Titanium alloy used for high performance cutter

A titanium alloy, high-performance technology, applied in the field of titanium alloy materials, can solve the problems of high titanium alloy prices, achieve good market prospects, increase hardness, and reduce costs

Inactive Publication Date: 2018-12-04
江苏天工科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, some special industries, especially in the military industry, basically use titanium alloys for the production of knives. The hardness HRC value of the knives made of existing titanium alloys is generally less than 46, and the hardness HRC value of the knives used in some operations is higher than 46. If it is greater than 50, the cutting tools made of existing titanium alloys in some environments cannot meet the requirements. Chinese invention patent CN102851542A discloses a titanium alloy for making cutting tools and its preparation method. Although the method increases the HRC value To 55-57, but adding 4% metal vanadium, resulting in high prices of titanium alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The preparation method of titanium alloy for high-performance cutter of the present invention comprises the following steps:

[0018] A. Weigh each element powder, high-purity aluminum ingot and titanium sponge with a purity of more than 99.7% according to the formula;

[0019] B. Melting each raw material with a vacuum consumable electrode arc melting method to obtain a high-temperature titanium alloy ingot;

[0020] C. Heat preservation treatment at 650-700°C for 2-3 hours, then heat preservation treatment at 400-420°C for 2-3 hours, and then cool naturally.

Embodiment 1

[0022] A high-performance titanium alloy for cutting tools, including the following components by weight: Al 1.2%, B 0.2%, W 0.8%, Co 1.0%, Fe 0.4%, Cr 0.7%, the balance is Ti and unavoidable impurities .

Embodiment 2

[0024] A high-performance titanium alloy for cutting tools, including the following components by weight: Al 1.2%, B 0.1%, W 0.8%, Co 1.2%, Fe 0.2%, Cr 1.0%, the balance is Ti and unavoidable impurities .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a titanium alloy used for a high performance cutter. The titanium alloy includes, by weight, the following components: 1.0-1.5% of Al, 0.1-0.3% of B, 0.5-1.0% of W, 0.8-1.2% ofCo, 0.2-0.5% of Fe, 0.6-1.0% of Cr, with the balance being Ti and unavoidable impurities. A hardness HRC value of the titanium alloy is increased to 60-62; vanadium is completely replaced by cheap elements of chromium, iron, cobalt, boron and tungsten, so that the cost is greatly reduced, and the cost performance is very excellent; and a preparation method of the titanium alloy is simple, the cost is significantly lower than cost of market products, and the titanium alloy has a very good market prospect.

Description

technical field [0001] The invention relates to the technical field of titanium alloy materials, in particular to a titanium alloy for high-performance cutting tools. Background technique [0002] At present, some special industries, especially in the military industry, basically use titanium alloys for the production of knives. The hardness HRC value of the knives made of existing titanium alloys is generally less than 46, and the hardness HRC value of the knives used in some operations is higher than 46. If it is greater than 50, the cutting tools made of existing titanium alloys in some environments cannot meet the requirements. Chinese invention patent CN102851542A discloses a titanium alloy for making cutting tools and its preparation method. Although this method increases the HRC value To 55-57, but adding 4% metal vanadium, resulting in high prices of titanium alloys. [0003] Therefore, it is necessary to develop a high-performance titanium alloy for cutting tools, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C14/00C22C1/02C22F1/18
CPCC22C1/02C22C14/00C22F1/183
Inventor 朱小坤陈杰候宇鑫江静蒋荣军
Owner 江苏天工科技股份有限公司