Wear-resistant waterproof breathable antibacterial cloth
A waterproof and breathable fabric technology, applied in the field of wear-resistant, waterproof, breathable and antibacterial fabrics, can solve the problems of non-bacterial, poor waterproof and breathable performance, and unreasonable ingredients, and achieve the effects of uniform thickness, enhanced toughness, and high wear resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A wear-resistant, waterproof, breathable and antibacterial cloth, comprising the following components in parts by weight:
[0025] 25 parts of high-pressure polyethylene, 25 parts of low-pressure polyethylene, 0.2 parts of nano-silver, 1.6 parts of hydroxyethyl cellulose, 5 parts of alkyd resin, 1 part of silane coupling agent, 0.1 part of zinc oxide, and 4 parts of polymer plastics.
[0026] The preparation process of the wear-resistant, waterproof, breathable and antibacterial cloth includes the following steps:
[0027] 1) Fully mix low-pressure polyethylene, alkyd resin, high-pressure polyethylene, and polymer plastics in an ultrasonic generator for 3-5 minutes, and pass through a 200-250-mesh sieve;
[0028] 2) Add hydroxyethyl cellulose to deionized water, stir evenly at 40-50°C at a speed of 900-1500r / min;
[0029] 3) Add nano-silver, coupling agent and zinc oxide in sequence, and heat up to 60°C for 1.5-2 hours;
[0030] 4) Use a Buchner funnel to filter and s...
Embodiment 2
[0032] A wear-resistant, waterproof, breathable and antibacterial cloth, comprising the following components in parts by weight:
[0033] 40 parts of high-pressure polyethylene, high-pressure polyethylene is calcite-type cubic nano-particles, its particle size ≤ 50nm, 15 parts of low-pressure polyethylene, 0.6 parts of nano-silver, 0.8 parts of hydroxyethyl cellulose, 2 parts of alkyd resin, borate 3 parts of coupling agent, 0.5 parts of zinc oxide, 8 parts of polymer plastic.
[0034] The preparation process of the wear-resistant, waterproof, breathable and antibacterial cloth includes the following steps:
[0035] 1) Fully mix low-pressure polyethylene, alkyd resin, high-pressure polyethylene, and polymer plastics in an ultrasonic generator for 3 to 5 minutes, and pass through a sieve of 200 to 250 mesh; the power of the ultrasonic generator is 1.2KW, and the time is 15 minutes , the working method is intermittent work, every 30 seconds of work, 30 seconds of pause;
[003...
Embodiment 3
[0040] A wear-resistant, waterproof, breathable and antibacterial cloth, comprising the following components in parts by weight:
[0041] 30 parts of high-pressure polyethylene, high-pressure polyethylene is calcite-type cubic nanoparticles, and its particle size is ≤ 50nm;
[0042] 22 parts of low-pressure polyethylene, 0.4 parts of nano-silver, 1.2 parts of hydroxyethyl cellulose, 3.5 parts of alkyd resin,
[0043] 2 parts of silane coupling agent, titanate coupling agent and aluminate coupling agent with a mass ratio of 2:3 to 5:1, 0.3 part of zinc oxide, and 6 parts of polymer plastic.
[0044] The preparation process of the wear-resistant, waterproof, breathable and antibacterial cloth includes the following steps:
[0045] 1) Fully mix low-pressure polyethylene, alkyd resin, high-pressure polyethylene, and polymer plastics in an ultrasonic generator for 3-5 minutes, and pass through a 200-250-mesh sieve; the power of the ultrasonic generator is 1.5KW, and the time is 5 ...