Method for producing stair tread
A technology of stair treads and production methods, which is applied in wood treatment, charcoal burning/combustion, wood processing appliances, etc. It can solve the problems of easy warping, easy suspension of stair treads, large total area of stair treads, etc., and achieve the effect of reducing odor
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] Example 1. A method for producing stair treads, comprising the following steps,
[0019] a. Cut the beech wood boards into boards for making stair treads, and get product A,
[0020] b. Plane product A to get product B,
[0021] c. Place two aluminum plates on the front and back sides of product B respectively and clamp them to obtain product C.
[0022] d. Put product C into a kiln for carbonization, the temperature of carbonization is 195°C, and the time of carbonization is 1.5h. Product C is treated with ultrasonic wave while carbonizing. The frequency of ultrasonic wave is 42.5KHz to obtain product D.
[0023] e, remove the aluminum plate on product D and put it into a damp chamber, so that the moisture content of product D rises to 8%, and product E is obtained.
[0024] f. Carry out paint treatment to product E to obtain product F,
[0025] g, put F product into the kiln to keep warm after covering the tea leaves, the kiln temperature is 75°C, the relative air...
Embodiment 2
[0028] Example 2. A method for producing stair treads, comprising the following steps,
[0029] a. Cut the beech wood boards into boards for making stair treads, and get product A,
[0030] b. Plane product A to get product B,
[0031] c. Place two aluminum plates on the front and back sides of product B respectively and clamp them to obtain product C.
[0032] d. Put product C into the kiln for carbonization, the temperature of carbonization is 180°C, and the time of carbonization is 1h. Product C is treated with ultrasonic wave while carbonizing. The frequency of ultrasonic wave is 40KHz to obtain product D.
[0033] e. Remove the aluminum plate on product D and put it into a damp chamber, so that the moisture content of product D rises to 7-9%, and product E is obtained.
[0034] f. Carry out paint treatment to product E to obtain product F,
[0035] g, put F product into the kiln to keep warm after covering the tea leaves, the kiln temperature is 70°C, the relative air...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com