Remelting method of electroslag ingot for cold roll
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of electroslag remelting and electroslag ingot, which is applied in the field of iron and steel metallurgy
Active Publication Date: 2021-01-26
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] Therefore, how to prepare high-quality electroslag ingots for cold rolling rolls by electroslag remelting, so as to prepare qualified cold rolling rolls for subsequent processes, there is currently no effective solution
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0044] This embodiment is to use the method of the present invention to produce Φ1100mm electroslag ingots, and the specific steps are as follows:
[0045] a. The raw materials are initially smelted in an electric arc furnace. After the smelting is completed, the molten steel is placed in a ladle refining furnace to refine the molten steel, and adjusted according to the composition requirements, and then vacuum degassed. After the molten steel is refined, it is molded into Φ730mm corrugated Ingot electrode rod;
[0046] b. Remove the risers of the casted 2 Φ730mm corrugated ingot electrode rods and weld the dummy electrodes, then check the surface quality of the electrode rods, clean up impurities such as iron oxide scale, and then put the electrode rods into the bottom of the car for heat treatment The furnace is heated and baked, the heating temperature is 840±10°C, the heating rate is ≤60°C / h, and the holding time is 12 hours;
[0047] c. Benxi steel or similar steel types...
Embodiment 2
[0054] This embodiment is to use the method of the present invention to produce Φ1100mm electroslag ingots, and the specific steps are as follows:
[0055] a. The raw materials are initially smelted in an electric arc furnace. After the smelting is completed, the molten steel is placed in a ladle refining furnace to refine the molten steel, and adjusted according to the composition requirements, and then vacuum degassed. After the molten steel is refined, it is molded into Φ730mm corrugated Ingot electrode rod;
[0056] b. Remove the risers of the casted 2 Φ730mm corrugated ingot electrode rods and weld the dummy electrodes, then check the surface quality of the electrode rods, clean up impurities such as iron oxide scale, and then put the electrode rods into the bottom of the car for heat treatment The furnace is heated and baked, the heating temperature is 850±10°C, the heating rate is ≤60°C / h, and the holding time is 15 hours;
[0057] c. Benxi steel or similar steel types...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a method for remelting electroslag ingots for cold rolling rolls, belonging to the technical field of iron and steel metallurgy. The technical problem to be solved by the present invention is how to prepare high-quality electroslag ingots for cold rolling rolls through electroslag remelting. The invention provides a method for remelting electroslag ingots for cold rolling rolls, which includes the steps of baking electrode rods, selecting and baking slag systems, melting protective slag, electroslag remelting process, annealing process and the like. The present invention improves the chemical composition of the electrode rod, selects a suitable slag system, bakes the electrode rod and slag material, adjusts the electroslag remelting and annealing process, and prepares an electroslag ingot with good internal and external quality for cold rolling rolls. There are no defects such as ripples or slag grooves, and the high and low magnification inspections meet the quality requirements of the first-level billet, providing favorable conditions for the subsequent process to ensure product quality.
Description
technical field [0001] The invention belongs to the technical field of iron and steel metallurgy, and in particular relates to a method for remelting electroslag ingots for cold rolling rolls. Background technique [0002] The roll is one of the parts with the most complicated working conditions in the rolling mill, and it is also a high-tech product with the highest quality requirements, special materials, and complex manufacturing processes among roll products. With the rapid development of modern economic construction, the operating efficiency of large-scale cold rolling mills and the quality requirements of plates are constantly improving, and the required material strength requirements are getting higher and higher. Good performance and other aspects of development. The development of rolls at home and abroad mainly increases the content of Cr in cold rolls, from the initial 2% Cr to the 5% Cr cold rolls commonly used in the market, and continuously optimizes alloys su...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.