A kind of sodium sulfide slag preparation method of thermal insulation wall material

A technology for insulating walls and sodium sulfide, which is applied in the production of ceramic materials, clay products, and other household appliances, etc., to achieve the effect of reducing the amount of addition

Active Publication Date: 2021-07-20
SOUTHWEAT UNIV OF SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Stockpiling takes up arable land and there are potential environmental risks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sodium sulfide slag preparation method of thermal insulation wall material
  • A kind of sodium sulfide slag preparation method of thermal insulation wall material
  • A kind of sodium sulfide slag preparation method of thermal insulation wall material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be described in further detail below in conjunction with specific examples.

[0024] (1) Sodium sulfide slag pretreatment: Add water, surfactant, acid, and oxidant to sodium sulfide slag, mix and filter evenly to obtain pretreated sodium sulfide slag. The table below shows 20 examples of sodium sulfide slag pretreatment formula numbers 1-20.

[0025] Table 1

[0026]

[0027] Explanation: The addition amount of sulfuric acid, nitric acid and hydrochloric acid in the table is according to H 2 SO 4 、HNO 3 and HCl calculations.

[0028] (2) Preparation of thermal insulation wall materials: Add activated mud, plasticizer, and heating aid to the pretreated sodium sulfide slag and mix evenly, pour it into a mold and mold it, put it in an oven to dry, and put it in the furnace after drying Calcined to obtain thermal insulation wall material. The following table is 20 embodiments of the wall material formula numbered 1-20.

[0029] Table 2 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This patent discloses a method for preparing a thermal insulation wall material from sodium sulfide slag. Water, a surfactant, an acid, and an oxidizing agent are added to the sodium sulfide slag, mixed uniformly and filtered to obtain pretreated sodium sulfide slag. Add activated mud, plasticizer and heating aid to the pretreated sodium sulfide slag, mix evenly, pour it into a mold for molding, put it in an oven for drying, and put it in a furnace for calcination after drying to obtain a thermal insulation wall material. The enamel material prepared from the tailings is coated on the surface of the thermal insulation wall material to increase the functionality of the wall material. Compared with the existing technical solutions, the method has the characteristics of low production cost, comprehensive utilization of resources and high added value of products.

Description

technical field [0001] The invention relates to the field of resource utilization of industrial waste slag, in particular to a method for the resource utilization of sodium sulfide slag for preparing wall insulation materials. Background technique [0002] High-temperature reduction of sodium sulfate by pulverized coal is currently the main method for domestic production of sodium sulfide. It uses ordinary high-ash coal to reduce sodium sulfate at high temperature (mostly 90% weathered nitric acid) to obtain sodium sulfide "black ash", and then through leaching and sedimentation , washing, evaporation and a series of follow-up treatments to obtain a product with a sodium sulfide content of 60% [Zhao Xiuping, Jing Xiaobing, Su Gang. Research on the preparation of sodium sulfide by one-step method of reducing sodium sulfate from ultra-low ash pure coal[J]. Salt Industry and Chemical Industry , 2015, 44(12): 36-40]. In the production process of sodium sulfide, the slag obtaine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/132C04B33/13C04B41/86
CPCC04B33/1305C04B33/131C04B33/132C04B33/1321C04B41/5022C04B41/86Y02P40/60
Inventor 谭宏斌董发勤李玉香马小玲王进贺小春吴浪张魁宝
Owner SOUTHWEAT UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap