Polyethylene film for automatic packaging and preparation method thereof

A polyethylene film and automatic packaging technology, applied in the field of polyethylene film, can solve the problems of low bag breaking rate, poor thermal adhesive strength and impact strength, and high bag breaking rate

Active Publication Date: 2018-11-09
青岛东海包装产业有限公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] This high-strength anti-static polyethylene film has good tensile strength and anti-static properties, but because of poor thermal bonding strength and impact resistance, the bag breakage rate ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene film for automatic packaging and preparation method thereof
  • Polyethylene film for automatic packaging and preparation method thereof
  • Polyethylene film for automatic packaging and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: A polyethylene film for automatic packaging, comprising an outer layer, an intermediate layer and an inner layer laminated in sequence;

[0045] The outer layer is composed of the following parts by weight: 20 parts has a melt index of 1.9g / 10min and a density of 0.924g / cm 3 LDPE, 30 parts melt index is 1.0g / 10min, density is 0.92g / cm 3 LLDPE, 20 parts melt index is 1.1g / 10min, density is 0.920g / cm 3 LLDPE and 3 parts of emulsifier;

[0046] The middle layer is composed of the following parts by weight: 10 parts has a melt index of 1.9 g / 10 min and a density of 0.925 g / cm 3 LDPE, 30 parts, the melt index is 1.1g / 10min, and the density is 0.920g / cm 3 LLDPE, 30 parts melt index is 2.4g / 10min, density is 0.921g / cm 3 LLDPE, 7 parts of emulsifier, 5 parts of density 1.47g / cm 3 Polyether ether ketone, 10 parts of white masterbatch for polyethylene;

[0047] The inner layer is composed of the following parts by weight: 10 parts has...

Embodiment 2

[0056] Embodiment 2: a polyethylene film for automatic packaging, comprising an outer layer, an intermediate layer and an inner layer laminated in sequence;

[0057] The outer layer is composed of the following parts by weight: 30 parts has a melt index of 1.9g / 10min and a density of 0.924g / cm 3 LDPE, 40 parts, the melt index is 1.0g / 10min, and the density is 0.92g / cm 3 LLDPE, 30 parts, the melt index is 1.1g / 10min, and the density is 0.920g / cm 3 LLDPE and 4 parts of emulsifier;

[0058]The middle layer is composed of the following parts by weight: 20 parts has a melt index of 1.9g / 10min and a density of 0.925g / cm 3 LDPE, 40 parts, the melt index is 1.1g / 10min, and the density is 0.920g / cm 3 The LLDPE, 40 parts have a melt index of 2.4g / 10min and a density of 0.921g / cm 3 LLDPE, 8 parts emulsifier, 10 parts density of 1.47g / cm 3 Polyether ether ketone, 12 parts of white masterbatch for polyethylene;

[0059] The inner layer is composed of the fol...

Embodiment 3

[0068] Embodiment 3: A polyethylene film for automatic packaging, comprising an outer layer, an intermediate layer and an inner layer laminated in sequence;

[0069] The outer layer is composed of the following parts by weight: 40 parts has a melt index of 1.9 g / 10 min and a density of 0.924 g / cm 3 LDPE, 50 parts melt index is 1.0g / 10min, density is 0.92g / cm 3 LLDPE, 40 parts, the melt index is 1.1g / 10min, and the density is 0.920g / cm 3 LLDPE and 5 parts of emulsifier;

[0070] The middle layer is composed of the following parts by weight: 30 parts have a melt index of 1.9 g / 10 min and a density of 0.925 g / cm 3 LDPE, 50 parts melt index is 1.1g / 10min, density is 0.920g / cm 3 LLDPE, 50 parts melt index is 2.4g / 10min, density is 0.921g / cm 3 LLDPE, 9 parts of emulsifier, 15 parts of density 1.47g / cm 3 14 parts of polyetheretherketone and 14 parts of white masterbatch for polyethylene;

[0071] The inner layer is composed of the following parts by we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyethylene film for automatic packaging. The polyethylene film comprises an outer layer, an intermediate layer and an inner layer which are sequentially laminated. The outer layer is prepared from the following substances in parts by weight: 20-40 parts of low density polyethylene (LDPE), 30-50 parts of linear low density polyethylene (LLDPE), and 20-40 parts of LLDPE with melt index of 1.1 g/10 min and density of 0.920 g/cm<3>. The intermediate layer is prepared from the following substances in parts by weight: 10-30 parts of LDPE, 30-50 parts of LLDPE with melt index of 1.1 g/10 min and density of 0.920 g/cm<3>, and 30-50 parts of LLDPE with melt index of 2.4 g/10 min and density of 0.921 g/cm<3>. The inner layer is prepared from the following substances in parts by weight: 10-30 parts of LDPE, 30-50 parts of LLDPE, and 10-30 parts of LLDPE. The invention solves the problem that the polyethylene film has lower thermal viscosity and higher bag breaking rate.

Description

technical field [0001] The present invention relates to a kind of polyethylene film, more specifically, it relates to a kind of polyethylene film for automatic packing and preparation method thereof. Background technique [0002] Polyethylene is one of the most important resins in polyolefin resins, and it is a material with the fastest development and strong demand in the world today. Polyethylene mainly includes low-density polyethylene, linear low-density polyethylene, medium-density polyethylene, high-density polyethylene, etc., and has a very wide range of applications in packaging, medical treatment, pipes and other fields. [0003] In the prior art, reference can be made to the Chinese invention patent application document whose application publication number is CN105968489A, which discloses a preparation method of polyethylene antibacterial packaging film, expressed in parts by weight, with 0.3-1.0 parts of silver-loaded nano-titanium dioxide antibacterial agent, Ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/08B32B27/32B32B27/28B32B27/18C08L23/08C08L23/06C08L61/16C08L69/00C08K3/36C08K5/20
Inventor 吴伟张贵金吉东升
Owner 青岛东海包装产业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap