Compression test method for honeycomb SCR catalyst

Abstract

The invention relates to a compression test method for a honeycomb SCR catalyst. According to the method, a pressure test machine is used for extruding a catalyst test block at a constant speed; a pressure sensor on the pressure test machine measures a pressure value of the catalyst test block; a pressure curve is drawn by taking the time as horizontal coordinates and the pressure value as vertical coordinates; the curve is composed of a continuous elastic deformation curve S1 and a brittle deformation curve S2; pressure application is stopped after a peak value appears on the brittle deformation curve S2 in the pressure curve; and then a tangent line L1 and a tangent line L2 of the curves S1 and S2 are drawn, the tangent line L1 and the tangent line L2 are intersected, an intersection point is a threshold point of the catalyst test block, and the threshold point of the catalyst test block is defined as a compressive strength value of the catalyst.

Description

technical field [0001] The invention relates to a compression test method for a honeycomb SCR flue gas denitrification catalyst, which belongs to the field of mechanical performance detection of SCR flue gas denitrification catalysts. Background technique [0002] Catalyst is the core of SCR flue gas denitrification technology, and honeycomb catalyst is a kind of commercial SCR flue gas denitrification catalyst that is widely used at present. The mechanical performance of the catalyst is directly related to the safety and reliability of the SCR flue gas denitrification system, and the compressive strength is a key indicator for judging the mechanical performance of the honeycomb catalyst. In the process of honeycomb catalyst production and quality inspection, it is necessary to carry out sampling inspection of the compressive strength of the finished catalyst, so as to ensure that the mechanical properties of the honeycomb catalyst product meet the actual use requirements. ...

AI Technical Summary

Problems solved by technology

In the process of anti-pressure detection of finished catalyst products, the commonly used detection devices are mainly anti-pressure detection devices in the construction/cement industry. The current method has the following problems in the actual use process: 1) The measurement mode is based on a constant liter of 1125N/s The pressure rate is used to squeeze the sample until the sample breaks

Due to the instability of the catalyst structure during the rapid pressurization process, it is easy to cause large errors in the measurement results, high degree of dispersion, and poor reproducibility. It is impossible to accurately determine the real mechanical properties of the honeycomb SCR flue gas denitrification catalyst.

2) The detectio...