A thermal insulation mortar for building exterior walls with good rheology

A technology for building exterior walls and thermal insulation mortar is applied in the field of external wall thermal insulation mortar, which can solve the problems of unstable thermal insulation performance of products and uneven distribution of lightweight materials.

Active Publication Date: 2021-07-06
温州市工大节能材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the external wall thermal insulation mortar currently sold on the market is not uniform due to the uneven distribution of light materials, resulting in unstable thermal insulation performance of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A thermal insulation mortar for building exterior walls with good rheology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A building exterior wall thermal insulation mortar with good rheology and a manufacturing method thereof,

[0023] The thermal insulation mortar for building exterior walls with good rheology includes parts by weight: 210 parts of cement, 12 parts of superfine phosphorus slag powder, 5 parts of quicklime, 100 parts of sand, 70 parts of modified expanded lightweight aggregate, and 20 parts of rheological agent , 7 parts of hydroxypropyl cellulose, 2 parts of polycarboxylate high-performance water reducer, 90 parts of water,

[0024] The method for manufacturing the thermal insulation mortar for building exterior walls with good rheology includes the following steps: firstly, prepare a rheological agent: heat 150ml of methyl methacrylate to 46-50°C, stir and add 12g of triisopropanolamine, and heat up for 60-70°C ℃, add 5g of sodium xylene sulfonate and 6g of sodium alginate to the reaction kettle, use a magnetic stirrer to stir the reaction at a speed of 230r / min, then a...

Embodiment 2

[0028] A building exterior wall thermal insulation mortar with good rheology and a manufacturing method thereof,

[0029] The building exterior wall thermal insulation mortar with good rheology includes parts by weight: 200 parts of cement, 14 parts of superfine phosphorus slag powder, 9 parts of quicklime, 120 parts of sand, 110 parts of modified expanded lightweight aggregate, and 24 parts of rheological agent , 6 parts of hydroxypropyl cellulose, 5 parts of polycarboxylate high-performance water reducer, 90 parts of water,

[0030] The method for manufacturing the thermal insulation mortar for building exterior walls with good rheology includes the following steps: firstly, prepare a rheological agent: heat 100ml of methyl methacrylate to 46-50°C, add 11g of triisopropanolamine with stirring, and heat up for 60-70°C ℃, add 6g of sodium xylene sulfonate and 6g of sodium alginate to the reaction kettle, use a magnetic stirrer to stir the reaction at a speed of 210r / min, then ...

Embodiment 3

[0034] A building exterior wall thermal insulation mortar with good rheology and a manufacturing method thereof,

[0035] The thermal insulation mortar for building exterior walls with good rheology includes parts by weight: 220 parts of cement, 14 parts of superfine phosphorus slag powder, 10 parts of quicklime, 120 parts of sand, 90 parts of modified expanded lightweight aggregate, and 22 parts of rheological agent , 7 parts of hydroxypropyl cellulose, 5 parts of polycarboxylate high-performance water reducer, 75 parts of water,

[0036]The manufacturing method of the thermal insulation mortar for building exterior walls with good rheological properties includes the following steps: firstly prepare a rheological agent: heat 130ml of methyl methacrylate to 48°C, stir and add 10g of triisopropanolamine, heat up to 62°C, and add to the reaction Add 5g of sodium xylenesulfonate and 7g of sodium alginate to the kettle, and use a magnetic stirrer to carry out stirring reaction at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A building exterior wall thermal insulation mortar with good rheology and a manufacturing method thereof, wherein the rheological good building exterior wall thermal insulation mortar comprises parts by weight: 200-240 parts of cement, 10-15 parts of superfine phosphorous slag powder, 5-5 parts of quicklime 10 parts, 100-120 parts of sand, 50-120 parts of modified expanded lightweight aggregate, 20-25 parts of rheological agent, 5-10 parts of hydroxypropyl cellulose, 2-parts of polycarboxylate high-performance water reducer 6 parts, 70-90 parts of water, the present invention uses modified ball milling agent to carry out ball milling to lightweight aggregate and its surface modification, makes lightweight aggregate particle size more uniform, and improves its surface wettability, and its bone The more uniform the surface wettability of the material, the more uniform its distribution in the slurry.

Description

technical field [0001] The invention relates to a building exterior wall thermal insulation mortar with good rheology, and belongs to the technical field of external wall thermal insulation mortar. Background technique [0002] External wall insulation system is currently the most widely used energy-saving technical measure in my country's building wall energy-saving. It is being popularized across the country and has made great contributions to building energy conservation. Currently on the market, the building insulation system with rubber powder polystyrene particle insulation mortar as the insulation layer occupies a considerable proportion in industrial and civil buildings. But, the external wall insulation mortar sold on the market is not uniform because of the uneven distribution of light materials, which causes the unstable defect of product insulation performance. Thereby there is an urgent need in the market for an exterior wall insulation mortar that improves pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/12C04B20/06C04B20/02C08B37/04
CPCC04B20/023C04B20/06C04B28/12C04B2201/50C08B37/0084C04B7/00C04B14/06C04B24/383C04B2103/302C04B18/145C04B14/14C04B24/166
Inventor 刘刚
Owner 温州市工大节能材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com