Ru porcelain retro glaze and production method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and technique of Ru porcelain, applied in clay products, other household utensils, applications, etc., to achieve the effect of improving the strong texture of glass
Inactive Publication Date: 2018-09-04
刘冬青
View PDF5 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0009] Aiming at the problem that the surface gloss of modern Ru porcelain is strong, glass luster, and the glaze color obtained by phase separation is bluish, which is quite different from ancient Ru porcelain. After years of repeated research and development, the Holly glaze has been successfully developed. The invention uses a special glaze, and the holly glaze prepared through a unique firing process breaks through the modern glass glaze glaze and firing process, showing the true color of Ru porcelain and achieving a retro effect
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0033] A kind of ancient glaze for Ru porcelain, which is composed of the following raw materials in weight percentage: 18.8% potassium feldspar, 5% calcite, 12% plant ash, 13.5% yellow feldspar, 12% black stone, 2% bone ash, 5.7% golden soil, 14% dolomite %, talc 3%, agate 11%, kaolin 3%.
[0034] The above is the basic implementation mode of the present invention, further improvement, perfection and limitation can be made on the basis of the above: the potassium feldspar is medical stone.
[0035] The above is the basic implementation mode of the present invention, and further improvements, perfections and limitations can be made on the basis of the above: the ashes described are bovine or sheep ashes.
[0036] The preparation method of the present invention is:
[0037] Step 1: crush the above-mentioned raw materials, pass through a 20-mesh sieve, mix according to weight percentage, and set aside;
[0038] Step 2: Put the spare mixed material in step 1 into the ball mill,...
Embodiment 2
[0054] A kind of ancient glaze for Ru porcelain, which is composed of the following raw materials in weight percentage: 18.8% potassium feldspar, 5% calcite, 12% plant ash, 13.5% yellow feldspar, 12% black stone, 2% bone ash, 5.7% golden soil, 14% dolomite %, talc 3%, agate 11%, kaolin 3%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention provides Ru porcelain retro glaze and a production method thereof. The Ru porcelain retro glaze comprises the following components as raw materials in percent by weight: 18.8% of potassium feldspar, 5% of calcite, 12% of plant ash, 13.5% of melilite, 12% of black stone, 2% of bone ash, 5.7% of golden soil, 14% of dolomite, 3% of talc, 11% of agate and 3% of kaolin. The green glaze produced by the invention is as gentle as jade, dignified and restrained in texture, and improves the current situation of a strong glass texture of a modern Ru porcelain glaze layer; through a unique glaze formula, by a retro firing method, the glazed surface shows a crystallization effect, the Ru porcelain is as gentle as jade, dignified and restrained, and a retro effect is achieved; the green glaze restores the true color of the Ru porcelain blueish green glaze and is different from the current situation of the bluish color of the existing Ru porcelain glaze in the market, and the retro effect is achieved.
Description
technical field [0001] The invention relates to the field of Ru porcelain production, in particular to a Ru porcelain vintage glaze and a manufacturing process thereof. Background technique [0002] Ruzhou is the hometown of Ru porcelain. Ru porcelain is one of the five famous porcelains of "Ru, Guan, Jun, Ge and Ding" in the Song Dynasty. It was named after it was produced in Ruzhou. Ru kiln was created and fired in the early Northern Song Dynasty, and was famous for firing green glazed porcelain. In the late Northern Song Dynasty, because of the outstanding products of Ru kiln, its porcelain making technology was monopolized by the royal family, and "Ru official porcelain" was fired exclusively for the court, which is later literature. The so-called "Ru Porcelain" in Chinese is forbidden by the people. [0003] As the Jin soldiers went south and the Song Dynasty moved south, the production of Ru porcelain stopped immediately, which lasted for about forty years. Due to t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.