High-temperature-resistant glue

A technology of high temperature resistance and glue, which is applied in the direction of adhesives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc. It can solve problems such as factory troubles, glues that cannot be found, and glues that do not have high temperature resistance. Achieve the effect of high temperature resistance performance improvement, rich functionality, and improved use effect

Inactive Publication Date: 2019-04-02
王小明
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing glues generally do not have good high temperature resistance, which makes these glues unsuitable for some high temperature workshops. These high temperature workshops cannot find suitable glue for use, which brings great trouble to the factory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A high temperature resistant glue, consisting of the following components in parts by weight:

[0018] 15 parts of petroleum resin, 6 parts of polyisobutyl ester, 3 parts of borax, 5 parts of quartz powder, 1 part of styrene, 5 parts of EVA resin, 10 parts of fly ash, 3 parts of calcium formate, 4 parts of n-butanol, oxidized water 30 servings.

Embodiment 2

[0020] A high temperature resistant glue, consisting of the following components in parts by weight:

[0021] 20 parts of petroleum resin, 10 parts of polyisobutyl ester, 6 parts of borax, 15 parts of quartz powder, 3 parts of styrene, 10 parts of EVA resin, 15 parts of fly ash, 8 parts of calcium formate, 8 parts of n-butanol, oxidized water 50 servings.

Embodiment 3

[0023] A high temperature resistant glue, consisting of the following components in parts by weight:

[0024] 17 parts of petroleum resin, 8 parts of polyisobutyl ester, 4 parts of borax, 10 parts of quartz powder, 2 parts of styrene, 7 parts of EVA resin, 12 parts of fly ash, 6 parts of calcium formate, 6 parts of n-butanol, oxidized water 40 servings.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature-resistant glue, which comprises, by weight, 15-20 parts of a petroleum resin, 6-10 parts of polyisobutyl ester, 3-6 parts of borax, 5-15 parts of quartz powder, 1-3 parts of styrene, 5-10 parts of an EVA resin, 10-15 parts of fly ash, 3-8 parts of calcium formate, 4-8 parts of n-butanol, and 30-50 parts of oxidized water. Compared with the high-temperature-resistant glue in the prior art, the high-temperature-resistant glue of the present invention has substantially improved high-temperature resistance, can be used in a lot of high-temperature workshops, and further has advantages of enriched functionality and improved use effect.

Description

technical field [0001] The invention specifically relates to a high temperature resistant glue. Background technique [0002] Existing glues generally do not have good high temperature resistance, which makes these glues unsuitable for some high-temperature workshops. These high-temperature workshops cannot find suitable glue for use, which brings great trouble to the factory. Contents of the invention [0003] Purpose of the invention: In order to overcome the deficiencies in the prior art, provide a glue with good high temperature resistance. [0004] Technical solution: In order to achieve the above purpose, the present invention provides a high temperature resistant glue, which consists of the following components in parts by weight: [0005] 15-20 parts of petroleum resin, 6-10 parts of polyisobutyl ester, 3-6 parts of borax, 5-15 parts of quartz powder, 1-3 parts of styrene, 5-10 parts of EVA resin, 10-15 parts of fly ash , 3-8 parts of calcium formate, 4-8 parts o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06C09J11/04C09J11/06
CPCC09J4/06C09J11/04C09J11/06
Inventor 王小明
Owner 王小明