Method for preparing barium chloride by high-calcium witherite

A technology of witherite and barium chloride, which is applied in the field of producing barium chloride from high-calcium witherite ore, can solve problems such as low reserves of high-quality ore and difficulty in using witherite, and achieves high output, low steam consumption and electric energy consumption, high purity effect

Inactive Publication Date: 2019-02-15
宜昌华昊新材料科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies in the prior art, the present invention provides a method for producing barium chloride from high-calcium witherite ore, which has the advantage that high-calcium witherite ore can produce barium chloride in large quantities at low cost, and solves the problem of continuous production of barium chloride with the continuous increase in mining volume. Increasingly, high-quality ore reserves are becoming less and less, and witherite with low grade and calcium carbonate content greater than 25% is difficult to utilize

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The method for preparing barium chloride from high-calcium witherite ore comprises the following raw materials in parts by weight: .

[0025] The preparation method of the method for producing barium chloride from high-calcium witherite ore comprises the following steps: 100KG barium carbonate content is between 40%-55%, calcium carbonate content is at 25%-30% high-calcium witherite ore, concentration It is 32% high concentration hydrochloric acid.

[0026] 1) Get 100KG barium carbonate content between 40%-55%, calcium carbonate content in 25%-30% high-calcium witherite ore, wash and place it in a ventilated place to dry for later use.

[0027] 2) introducing a sufficient amount of 32% high-concentration hydrochloric acid solution into the reaction tank, and putting the high-calcium witherite ore in step 1) into the reaction tank until the high-calcium witherite ore is completely reacted.

[0028] 3) After the reaction is complete, pass the mixed solution through prima...

Embodiment 2

[0033] The method for preparing barium chloride from high-calcium witherite ore comprises the following raw materials in parts by weight: .

[0034] The preparation method of the method for producing barium chloride from high-calcium witherite ore comprises the following steps: 100KG barium carbonate content is between 40%-55%, calcium carbonate content is at 25%-30% high-calcium witherite ore, concentration It is 26% high concentration hydrochloric acid.

[0035] The preparation method of the method for producing barium chloride from high-calcium witherite ore comprises the following steps: 100KG barium carbonate content is between 40%-55%, calcium carbonate content is at 25%-30% high-calcium witherite ore, concentration It is 26% high concentration hydrochloric acid.

[0036] 1) Get 100KG barium carbonate content between 40%-55%, calcium carbonate content in 25%-30% high-calcium witherite ore, wash and place it in a ventilated place to dry for later use.

[0037] 2) introd...

Embodiment 3

[0043] The method for preparing barium chloride from high-calcium witherite ore comprises the following raw materials in parts by weight: .

[0044] The preparation method of the method for producing barium chloride from high-calcium witherite ore comprises the following steps: 100KG barium carbonate content is between 40%-55%, calcium carbonate content is at 25%-30% high-calcium witherite ore, concentration It is 38% high concentration hydrochloric acid.

[0045] 1) Get 100KG barium carbonate content between 40%-55%, calcium carbonate content in 25%-30% high-calcium witherite ore, wash and place it in a ventilated place to dry for later use.

[0046]2) introducing a sufficient amount of 38% high-concentration hydrochloric acid solution into the reaction tank, and putting the high-calcium witherite ore in step 1) into the reaction tank until the high-calcium witherite ore is completely reacted.

[0047] 3) After the reaction is complete, pass the mixed solution through primar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing barium chloride by high-calcium witherite. The method comprises the following raw materials by weight: 100 KG of high-calcium witherite with a barium carbonate content of 40-55 percent and a calcium carbonate content of 25-30 percent, and high-concentration hydrochloric acid with a concentration of 32 percent. The method for preparing the barium chloride by the high-calcium witherite, disclosed by the invention, has the benefits that by utilizing a common-ion effect, the high-concentration hydrochloric acid is adopted for reaction; the high-concentration hydrochloric acid is adopted for reaction with ores, calcium chloride produced by the reaction is fully dissolved in water brought by the hydrochloric acid, only a very small amount of produced barium chloride is dissolved in the water, and most of produced barium chloride exist in barium slag in a solid form; through primary filtration, a filtered liquid is a calcium chloride liquid, thecalcium chloride is removed, and then filter residues enter beating barrel for beating with water; the barium chloride in the barium slag is completely leached out to obtain barium chloride liquid with high purity, and then the barium chloride liquid is used for evaporative crystallization, so that the obtained product is high in purity and high in yield, and the steam consumption and the power consumption per ton of products are low.

Description

technical field [0001] The invention relates to the field of barium chloride preparation, in particular to a method for preparing barium chloride from high-calcium witherite ore. Background technique [0002] Barium chloride is a white crystal, easily soluble in water, slightly soluble in hydrochloric acid and nitric acid, insoluble in ethanol and ether, easy to absorb moisture, needs to be sealed and stored, used as analytical reagent, dehydrating agent and barium salt, and used in electronics, Instrumentation and metallurgy industries, mainly used in metal heat treatment, barium salt manufacturing and electronic instruments, also used as heat treatment agent in mechanical processing, determination of sulfate and selenate, chromatographic analysis, spot analysis determination of platinum, water softener and fabric dyeing. [0003] For the production method of barium chloride proposed by Chinese patent CN105967216B, the method utilizes a ball mill to grind barium slag with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01F11/28
CPCC01F11/28
Inventor 林福平
Owner 宜昌华昊新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products