Adhesive resin for continuous fiber reinforced plastic composite pipe and preparation method thereof

A technology of reinforced plastics and bonding resins, applied in the direction of adhesives, adhesive types, adhesive additives, etc., can solve the problems of inability to quickly and continuously construct, unfavorable environmental protection, construction efficiency and environmental protection problems, etc., to achieve light weight, Improve the bonding effect and the effect of good adhesion

Active Publication Date: 2022-03-11
GUANGZHOU LUSHAN NEW MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent can achieve full infiltration of continuous fibers through the solution impregnation process, and can produce chain extension reaction after co-vulcanization with rubber to improve the bonding strength. Oxazoline and cycloethylene glycol will cause VOC problems, which is not conducive to environmental protection, and construction efficiency and environmental protection problems cannot meet the requirements of modern industrial systems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive resin for continuous fiber reinforced plastic composite pipe and preparation method thereof
  • Adhesive resin for continuous fiber reinforced plastic composite pipe and preparation method thereof
  • Adhesive resin for continuous fiber reinforced plastic composite pipe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The preparation method of the above-mentioned adhesive resin for continuous fiber reinforced plastic composite pipes comprises the following steps: grafting the weighed polyolefin with silane, compatibilizer, polyolefin matrix resin, elastomer tackifying resin, processing anti-aging aid After being dried separately, it is pre-mixed by a high-speed mixer and then added to the twin-screw extruder; the reactive polyurethane is heated and then added to the twin-screw extruder by online metering and filling; it is extruded and bonded after twin-screw mixing Resin; after multi-stage air cooling, granulation and sealed packaging, the whole process is dried to prevent the entry of water vapor; the adhesive resin for continuous fiber reinforced plastic composite pipes is obtained.

[0033] As a further embodiment, the temperature in the twin-screw extruder is 200° C., the screw speed is 300 rpm, the feeding is 7 Hz, and the twin-screw length-to-diameter ratio L / D is 38:1.

Embodiment 1

[0036] An adhesive resin for continuous fiber-reinforced plastic composite pipes, which is prepared from the following components in percentage by weight:

[0037]

[0038]

[0039] Among them, polyethylene grafted silane is High-density polyethylene grafted silane (melt flow rate MI: 2.0g / 10min, melting point Tm: 134°C, grafting rate GR: 0.8%) 100%;

[0040] Reactive polyurethane is Reactive polyurethane PUR 9350;

[0041] compatibilizer is Ethylene-butyl acrylate copolymer EBA 3427;

[0042] Polyethylene matrix resin is 60% High-density polyethylene DGDA-2399, 40% High-density polyethylene TR480;

[0043] Elastomeric tackifying resins are Polyolefin elastomer POE 8200;

[0044] Processing anti-aging additives are Antioxidant B215.

Embodiment 2

[0046] An adhesive resin for continuous fiber-reinforced plastic composite pipes, which is prepared from the following components in percentage by weight:

[0047]

[0048] Among them, polyethylene grafted silane is High-density polyethylene grafted silane (MI: 2.0g / 10min, Tm: 134°C, grafting rate GR: 0.8%);

[0049] Reactive polyurethane is Reactive polyurethane PUR 9350;

[0050] compatibilizer is Ethylene-butyl acrylate copolymer grafted maleic acid EBA-g-MAH 3427 (MI: 2.1g / 10min, Tm: 91°C, grafting rate GR: 0.7%);

[0051] Polyethylene matrix resin is 50% High-density polyethylene DGDA-2399, 50% High-density polyethylene TR480;

[0052] Elastomeric tackifying resins are Polyolefin elastomer POE 8200;

[0053] Processing anti-aging additives are Antioxidant B215.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention discloses an adhesive resin for continuous fiber-reinforced plastic composite pipes, which is prepared from the following components in percentage by weight: polyolefin grafted silane 7-40%, reactive polyurethane 1-10%, 0.1-10% compatibilizer, 30-80% polyolefin matrix resin, 5-35% elastomer tackifying resin, 0.1-2% processing anti-aging additive. The invention also provides a preparation method of the adhesive resin for the continuous fiber reinforced plastic composite pipe. The bonding resin of the present invention has a good bonding effect on continuous fiber materials such as continuous glass fiber, polyester fiber, nylon fiber, aramid fiber, carbon fiber, etc., and the continuous fiber reinforced thermoplastic pipe prepared by it has a multi-layer structure, many The bonding between the layers is firm, the pressure bearing capacity is high, and the weight is light. It is an excellent choice in the field of high-pressure pipes.

Description

technical field [0001] The invention relates to the field of material compositions, in particular to an adhesive resin for continuous fiber reinforced plastic composite pipes and a preparation method thereof. Background technique [0002] Continuous fiber is a kind of continuous high-strength fiber, commonly used are glass fiber, polyester fiber, nylon fiber, aramid fiber, carbon fiber, etc., which have excellent properties such as high strength, high toughness, insulation and heat resistance, and are used in aerospace, automotive, etc. , clothing, military industry, building materials and many other aspects. Polyolefin adhesive resin has good wettability and high bonding strength for various materials including some non-polar materials. At the same time, as an environmentally friendly material, it also has excellent processing. In terms of operation, it can be applied to high-speed continuous The production line improves production efficiency and is widely used in composit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J123/06C09J175/04C09J123/26C09J11/08
Inventor 汪加胜杜壮唐舫成孔超
Owner GUANGZHOU LUSHAN NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com