Liquid water-soluble fertilizer and preparation method thereof
A water-soluble fertilizer, liquid technology, applied in nitrogen fertilizer, magnesium fertilizer, potash fertilizer and other directions, can solve the problem of wasting labor and achieve the effect of reducing pesticide residues, promoting transformation, and comprehensive nutrients
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] 1. Prepare large and medium element solutions: Weigh urea, monoammonium phosphate, potassium sulfate and potassium dihydrogen phosphate according to the mass ratio of 30:16:15:13, add 30 parts of water, and rotate at 1500 rpm Stir for 30 minutes under shear emulsification and stirring conditions, add calcium disodium edetate and magnesium disodium edetate with a mass ratio of 40:40, and stir for 30 minutes to form a homogeneous liquid. Let stand for 8 hours. use;
[0024] 2. Add 20% water and 15% organic matter to the stirring tank, heat to 60-70℃, keep for 30 minutes, add 28.8% large and medium element solution, stir until the solid is completely dissolved; pump into the reactor, add 14.2% Trace elements, 4% humic acid, 16% potassium fulvic acid, stir for 50 minutes, and cool to 35°C to obtain slurry, which is put into the slurry buffer tank for thickening;
[0025] 3. Add 2% talc powder, maintain the temperature at 60-65℃, filter through a 100-mesh sieve...
Example Embodiment
[0026] Example 2
[0027] 1. Prepare large and medium element solutions: weigh ammonium nitrate, ammonium polyphosphate, and potassium dihydrogen phosphate according to the mass ratio of 40:45:36, add 26 parts of water, and stir at a shear emulsification at a speed of 1100 rpm Stir under the conditions for 20 minutes, add calcium nitrate tetrahydrate, magnesium nitrate decahydrate, and magnesium sulfate with a mass ratio of 30:37, stir for 30 minutes to form a homogeneous liquid, and let it stand for 10 hours before use;
[0028] 2. Add 20% water and 17% organic matter into the stirring tank, heat to 60-65℃, keep for 40 minutes, add 25% large and medium element solution, stir until the solid is completely dissolved; pump into the reactor, add 11% Trace elements, 6% humic acid, 18% potassium fulvic acid, stir for 40 minutes, and cool to 30°C to obtain slurry, which is put into the slurry buffer tank to thicken;
[0029] 3. Add 3% talc powder, maintain the temperature at 60-65°C, filt...
Example Embodiment
[0030] Example 3
[0031] 1. Prepare large and medium element solutions: Weigh monoammonium phosphate, ammonium polyphosphate, potassium dihydrogen phosphate, and potassium chloride according to the mass ratio of 30:46:28:23, add 30 parts of water, and rotate at 1000 rpm Stir for 40 minutes under the condition of shear emulsification / min., add magnesium sulfate, magnesium acetate, calcium acetate, calcium nitrate with a mass ratio of 49:35:32:30, stir for 30 minutes to form a homogeneous liquid, and let stand for 8 hours Backup
[0032] 2. Add 13% water and 12% organic matter to the stirring tank, heat to 55-65℃, keep for 40 minutes, add 30% large and medium element solution, stir until the solid is completely dissolved; pump into the reactor, add 16% Trace elements, 6% humic acid, 18% potassium fulvic acid, stir for 60 minutes, and cool the temperature to 38°C to obtain slurry, which is put into the slurry buffer tank to thicken;
[0033] 3. Add 5% talc powder, maintain the temper...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap