PPO/PA alloy material with high impact resistance, and preparation method thereof

A technology of alloy material and high impact resistance, applied in the field of high impact resistance PPO/PA alloy material and its preparation, can solve the problems of poor fluidity, difficult processing, poor dimensional stability, poor heat resistance, etc., and achieve excellent dimensional stability properties, high notched impact strength, and excellent heat resistance

Inactive Publication Date: 2018-09-28
SHANGHAI PRET COMPOSITES +4
View PDF8 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] PPO (polyphenylene ether) resin is an amorphous material with excellent heat resistance, good dimensional stability, excellent electrical insulation and excellent creep resistance. It is one of the most important engineering plastics, but its impact performance is relatively low. Poor, and poor fluidity is difficult to process, which greatly limits its application in some fields
PA66 resin is a crystalline material with good fluidity and easy processing, but it is easy to absorb water, has poor dimensional stability and poor heat resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1): Weigh 39.6 parts of PPO resin and 50 parts of PA resin according to the weight ratio, and dry them in an oven; add 3 parts of compatibilizer, 7 parts of toughening agent, and 0.4 part of antioxidant and stir in a high-speed mixer Mix for 3 to 5 minutes;

[0025] 2): The material obtained in step (1) is fed into the twin-screw extruder through the main feeder, and melted and extruded through the twin-screw extruder. The extrusion process is: twin-screw extruder temperature zone: one zone Temperature 190℃~250℃, zone 2 temperature 220℃~270℃, zone 3 temperature 270℃~300℃, zone 4 temperature 270℃~300℃, zone 5 temperature 270℃~300℃, zone 6 temperature 270℃~300℃ ℃, the temperature of the seventh zone is 270℃~300℃, the temperature of the eighth zone is 270℃~300℃, the temperature of the ninth zone is 270℃~300℃, the temperature of the head is 290℃~310℃, the screw speed is 300r / min~600r / min, and the pressure is 10-16MPa;

[0026] 3): The material obtained in step (2) is subj...

Embodiment 2

[0028] 1): Weigh 49.6 parts of PPO resin and 40 parts of PA resin according to the weight ratio, and dry them in an oven; add 3 parts of compatibilizer, 7 parts of toughening agent, and 0.4 part of antioxidant and stir in a high-speed mixer Mix for 3 to 5 minutes;

[0029] 2): The material obtained in step (1) is fed into the twin-screw extruder through the main feeder, and melted and extruded through the twin-screw extruder. The extrusion process is: twin-screw extruder temperature zone: one zone Temperature 190℃~250℃, zone 2 temperature 220℃~270℃, zone 3 temperature 270℃~300℃, zone 4 temperature 270℃~300℃, zone 5 temperature 270℃~300℃, zone 6 temperature 270℃~300℃ ℃, the temperature of the seventh zone is 270℃~300℃, the temperature of the eighth zone is 270℃~300℃, the temperature of the ninth zone is 270℃~300℃, the temperature of the head is 290℃~310℃, the screw speed is 300r / min~600r / min, and the pressure is 10-16MPa;

[0030] 3): The material obtained in step (2) is subj...

Embodiment 3

[0032] 1): Weigh 59.6 parts of PPO resin and 30 parts of PA resin according to the weight ratio, and dry them in an oven; add 3 parts of compatibilizer, 7 parts of toughening agent, and 0.4 part of antioxidant and stir in a high-speed mixer Mix for 3 to 5 minutes;

[0033] 2): The material obtained in step (1) is fed into the twin-screw extruder through the main feeder, and melted and extruded through the twin-screw extruder. The extrusion process is: twin-screw extruder temperature zone: one zone Temperature 190℃~250℃, zone 2 temperature 220℃~270℃, zone 3 temperature 270℃~300℃, zone 4 temperature 270℃~300℃, zone 5 temperature 270℃~300℃, zone 6 temperature 270℃~300℃ ℃, the temperature of the seventh zone is 270℃~300℃, the temperature of the eighth zone is 270℃~300℃, the temperature of the ninth zone is 270℃~300℃, the temperature of the head is 290℃~310℃, the screw speed is 300r / min~600r / min, and the pressure is 10-16MPa;

[0034] 3): The material obtained in step (2) is subj...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PPO / PA alloy material with high impact resistance, and a preparation method thereof, wherein the PPO / PA alloy material comprises, by weight, 30-70 parts of a PPO resin, 30-70parts of a PA resin, 3-10 parts of a compatibilizer, 5-15 parts of a toughening agent, and 0.1-1 part of an antioxidant. According to the present invention, the PPO / PA alloy obtained by blending PPOand PA integrates the unique advantages of PPO and PA, wherein the unique advantages comprise excellent heat resistance, excellent processing property, excellent dimensional stability and high notchedimpact strength; and the PPO / PA material with high impact resistance is extremely focused at home and abroad, especially in the vehicle industry, and the modified PPO / PA alloy can easily process larger-size parts through injection molding and can provide good impact resistance.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a high-impact PPO / PA alloy material and a preparation method thereof. Background technique [0002] PPO (polyphenylene ether) resin is an amorphous material with excellent heat resistance, good dimensional stability, excellent electrical insulation and excellent creep resistance. It is one of the most important engineering plastics, but its impact performance is relatively low. Poor, and poor fluidity is difficult to process, which greatly limits its application in some fields. PA66 resin is a crystalline material with good fluidity and easy processing, but it is easy to absorb water, has poor dimensional stability and poor heat resistance. Contents of the invention [0003] In order to overcome the shortcomings of the existing technology, the invention provides a high impact resistance PPO / PA alloy material with good impact resistance and excellent proce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/12C08L77/02C08L77/06C08L51/08C08L53/02C08L51/00C08L51/06C08K5/134C08K5/526
CPCC08L71/123C08L77/02C08L77/06C08L2201/08C08L2205/035C08L2205/08C08L51/08C08L53/025C08L51/003C08L51/06C08K5/1345C08K5/526
Inventor 张中伟肖浩蔡青郑杭景田兰周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com