Aluminum plastic-plated woven film suitable for environmentally-friendly water-based glue and preparation method thereof

A water-based glue and aluminum plating technology, applied in chemical instruments and methods, applications, household appliances, etc., can solve the problems of low peeling strength, waste of wood resources, increase use cost, etc., and achieve high peeling strength and good light-proof performance. , non-volatile effect

Inactive Publication Date: 2018-12-28
FU RONG HUI IND FUJIAN
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional plastic woven bags are generally replaced by paper materials, which cannot be recycled for secondary use, which will not only waste a lot of wood resources, but also increase the user's use cost
At present, the plastic woven film produced by domestic BOPP manufacturers has poor anti-ultraviolet radiation performance. When using environmentally friendly water-based adhesive as a binder and packaging with aluminum-coated plastic woven film, the environmentally friendly water-based adhesive is easy to volatilize under ultraviolet radiation, and the peeling strength is low. Low, the product is not easy to store

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum plastic-plated woven film suitable for environmentally-friendly water-based glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An aluminum-coated plastic woven film suitable for environmentally friendly water-based adhesives, consisting of a surface layer 1, a surface layer 2 and a core layer;

[0014] The surface layer 1 is composed of the following components in parts by weight: F800EDF 96.50% (purchased from Shanghai Petrochemical Co., Ltd.), ABPP905 3.50% (purchased from Shantou Best Technology Co., Ltd.);

[0015] The surface layer 2 is composed of the following components in parts by weight: T30S 96.40% (purchased from Sinochem Quanzhou Co., Ltd.), ABPP905 3.60%;

[0016] The core layer is composed of the following components in parts by weight: L5E89 50% (purchased from Sinochem Quanzhou Co., Ltd.), L5D9850% (purchased from Sinochem Quanzhou Co., Ltd.).

[0017] The preparation method of the aluminum-plated plastic woven film suitable for environmental protection water-based adhesive is: adopt three-layer structure co-extrusion followed by biaxial stretching molding, the process paramete...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminum plastic-plated woven film suitable for environmentally-friendly water-based glue and a preparation method thereof. The aluminum plastic-plated woven film is composed of a surface layer 1, a surface layer 2 and a core layer; the surface layer 1 is composed of, by weight parts, 96.50% of F800EDF and 3.50% of ABPP905; the surface layer 2 is composed of, by weight parts, 96.40% of T30S and 3.60% of ABPP905; the core layer is composed of, by weight parts, 50% of L5E89 and 50% of L5D98. The aluminum plastic-plated woven film suitable for the environmentally-friendly water-based glue is prepared by bi-directional stretching forming after co-extrusion of a three-layer structure and the aluminum plastic-plated woven film is good in light resistance. When the environmentally-friendly water-based glue is used as a binder to use the prepared aluminum plastic-plated woven film for packaging, the environmentally-friendly water-based glue does not volatilize underultraviolet irradiation, has high peeling strength and is environmentally friendly, and the product is easier to store.

Description

technical field [0001] The invention belongs to the field of BOPP film preparation, and in particular relates to an aluminum-coated plastic woven film suitable for environmental protection water-based glue and a preparation method thereof. Background technique [0002] Plastic woven film is a very important flexible packaging material, which is widely used to cover the outside of the woven bag, which can increase the fastness and aesthetics of the product. Traditional plastic woven bags are generally replaced by paper materials, which cannot be recycled for secondary use. This will not only waste a lot of wood resources, but also increase the user's use cost. At present, the plastic woven film produced by domestic BOPP manufacturers has poor anti-ultraviolet radiation performance. When using environmentally friendly water-based adhesive as a binder and packaging with aluminum-coated plastic woven film, the environmentally friendly water-based adhesive is easy to volatilize u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/30B32B27/06B32B33/00B29C69/02B29C47/92B29C47/06B29L7/00
CPCB32B27/30B29L2007/00B32B27/08B32B33/00B32B2307/40
Inventor 单利英王永祥
Owner FU RONG HUI IND FUJIAN