Luminous type high-brightness porcelain glue and preparation method thereof

A high-brightness, true porcelain technology, applied in the direction of adhesives, epoxy resin glue, adhesive types, etc., can solve the problems of short setting time, difficulty in removing residual materials, yellowish and greenish surface, etc.

Inactive Publication Date: 2019-05-17
广东鑫凯科技实业有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the hardness of the existing real porcelain glue products has not reached the hardness of the advertised ceramics, and cracks are prone to occur after long-term use
Moreover, due to the use in harsh environments all the year round, its surface often turns yellow and green, which makes its aesthetic effect poor
In addition, when applying the glue, due to the need to remove the remaining material, the existing real porcelain glue has a high initial viscosity and a short solidification time, so it is difficult to remove the remaining material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1 provides a luminous high-brightness true porcelain glue, which includes material A and material B mixed uniformly with each other, and the dosage ratio of material A and material B is 1:1. Material A is composed of the following components in parts by weight: 13 parts of epoxy resin, 45 parts of curing agent, 27 parts of diluent, 5 parts of thixotropic agent, and 10 parts of luminous powder. Material B is composed of the following components in parts by weight: 84 parts of epoxy resin, 10 parts of diluent, and 6 parts of thixotropic agent.

[0028] In terms of specific components, the epoxy resin in the A material and the B material is one of E-44 and E-51. The 45 parts by weight of the curing agent in the material A is composed of the following parts by weight: 20 parts by weight of isophorone diamine and 25 parts by weight of 1.3-cyclohexanedimethylamine. The diluents in the A material and the B material are both benzyl alcohol. The thixotropic agents i...

Embodiment 2

[0031] Embodiment 2 provides the preparation method of the real porcelain glue of above-mentioned embodiment 1, described method comprises the following steps:

[0032] Step 1: In the mixing equipment, add the following components: 13 parts of epoxy resin, 45 parts of curing agent, 27 parts of diluent, 5 parts of thixotropic agent, 10 parts of luminous powder, and stir evenly at a stirring temperature of 150°C , get A material;

[0033] Step 2: In the mixing equipment, add the following material components: 84 parts of epoxy resin, 10 parts of diluent, 6 parts of thixotropic agent, and stir evenly at a stirring temperature of 150 ° C to obtain material B;

[0034] Step 3: Put the uniformly stirred material A and material B into the glue filling machine respectively. In each glue cartridge of the glue filling machine, the dosage ratio of material A and material B is 1:1, and pack after the glue filling is completed. store.

[0035] In terms of specific components, the epoxy r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses luminous type high-brightness porcelain glue and a preparation method thereof. The porcelain glue comprises a material A and a material B which are uniformly mixed with each other, wherein the dosage ratio of the material A to the material B is 1 to1; the material A is prepared from the following components in parts by weight: 13 parts of epoxy resin, 45 parts of a curing agent, 27 parts of diluent, 5 parts of a thixotropic agent and 10 parts of noctilucent powder; and the material B is prepared from the following components in parts by weight: 84 parts of epoxy resin,10 parts of diluent and 6 parts of a thixotropic agent. The luminous type high-brightness porcelain glue has the characteristics of high hardness, high brightness, luminous effect, easy shovel of residual materials and the like, and is suitable for bonding ceramic or stone building materials and gap filling and beautifying.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a luminous-type high-brightness true porcelain glue and a preparation method thereof. Background technique [0002] True porcelain glue is a beautiful seam product used for bonding and gap filling and beautifying all kinds of ceramic or stone building materials such as tile floors, tile walls, wash basins, bathtubs, toilets, kitchen counters, door stones, etc. [0003] However, the hardness of the existing real porcelain glue products cannot reach the hardness level of the advertised ceramics, and cracks and the like are prone to occur after long-term use. And, because it is used under harsh environment all the year round, its surface often turns yellow and turns green, so that its aesthetic effect is relatively poor. In addition, during glue application, due to the need to remove the remaining material, the existing real porcelain glue has a high initial viscosity and a short ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J11/04C08G59/50
Inventor 周国平周国安涂冬琴杨玉芳
Owner 广东鑫凯科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com