Polycarbonate resin composition and molded article thereof

A technology of polycarbonate resin and composition, which is applied in the field of polycarbonate resin composition, can solve unknown problems and achieve the effect of excellent transparency

Active Publication Date: 2020-08-14
MITSUBISHI CHEM CORP
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, so far, no examples of the use of polyrotaxanes in polycarbonate resins to improve mechanical properties have been known

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polycarbonate resin composition and molded article thereof
  • Polycarbonate resin composition and molded article thereof
  • Polycarbonate resin composition and molded article thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0254] Hereinafter, the present invention will be described in more detail by way of examples, but the present invention is not limited to the following examples unless the gist is exceeded.

[0255] [Evaluation method]

[0256] Hereinafter, evaluation of the physical properties or characteristics of the polycarbonate resin (A), polyrotaxane (B) and the resin composition was performed by the following methods.

[0257] (1) Determination of elongation at break

[0258] Using STROGRAPH (model name VG10E) manufactured by Toyo Seiki Co., Ltd., the elongation at breaking point was measured at a tensile speed of 50 mm / min at a room temperature of 23°C. It should be noted that the larger the value of elongation at break, the better the mechanical strength, and in the present invention, it is judged that the value is 12% or more to be excellent in mechanical strength.

[0259] (2) Total light transmittance

[0260] The pellets of the polycarbonate resin composition were dried at 90° ...

manufacture example 1

[0302] The polycarbonate resin was polymerized using a continuous polymerization equipment consisting of 3 vertical stirred reactors and 1 horizontal stirred reactor and a twin-screw extruder. Specifically, firstly, ISB, CHDM and DPC are melted in a tank respectively, and ISB is 35.2 kg / hr, CHDM is 14.9 kg / hr, and DPC is 74.5 kg / hr (by molar ratio, ISB / CHDM / DPC= 0.700 / 0.300 / 1.010) was continuously supplied to the first vertical stirring reactor. Simultaneously, an aqueous solution of calcium acetate monohydrate was supplied to the first vertical stirring reactor so that the amount of calcium acetate monohydrate added as a catalyst was 1.5 μmol relative to 1 mol of the total dihydroxy compound. The reaction temperature, internal pressure, and residence time of each reactor were set as the first vertical stirred reactor: 190°C, 25kPa, 90 minutes, the second vertical stirred reactor: 195°C, 10kPa, 45 minutes, and the third vertical stirred reactor. Type stirred reactor: 210°C, 3...

Embodiment 1

[0310] Using a torque rheometer (LABO PLASTOMILL) 4C150-01 manufactured by Toyo Seiki Co., Ltd., 47.5 g of the copolycarbonate resin obtained in Production Example 1 and 2.5 g of SeRM Super Polymer SH2400P as a polyrotaxane were carried out at 240° C. Mix for 10 minutes (refer to Table 1 for the mixing ratio).

[0311] After drying the obtained kneaded resin in a vacuum dryer at 90° C. for 5 hours, it was heated at 200° C. for 10 hours using a hot press made by Toyo Seiki Co., Ltd. (Mini Test Press (200×200 mm) model MP-2FH). Hot pressing was carried out within 1 minute to obtain a composite composite composition pressboard of copolycarbonate and polyrotaxane with a thickness of 0.5 mm. The total light transmittance of the obtained pressed board was evaluated, and the test piece for the tensile test was punched out, and the amount of stretch was evaluated by the tensile test.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

An object of the present invention is to provide a polycarbonate resin composition, a method for producing the same, and a molded article of the polycarbonate resin composition that can balance impact resistance at a high level. The present invention relates to a polycarbonate resin composition containing a polycarbonate resin (A) and a polyrotaxane (B), a method for producing the same, and a molded article of the resin composition. The polycarbonate resin (A) Contains a structural unit derived from a compound represented by formula (1).

Description

technical field [0001] The present invention relates to a polycarbonate resin composition excellent in transparency and well balanced with mechanical properties such as impact resistance and elongation at break, and heat and humidity resistance, a method for producing the same, and a molded article obtained by molding the resin composition . Background technique [0002] Existing aromatic polycarbonate resins containing structures derived from bisphenol A, etc., and those using isosorbide (ISB), which is a dihydroxy compound obtained from biomass resources, have been researched and developed in recent years The new polycarbonate resin has excellent mechanical properties such as impact resistance, heat resistance, and transparency, and is widely used in various mechanical parts, optical discs, and automotive parts. [0003] For example, in the case of being used for automobile parts, it is required to be able to withstand a wide temperature range or a harsh environment even ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08G64/02C08L71/02
CPCC08L71/02C08L69/00C08L5/16C08G64/02C08G83/007C08L87/00C08G64/305C08L2201/08
Inventor 安藤正人田中智彦
Owner MITSUBISHI CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com