Silica gel composite bath towel and preparation method thereof

A technology of silica gel and bath towels, which is applied in sanitary equipment, other household appliances, personal care, etc. It can solve the problems of weak bonding between silica gel and bath towel cloth, silica gel affecting performance, and difficulty in uniform coating, etc., reaching the operating temperature range Wide, excellent transparency, good air permeability

Inactive Publication Date: 2018-11-16
王延民
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it is also disclosed to compound silica gel and fabric, simply compound silica gel and bath towel cloth, the bonding force of the two phases of silica gel and bath towel cloth is weak, and the silica gel layer is easy to fall off during use
In addition, the bath towel obtained by compounding bath towel cloth and silica gel is not easy to coat evenly during the preparation process, and the hardness of silica gel will also affect the performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silica gel composite bath towel and preparation method thereof
  • Silica gel composite bath towel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The silica gel composite bath towel includes a silica gel composite layer 1, a water-absorbing layer 2, and a lining layer 3 arranged sequentially from top to bottom. The coating material layer 11 is higher than the thickness of the matrix material layer 12 and is 0.8mm, and the area of ​​the hanging coating material layer 11 is 50% of the area of ​​the matrix material layer 12, and the matrix material is a bath towel;

[0034] The hanging coating material includes the following raw materials in parts by weight: 100 parts of liquid silica gel, 1 part of cyclopolydimethylsiloxane and 1 part of fumed white carbon black;

[0035] The liquid silica gel includes A component and B component, and the weight ratio of the A component and B component is 1:1,

[0036] The A component includes the following raw materials in parts by weight: 12 parts of polymethylvinylsiloxane, 13.965 parts of hydroxyl polydimethylsiloxane, 25 parts of vinyl MQ silicone resin and 0.03 parts of plati...

Embodiment 2

[0043] The silica gel composite bath towel includes a silica gel composite layer 1, a water-absorbing layer 2 and a lining layer 3 arranged sequentially from top to bottom. The thickness of the hanging coating material layer 11 higher than the base material layer 12 is 0.6mm, and the area of ​​the hanging coating material layer 11 is 80% of the area of ​​the base material layer 12, and the base material is bath towel cloth;

[0044] The hanging coating material includes the following raw materials in parts by weight: 100 parts of liquid silica gel, 45 parts of cyclopolydimethylsiloxane and 1 part of fumed white carbon black;

[0045] The liquid silica gel includes A component and B component, and the weight ratio of the A component and B component is 1:1,

[0046] The A component includes the following raw materials in parts by weight: 15 parts of polymethylvinylsiloxane, 15 parts of hydroxyl polydimethylsiloxane, 20 parts of vinyl MQ silicone resin and 0.015 parts of platinum...

Embodiment 3

[0053] The silica gel composite bath towel includes a silica gel composite layer 1, a water-absorbing layer 2 and a lining layer 3 arranged sequentially from top to bottom. The thickness of the hanging coating material layer 11 higher than the base material layer 12 is 0.8mm, and the area of ​​the hanging coating material layer 11 is 80% of the base material layer 12 area, and the base material is bath towel cloth, and the described bath towel cloth is shuttle fabric;

[0054] The hanging coating material includes the following raw materials in parts by weight: 100 parts of liquid silica gel, 15 parts of cyclopolydimethylsiloxane and 1 part of fumed white carbon black;

[0055] The liquid silica gel includes A component and B component, and the weight ratio of the A component and B component is 1:1,

[0056] The A component includes the following raw materials in parts by weight: 14 parts of polymethylvinylsiloxane, 12 parts of hydroxyl polydimethylsiloxane, 24 parts of vinyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a silica gel composite bath towel and a preparation method thereof. The silica gel composite towel comprises a silica gel composite layer, a water absorption layer and a liner layer which are sequentially arranged from top to bottom. The silica gel composite layer is composited by enabling a hanging coating material layer to run through a base material layer, the hanging coating material layer is 1 mm or less larger than the thickness of the base material layer, and the area of the hanging coating layer is 50% or more that of the base material layer. Polar functional groups on the surfaces of the base material and the hanging coating material of the silica gel composite bath towel can generate intermolecular force, under the high-pressure effect in the preparation process, the hanging coating material and the base material can achieve good combination, the hanging coating material can be evenly hung or coat the base material. The obtained silica gel composite bath towel is appropriate in hardness, can easily bring away dirt on the surface skin layer, no damage is caused to skin, and the breathable performance is good. The preparation method is easy to implement, capable of achieving batch production, uniform in hanging and coating thickness and not likely to be disengaged.

Description

technical field [0001] The invention belongs to the field of bath products, and in particular relates to a silica gel composite bath towel and a preparation method thereof. Background technique [0002] Bath towels are people's daily bath products. Currently, the common bath towels on the market include fabric bath towels with high surface roughness and bath towels integrally formed of polymers. The raw materials of fabric bath towels with high roughness are mostly fabrics doped with natural cotton, hemp and other fibers. To achieve the purpose of removing stains on the skin surface, bath towels made of these materials must have greater roughness, and larger Roughness and easy to damage the skin. The bath towel integrally formed by polymer has a smooth surface and can better remove dirt on the skin surface, but the bath towel made of pure polymer is thicker, not soft enough, and uses more materials. [0003] Chinese patent CN201220246570.5 discloses a bath towel, including...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A47K7/02C09D183/04C09D183/07C09D183/06C09D7/61B32B5/02B32B33/00
CPCA47K7/02B32B5/02B32B33/00B32B2307/412B32B2307/5825B32B2307/726B32B2555/00C08L2201/10C08L2205/025C08L2205/03C09D7/61C09D183/04C08L83/04C08L83/06C08K3/36
Inventor 王延民
Owner 王延民