Composite plastic having stability

A composite plastic and stability technology, applied in the field of plastics, can solve the problems of many toxic substances and difficult to degrade, and achieve the effect of scientific and reasonable ratio, fast degradation effect and good stabilization effect.

Inactive Publication Date: 2018-12-18
华正金属材料(太仓)有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing PVC materials contain many toxic subs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] A stable composite plastic, including the following components by weight:

[0020] 30 parts of PVC;

[0021] 10 parts of ACR resin powder;

[0022] 0.5 part of phenyl phthalate;

[0023] Carbon black 1 part;

[0024] 0.6 part of light stabilizer;

[0025] 0.5 parts of iron dialkyldithiocarbamate.

[0026] The beneficial effects of the invention are: the ratio is scientific and reasonable, PVC and resin powder are the main raw materials, and some additives added do not contain halogen or lead, which is more environmentally friendly, does not produce pollution, and has a fast degradation effect. Stabilizer with good stabilizing effect.

Example Embodiment

[0027] Example 2

[0028] A stable composite plastic, including the following components by weight:

[0029] 35 parts of PVC;

[0030] 15 parts of ACR resin powder;

[0031] 1 part of phenyl o-hydroxybenzoate;

[0032] 1.5 parts of carbon black;

[0033] Light stabilizer 0.9 parts;

[0034] 0.75 parts of iron dialkyldithiocarbamate.

[0035] The beneficial effects of the invention are: the ratio is scientific and reasonable, PVC and resin powder are the main raw materials, and some additives added do not contain halogen or lead, which is more environmentally friendly, does not produce pollution, and has a fast degradation effect. Stabilizer with good stabilizing effect.

Example Embodiment

[0036] Example 3

[0037] A stable composite plastic, including the following components by weight:

[0038] 40 parts of PVC;

[0039] 20 parts of ACR resin powder;

[0040] 1.5 parts of phenyl o-hydroxybenzoate;

[0041] 2 parts of carbon black;

[0042] 1.3 parts of light stabilizer;

[0043] 1 part of iron dialkyldithiocarbamate.

[0044] The beneficial effects of the invention are: the ratio is scientific and reasonable, PVC and resin powder are the main raw materials, and some additives added do not contain halogen or lead, which is more environmentally friendly, does not produce pollution, and has a fast degradation effect. Stabilizer with good stabilizing effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite plastic having stability, which comprises the following components in parts by weight: 30-40 parts of PVC; 10-20 parts of resin powder; 0.5-1.5 parts of an anti-UVagent; 1-2 parts of carbon black; 0.6-1.3 parts of a light stabilizer; and 0.5-1 part of a photodegradation agent. The composite plastic has the beneficial effects that the ratio is scientific and reasonable, PVC and the resin powder are the main raw materials, and the added additives do not contain halogen or lead, and are more environmentally friendly and do not cause pollution, at the same time, the degradation effect is fast, and the added light stabilizer has the good stabilizing effect.

Description

technical field [0001] The invention relates to a plastic, in particular to a stable composite plastic. Background technique [0002] PVC (polyvinyl chloride) is a thermoplastic resin polymerized by vinyl chloride under the action of an initiator. It is a homopolymer of vinyl chloride. Vinyl chloride homopolymer and vinyl chloride copolymer are collectively referred to as vinyl chloride resin. PVC has good mechanical properties, the tensile strength is about 60mpa, the impact strength is 5-10kj / m2, and it has excellent dielectric properties, but it has poor stability to light and heat. Decomposition produces hydrogen chloride, and further autocatalytic decomposition causes discoloration and rapid decline in physical properties. In practical applications, stabilizers must be added to improve the stability to heat and light. In terms of specific applications, according to the main properties of PVC products, it can be divided into rigid PVC and soft PVC. Among them, rigid PV...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L33/04C08K13/02C08K3/04C08K5/00C08K3/014
CPCC08L27/06C08L2201/22C08L33/04C08K13/02C08K3/04C08K5/005C08K3/014
Inventor 钱珠明
Owner 华正金属材料(太仓)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap