A ramie and artificial technology is applied in the field of preparation of ramie-made artificial wig fibers, which can solve the problems of poor qualitative effect, not easy to knot, easy to change color, and deteriorate, and achieves great market promotion and application value, raw material safety and environmental protection, A wide range of effects

Inactive Publication Date: 2019-02-01
太和县慧美发制品有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Wigs are called "fashion on the head". Various types of wigs meet people's diverse needs. Wearing wigs can not only be used as a substitute for sparse hair, but also as a decoration that cannot be used in various popular beauty treatments in recent years. The material of the wig There are materials such as real hair, plant fiber or chemical fiber. The wig made of human hair is made of treated pure human hair. It has high fidelity and is not easy to knot. The price is high, the qualitative effect is not very good, and the sources of human hair raw materials are very limited; chemical fiber wigs are made of chemical fibers, although the price is low, but the fidelity is poor, and it is easy to cause scalp allergies when worn; plant fibers have a wide range of sources , low price, and safe to wear, but it is easy to change color, deteriorate, or even break if it is used for a long time, and it will be infected by bacteria and mites if it is placed for a long time. Mites and wig fibers with stable performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing ramie artificial wig fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of preparation method of ramie artificial wig fiber, comprises the steps:

[0031] (1) Acid treatment:

[0032] Put the ramie stems in the acid solution for stirring treatment, keep the temperature of the acid solution at 46°C during the stirring treatment, and after stirring for 36 minutes, filter out the ramie stems for later use;

[0033] (2) Alkaline treatment:

[0034] The castor stems treated with the acid solution in step (1) are placed in the lye for stirring treatment, and the temperature in the lye is kept at 61°C during the stirring treatment, and after stirring for 24 minutes, the ramie stems are filtered out for later use;

[0035] (3) Crushing treatment:

[0036] Put the ramie stems treated with alkali solution in step (2) into a cryogenic pulverizer for pulverization, the temperature in the pulverizer is controlled at -17°C, after pulverization for 42 minutes, pass through a 30-mesh sieve for later use;

[0037] (4) Soaking treatment:

[0038] ...

Embodiment 2

[0052] A kind of preparation method of ramie artificial wig fiber, comprises the steps:

[0053] (1) Acid treatment:

[0054] Put the stems of ramie in the acid solution for stirring treatment, keep the temperature of the acid solution at 47°C during the stirring treatment, and after stirring for 40 minutes, filter out the stems of ramie for later use;

[0055] (2) Alkaline treatment:

[0056] The castor stems treated with the acid solution in step (1) are placed in the lye for stirring treatment, and the temperature in the lye is kept at 62°C during the stirring treatment, and after stirring for 26 minutes, the ramie stems are filtered out for later use;

[0057] (3) Crushing treatment:

[0058] Put the ramie stems treated with alkali solution in step (2) into a cryogenic pulverizer for pulverization, the temperature in the pulverizer is controlled at -15°C, after pulverization for 45 minutes, pass through a 30-mesh sieve for later use;

[0059] (4) Soaking treatment:

[...

Embodiment 3

[0074] A kind of preparation method of ramie artificial wig fiber, comprises the steps:

[0075] (1) Acid treatment:

[0076] Put the stems of ramie in the acid solution for stirring treatment, keep the temperature of the acid solution at 48°C during the stirring treatment, and after stirring for 44 minutes, filter out the stems of ramie for later use;

[0077] (2) Alkaline treatment:

[0078] The castor stems treated with the acid solution in step (1) are placed in the lye for stirring treatment, and the temperature in the lye is kept at 63°C during the stirring treatment, and after stirring for 28 minutes, the ramie stems are filtered out for later use;

[0079] (3) Crushing treatment:

[0080] Put the ramie stems treated with alkali solution in step (2) into a cryogenic pulverizer for pulverization, the temperature in the pulverizer is controlled at -13°C, after pulverization for 48 minutes, pass through a 30-mesh sieve for later use;

[0081] (4) Soaking treatment:

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing ramie artificial wig fiber. The method comprises the following steps: (1) acid solution treatment; (2) alkali lye treatment; (3) pulverization treatment;(4) immersion treatment; and (5) preparation of ramie fiber. The artificial wig fiber finally obtained by the invention has excellent toughness, and has the characteristics of antibacterial, anti-mite, heatproof, temperature-resistant and flame retardant performance, the raw materials are safe and environmentally friendly, and have a wide range of sources, which are beneficial to the human body,so that the artificial wig fiber has great market application value.

Description

technical field [0001] The invention belongs to the technical field of wig fiber preparation, in particular to a method for preparing artificial wig fiber made from ramie. Background technique [0002] In recent years, wigs have entered people's lives as a new fashion consumer product. Wigs are called "fashion on the head". Various types of wigs meet people's diverse needs. Wearing wigs can not only be used as a substitute for sparse hair, but also as a decoration that cannot be used in various popular beauty treatments in recent years. The material of the wig There are materials such as real hair, plant fiber or chemical fiber. The wig made of human hair is made of treated pure human hair. It has high fidelity and is not easy to knot. The price is high, the qualitative effect is not very good, and the sources of human hair raw materials are very limited; chemical fiber wigs are made of chemical fibers, although the price is low, but the fidelity is poor, and it is easy to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/02D01F8/18D01F1/10D01F1/07D01F2/00
CPCD01F8/02D01F1/07D01F1/103D01F2/00D01F8/18
Inventor 田建峰
Owner 太和县慧美发制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com