Nanoparticles, preparation method and application thereof, medicament

A nanoparticle and nanorod technology, applied in the field of nanoparticles, can solve the problems of low spatial resolution of photoacoustic imaging, high autofluorescence background, poor photothermal treatment effect, etc., achieve high spatial resolution, avoid abuse, improve The effect of photothermal therapy effect

Active Publication Date: 2021-03-23
SHENZHEN INST OF ADVANCED TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The current photothermal antibacterial effect of gold nanomaterials is usually limited to photothermal therapy in the near-infrared region, but the photothermal therapy tissue penetration depth in the first region is shallow, the effect of photothermal therapy is poor, and the spatial resolution of photoacoustic imaging is relatively low. Low, but with high autofluorescence background

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nanoparticles, preparation method and application thereof, medicament
  • Nanoparticles, preparation method and application thereof, medicament
  • Nanoparticles, preparation method and application thereof, medicament

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0089] According to a second aspect of the present invention, there is provided a method for preparing the aforementioned nanoparticles, comprising the following steps:

[0090] Au / Ag nanorods are obtained by growing silver shells on the surface of gold nanorods.

[0091] The method for growing the silver shell layer can be carried out by using a conventional method for growing nanoparticles with a core-shell structure.

[0092] In one embodiment, the step of growing a silver shell layer on the surface of the gold nanorod comprises:

[0093] A surfactant solution, a silver source solution and a reducing agent solution are added to the gold nanorod-water dispersion liquid for mixed reaction to obtain Au / Ag nanorods.

[0094] The gold nanorod-water dispersion refers to a dispersion obtained by dispersing gold nanorods in water. The concentration of gold nanorods in the dispersion is, for example, 4 μg / mL, 5 μg / mL, 6 μg / mL, 7 μg / mL, 8 μg / mL, 9 μg / mL or 10 μg / mL.

[0095] A typ...

Embodiment approach

[0111] An exemplary embodiment, the preparation method of gold nanorods comprises the following steps:

[0112] (a) For every 0.1-20mL of 0.1-2mol / L gold source solution, add 0.1-20mL of 0.1-1mol / L surfactant solution and mix well; then, add 0.1-200μL of 0.1-2mol / L Mix the silver source solution evenly; add 0.1-2mL 0.1-2mol / L reducing agent solution after 60-3600min and mix evenly;

[0113] (b) Disperse the solution obtained in step (a) with a 1-1500W cell crushing device, add 0.1-200 μL of 0.1-2 mol / L fresh ice-cold reducing agent solution, and ultrasonically mix for 60 minutes after being treated by the cell crushing device for 1-10 minutes -3600min, to obtain gold nanorods.

[0114] It should be noted here that the above volumes are all relative amounts, for example, 0.1-20 mL of surfactant solution is added for every 0.1-20 mL of gold source solution.

[0115] The reducing agent in step (a) is ascorbic acid, and the reducing agent in step (b) is sodium borohydride.

[0...

Embodiment 1

[0166] A nanorod, the core is a gold nanorod with an aspect ratio of 4, and the shell is a 2nm thick silver shell.

[0167] A method for preparing nanorods, comprising the following steps:

[0168] (1) 0.17mL of 0.05M HAuCl 4 The solution was added into 20mL 0.1M CTAB solution, and stirred vigorously to mix the solution evenly, and the solution was bright brownish yellow. Then, 70 μL of 0.1M AgNO 3 Add dropwise to the above solution, and stir vigorously to mix the solution evenly. After 5 min, 0.12 mL of 0.1 M ascorbic acid solution was added, and the solution was mixed evenly with vigorous stirring, and the solution became colorless. Disperse the above solution with a 1500W cell disruptor, and immediately add 8 μL of 0.001M ice-cold NaBH 4 The aqueous solution was treated with a cell disruptor for 5 minutes and then stirred rapidly for 120 minutes. The solution turned purple, and the product Au NR was successfully prepared. Centrifuge the product at 13000rpm for 12min, d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nano particle, its preparation method, application and medicament, and relates to the technical field of nano particles. The nanoparticle of the present invention includes a gold nanorod core and a silver shell layer coated on the outer surface of the gold nanorod. The aspect ratio of the gold nanorod is 4-8, and can further be made into Au / Ag / Au nanorod or Au / Ag / Au nanostars. The wavelength of the LSPR maximum absorption peak of the nanoparticles of the present invention falls in the second near-infrared region, which has a higher photothermal conversion efficiency than the first infrared region, has a good photothermal treatment effect, and is more conducive to the ablation of bacterial cells. Photoacoustic imaging has higher tissue penetration depth, high temporal and high spatial resolution. Ag released from the outer Ag shell + The antibacterial effect of Au and the photothermal sterilization effect of internal Au cooperate synergistically, and the sterilization efficiency is higher. The nanoparticles of the present invention can be used in photoacoustic imaging and bacterial infection diagnosis and treatment agents, and can non-invasively monitor Ag + Topical release and photothermotherapy process.

Description

technical field [0001] The invention relates to the technical field of nanoparticles, in particular, to a nanoparticle, its preparation method, application, and medicament. Background technique [0002] The discovery of antibiotics once saved millions of lives from deadly infections. However, with the long-term irregular use of antibiotics, drug-resistant bacteria have become a global problem; the most serious of which is methicillin-resistant grapevine. Cocci (Methicilin-resistant Staphylococcusaureus, MRSA). By the 1980s, MRSA had spread all over the world and became one of the common clinical pathogens. In recent years, the detection rate of MRSA has been on the rise, which can lead to diseases such as toxic shock syndrome and suppurative infection. Common antimicrobial drugs are ineffective, and the mortality rate is high. At present, MRSA has emerged multi-drug resistance, which poses an increasingly serious threat to human health and poses severe challenges to clinic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00B22F1/02C23C18/44A61K49/22A61K41/00A61K9/51A61P31/04A61K33/38
CPCA61K41/0052A61K49/225A61P31/04A61K9/5115A61K33/38C23C18/44B22F1/054B22F1/17A61K2300/00
Inventor 郑海荣胡德红盛宗海刘新
Owner SHENZHEN INST OF ADVANCED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap