Preparation method of soft tile particles

A particle and soft porcelain technology, which is applied in the field of preparation of soft porcelain particles, can solve the problems of poor mixing effect, poor dispersion effect, and low degree of automation, and achieve good mixing effect, good dispersion effect, and high degree of automation.

Active Publication Date: 2019-04-02
HUBEI WANSHUO NEW MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the defects and problems of poor dispersion effect, poor mixing effect and low degree of automation in the prior art, and provide a method for preparing soft porcelain particles with good dispersion effect, good mixing effect and high degree of automation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of soft tile particles

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] see figure 1 , a preparation method of soft porcelain particles, the preparation method comprising the following steps:

[0028] A. Prepare the raw materials of soft porcelain particles. The raw material composition and weight percentage of soft porcelain particles are: modified soil 55%~65%, modified inorganic powder 10%~15%, high molecular polymer and nanomaterials 15%~ 25%, plant fiber 2%~4%, multifunctional additive 0.5%~2%;

[0029] B. First add the plant fiber into the No. 1 dispersion tank 1 for dispersion, then add the modified soil and modified inorganic powder into the No. 2 dispersion tank 2 for dispersion and mixing, and then add the dispersed plant fiber into the No. 2 dispersion tank 2 Disperse and mix with the modified soil and modified inorganic powder, and then transport the dispersed and mixed plant fibers, modified soil and modified inorganic powder to the mixing tank 3;

[0030] The bottom of the No. 1 dispersing tank 1 communicates with the top of...

Embodiment 1

[0047] see figure 1 , a preparation method of soft porcelain particles, the preparation method comprising the following steps:

[0048] A. Prepare the raw materials of soft porcelain particles. The raw material composition and weight percentage of soft porcelain particles are: modified soil 55%~65%, modified inorganic powder 10%~15%, high molecular polymer and nanomaterials 15%~ 25%, plant fiber 2%~4%, multifunctional additive 0.5%~2%;

[0049] B. First add the plant fiber into the No. 1 dispersion tank 1 for dispersion, then add the modified soil and modified inorganic powder into the No. 2 dispersion tank 2 for dispersion and mixing, and then add the dispersed plant fiber into the No. 2 dispersion tank 2 Disperse and mix with the modified soil and modified inorganic powder, and then transport the dispersed and mixed plant fibers, modified soil and modified inorganic powder to the mixing tank 3;

[0050] The bottom of the No. 1 dispersing tank 1 communicates with the top of...

Embodiment 2

[0055] Basic content is the same as embodiment 1, the difference is:

[0056] see figure 1 , the top of the No. 1 dispersion tank 1 is provided with an air inlet 17 , and the position above the screw rod 13 in the No. 1 dispersion tank 1 is provided with a fan 18 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of soft tile particles. The preparation method comprises the following steps that A, raw materials of the soft tile particles are prepared, the soft tile particles are prepared from the raw material components in percentage by weight: 55-65% of modified clay, 10-15% of modified inorganic powder, 15-25% of high-molecular polymer and nanomaterials, 2-4% ofplant fiber, and 0.5-2% of a multi-functional addition agent; B, firstly, the plant fiber is added into a first dispersion tank to be dispersed, the modified clay and the modified inorganic powder are added into a second dispersion tank to be dispersed and mixed, then the dispersed plant fiber is added into the second dispersion tank to be dispersed and mixed, and then the dispersed and mixed plant fiber, the modified clay and the modified inorganic powder are conveyed into a stirring tank; and C, the high-molecular polymer, the nanomaterials, the multi-functional addition agent and water areadded into the stirring tank to be stirred and mixed, and thus the soft tile particles are obtained. The preparation method is good in disperse effect, good in mixing effect and high in automation degree.

Description

technical field [0001] The invention relates to the technical field of soft porcelain production, in particular to a method for preparing soft porcelain particles, which is mainly suitable for improving the dispersion effect and mixing effect of soft porcelain raw materials, and the automation degree of dispersion and mixing of soft porcelain raw materials. Background technique [0002] Soft porcelain is a new type of energy-saving and low-carbon decorative material. As a wall decoration material, it has the characteristics of light weight, good flexibility, various appearance shapes, and good weather resistance; as a floor decoration material, it has wear-resistant, non-slip, feet Features such as comfort. The construction of soft porcelain is simple and fast. Compared with traditional materials, it shortens the construction period, saves space and cost, and is not easy to fall off. In the production process of soft porcelain, the soft porcelain particles are prepared firs...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28C3/00B28C7/06B28C7/16B26D1/29
CPCB26D1/29B28C3/00B28C7/06B28C7/16
Inventor 高祥
Owner HUBEI WANSHUO NEW MATERIAL