Preparing method of alloy magnesium rod

An alloy and magnesium rod technology, applied in the field of magnesium rod preparation, can solve the problems of high copper prices and high cost of brass rods

Inactive Publication Date: 2019-04-23
王磊
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Brass rods are widely used in air-conditioning pipes, refrigerator pipes, oil pipes, water supply pipes and v

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0019] Add copper, sodium and magnesium to an industrial furnace for smelting; gradually add magnesium ingots until the composition requirements are met, wherein the mass percentage of copper is 0.1%, the mass percentage of sodium is 0.05%, and the rest is the magnesium; adding Refining agent sodium chloride, stirring and refining; pour the refined alloy melt into the holding furnace and let it stand, the temperature is controlled at 450°C; after extrusion, peeling and wire drawing, a round alloy with a diameter of 5mm and a length of 6m is obtained Magnesium rods.

Embodiment example 2

[0021] Add copper, sodium and magnesium to an industrial furnace for smelting; gradually add magnesium ingots until the composition requirements are met, wherein the mass percentage of copper is 1%, the mass percentage of sodium is 0.08%, and the rest is the magnesium; The refining agent potassium chloride is used for stirring and refining; the refined alloy melt is poured into the holding furnace for standing, and the temperature is controlled at 500°C; after extrusion, peeling and wire drawing, a square alloy magnesium with a diameter of 50mm and a length of 10m is obtained Great.

[0022] The finished alloy magnesium wire.

Embodiment example 3

[0024] Add copper, sodium and magnesium to an industrial furnace for smelting; gradually add magnesium ingots until the composition requirements are met, wherein the mass percentage of copper is 2%, the mass percentage of sodium is 0.1%, and the rest is the magnesium; adding Refining agent ammonium chloride is used for stirring and refining; the refined alloy melt is flowed into the holding furnace for standing, and the temperature is controlled at 480°C; after extrusion, peeling and wire drawing, a hexagonal shape with a diameter of 100mm and a length of 2m Alloy magnesium rod.

[0025] According to the embodiment provided by the present invention, the obtained alloy magnesium rods can be drawn into alloy magnesium rods of different lengths, diameters, and shapes according to requirements, and their mechanical properties and corrosion resistance are equivalent to those of brass rods, and the cost is greatly reduced.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparing method of an alloy magnesium rod. The preparing method comprises following steps that copper, sodium and magnesium are added into an industrial furnace to be smelted; a magnesium ingot is added step by step until the component need is achieved, the mass percent of the copper is 0.1 to 2%, the mass percent of the sodium is 0.05 to 0.1%, and the balance is magnesium; a refining agent is added, and stirring refining is carried out; the refined alloy melt is subjected to heat preservation, and the temperature is controlled to range from 450 to 500 DEG C; and through pressurized extrusion, the alloy magnesium rod is obtained. The alloy magnesium rod obtained through the preparing method can be drawn into different lengths, diameters and shapes according to needs, the mechanical property, and corrosion resistance of the magnesium rod are equivalent to those of the brass rod, and the cost is greatly reduced.

Description

technical field [0001] The invention relates to the technical field of magnesium rod preparation, in particular to a copper-sodium-magnesium alloy magnesium rod. Background technique [0002] Brass rods are widely used in air-conditioning pipes, refrigerator pipes, oil pipes, water supply pipes and various mechanical supporting materials, but the price of copper remains high, resulting in a high cost of brass rods. Replacing brass rods with a less expensive metal rod has become a common challenge in the industry. Contents of the invention [0003] The purpose of the present invention is to provide a method for preparing magnesium alloy rods. The magnesium alloy rods obtained by the preparation method can be drawn into different lengths, diameters, and shapes according to requirements, and their mechanical properties and corrosion resistance are equivalent to those of brass rods. Dropped significantly. [0004] The present invention provides a kind of preparation method o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/02C22C1/06C22C23/00
CPCC22C1/02C22C1/06C22C23/00
Inventor 王磊
Owner 王磊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap