Self-shaping method for gas-smelted quartz glass ingots

A quartz glass, self-aligning technology, used in glass forming, glass production, glass manufacturing equipment and other directions, can solve the problems of material waste, irregularity, and excessive difference, so as to reduce production costs, save materials, and improve utilization. Effect

Active Publication Date: 2018-11-13
江苏省晶瑞石英工业开发研究院有限公司
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the process of preparing quartz glass anchors by using a gas-refining machine, an oxygen-hydrogen flame is used as a heat source to melt quartz powder to prepare quartz glass anchors. During preparation, various parameters (such as the adjustment of temperature field temperature, the amount of material injection) Speed, blowing air pressure at the top of the molten glass body and the self-leveling parameters of the glass body in the high-temperature molten state), the cumulative error caused by mismatch in the combination control, resulting in excessive differences in the vertical height of the product's isometric value , so that the product forms an irregular state, causing a large waste of materials in the subsequent processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1, a method for self-shaping of quartz glass anchor by gas refining, the steps are as follows:

[0017] (1) Add 80-mesh to 200-mesh silicon material into the silo of the quartz hammering machine, and under the combined action of the carrying gas hydrogen and the excitation power supply at the end of the material delivery pipe, the silicon material is transported at a rate of 2kg / h~4kg / h The amount is sent into the quartz burner, under the action of the pre-ignited hydrogen-oxygen flame, it is heated and melted;

[0018] (2) Under the joint action of gravity and top air pressure, the molten silicon material flows into the furnace cavity and deposits and melts on the rotating deposition target. The deposition target is made of quartz, which gradually grows and accumulates, and is preformed into a cone shape. During the deposition and growth process, the silicon material flows radially from the center of the cone to the surroundings under the action of gravity. ...

Embodiment 2

[0021] Embodiment 2, a self-shaping method for gas refining quartz glass anchors as described in Embodiment 1: the carrying gas described in step (1) is hydrogen, and the delivery volume is 2 m³ / h to 10 m³ / h.

Embodiment 3

[0022] Example 3, in a self-shaping method for gas-refined quartz glass anchorage as described in Example 1: in step (1) in the hydrogen-oxygen flame, the delivery rate of hydrogen is 12 m³ / h~18m³ / h, oxygen The conveying capacity is 5 m³ / h~15m³ / h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a self-shaping method for gas-smelted quartz glass ingots. The self-shaping method comprises the following steps: adding a silicon material into a quartz beating machine, melting and flowing into a furnace chamber of a smelting furnace under the action of high temperature oxyhydrogen flame, carrying out deposition heap-up dissolving operation, forming concentric circle molten glassy-state cylindrical quartz glass ingots with different diameters at different deposition heights in a deposition growth and flowing process; and when the height of the ingots is stacked and grows to every 20 mm-50 mm, beginning to self-shape, allowing a quartz flame head and the molten glassy-state cylindrical quartz glass ingots together to move to the inner wall of the furnace chamber of the smelting furnace in a radial movement manner, making the maximum diameter of the molten glassy-state cylindrical quartz glass ingots produce friction with the inner wall of the furnace chamber,producing deformation, and making the product external dimension meet upper-and-lower equal diameter requirements in the height range, so as to obtain the product. The friction force between objects is used for shaping the appearance size of the product, the shape of the quartz glass ingots can be precisely controlled, the appearance defects of the product can be reduced, the efficiency can be improved and the production cost can be reduced.

Description

technical field [0001] The invention relates to the technology of preparing quartz products by using the physical method of powder materials (hydrogen-oxygen flame high-temperature fusion), especially a self-shaping method of gas refining quartz glass. Background technique [0002] At present, in the process of preparing quartz glass anchors by using a gas-refining machine, an oxyhydrogen flame is used as a heat source to melt quartz powder to prepare quartz glass anchors. During preparation, various parameters (such as the adjustment of the temperature field temperature, the amount of material injection) Speed, blowing air pressure at the top of the molten glass body and the self-leveling parameters of the glass body in the high-temperature molten state), the cumulative error caused by the mismatch in the combination control, resulting in a large difference in the vertical height of the product isometric value , so that the product forms an irregular state, causing a large ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B20/00
CPCC03B20/00Y02P40/57
Inventor 邱志坚邱志刚
Owner 江苏省晶瑞石英工业开发研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products