. [0003] At present, RTV silicone rubber on the market is mainly divided into three types: deacidification type, deketoxime type and dealcoholization type. During the vulcanization process, acetic acid, butanone oxime and alcohols are removed respectively. Acetic acid has strong biological irritation, butanone oxime has certain biological toxicity, and alcohols show better biological friendliness. Therefore, the amount of dealcoho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G77/38
CPCY02P20/584
Inventor 李超张原志成刘明何永富沈翔
Owner HANGZHOU ZHIJIANG SILICONE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com