A preparation method of highly efficient electromagnetic shielding porous material based on nanocellulose

A technology of nanocellulose and electromagnetic shielding, applied in the fields of magnetic/electric field shielding, metal material coating technology, electrical components, etc.

Active Publication Date: 2021-05-11
DONGHUA UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a preparation method of a highly efficient electromagnetic shielding porous material based on nanocellulose. Under the action of glucose, a uniform layer of metal is formed on the surface of the polydopamine-modified cellulose-based porous material. The silver coating will not destroy its open-pore structure. It has been proved by experiments that it is an excellent electromagnetic wave shielding material mainly absorbing electromagnetic waves, and the shielding principle is mainly based on electromagnetic wave absorption, so as to reduce secondary electromagnetic pollution and meet the needs of electromagnetic protection. It has great application prospects in special fields such as military aviation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of highly efficient electromagnetic shielding porous material based on nanocellulose
  • A preparation method of highly efficient electromagnetic shielding porous material based on nanocellulose
  • A preparation method of highly efficient electromagnetic shielding porous material based on nanocellulose

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Preparation of polydopamine-modified cellulose-based porous materials

[0031] Weighing 10 grams of the wood pulp cellulose nanowire suspension with a mass fraction of 1.3% was placed in a 50ml beaker, and at room temperature, 28.9mg of dopamine hydrochloride (dissolved in 1ml of water, slowly dropwise) was added under the effect of magnetic stirring Add), and adjust the pH to 8.5 with Tris-HCl buffer solution, keep the reaction at room temperature for 20h, add 130mg KH560 and continue to stir for 2h. Subsequently, the suspension was frozen with liquid nitrogen for 8 min and then freeze-dried on a freeze-drying agent for 48 h to obtain a polydopamine-modified cellulose-based porous material, which was baked at 110° C. for 30 min to increase the degree of crosslinking. Wherein, the porous material preparation method of the organosilane-modified cellulose-based porous material (ie, without PDA) was used as a blank control as described above.

[0032] (2) Silver-seedi...

Embodiment 2

[0039] (1) Preparation of polydopamine-modified cellulose-based porous materials

[0040] Weighing 10 grams of the wood pulp cellulose nanowire suspension with a mass fraction of 1.3% was placed in a 50ml beaker, and at room temperature, 28.9mg of dopamine hydrochloride (dissolved in 1ml of water, slowly dropwise) was added under the effect of magnetic stirring Add), and adjust the pH to 8.5 with Tris-HCl buffer solution, keep the reaction at room temperature for 20h, add 130mg KH560 and continue to stir for 2h. Subsequently, the suspension was frozen with liquid nitrogen for 8 min and then freeze-dried on a freeze-drying agent for 48 h to obtain a polydopamine-modified cellulose-based porous material, which was baked at 110° C. for 30 min to increase the degree of crosslinking. Wherein, the porous material preparation method of the organosilane-modified cellulose-based porous material (ie, without PDA) was used as a blank control as described above.

[0041] (2) Silver-seedi...

Embodiment 3

[0048] (1) Preparation of polydopamine-modified cellulose-based porous materials

[0049] Weighing 10 grams of the wood pulp cellulose nanowire suspension with a mass fraction of 1.3% was placed in a 50ml beaker, and at room temperature, 28.9mg of dopamine hydrochloride (dissolved in 1ml of water, slowly dropwise) was added under the effect of magnetic stirring Add), and adjust the pH to 8.5 with Tris-HCl buffer solution, keep the reaction at room temperature for 20h, add 130mg KH560 and continue to stir for 2h. Subsequently, the suspension was frozen with liquid nitrogen for 8 min and then freeze-dried on a freeze-drying agent for 48 h to obtain a polydopamine-modified cellulose-based porous material, which was baked at 110° C. for 30 min to increase the degree of crosslinking. Wherein, the porous material preparation method of the organosilane-modified cellulose-based porous material (ie, without PDA) was used as a blank control as described above.

[0050] (2) Silver-seedi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a highly efficient electromagnetic shielding porous material based on nanocellulose, which includes using cellulose nanowire suspension as a raw material, performing triple cross-linking with an organosilane coupling agent and dopamine, and utilizing the abundant Catechol and amino groups chelate silver ions and reduce them into silver species in situ. In the case of contact with electroless plating solution and the action of reducing agent glucose, silver particles start to grow on the silver species, and finally in the porous A uniform and firm metallic silver coating is formed on the surface of the material. Under the action of glucose, the present invention forms a layer of uniform metal silver coating on the surface of the polydopamine-modified cellulose-based porous material without destroying its open-pore structure, and is proved to be an excellent electromagnetic wave absorbing material by experiments to reduce the two Electromagnetic pollution, meet the needs of electromagnetic protection and have great application prospects in special fields.

Description

technical field [0001] The invention belongs to the field of electromagnetic shielding, in particular to a preparation method of a nanocellulose-based highly efficient electromagnetic shielding porous material. Background technique [0002] In recent years, due to the rapid development of science and technology, the rapid development of the electronic industry has brought us great convenience. At the same time, the electromagnetic waves generated by it have also affected the normal operation of electronic equipment and even threatened human health. Therefore, development and It is imminent to successfully prepare a highly efficient electromagnetic shielding porous material. An ideal electromagnetic shielding material needs to meet two technical key points: First, as a shielding material, it must have high electromagnetic shielding efficiency to shield electromagnetic waves to the greatest extent, and the shielding principle must be based on absorbing electromagnetic waves to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/28C08J9/36C08J3/24C08G73/06C23C18/44H05K9/00
CPCC08G73/0672C08J3/246C08J9/0066C08J9/28C08J9/36C08J2397/02C08J2479/04C08K2003/0806C23C18/44H05K9/0081
Inventor 隋晓锋武丽萍李营战王碧佳毛志平徐红张琳萍钟毅
Owner DONGHUA UNIV