Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Water-based chameleon solvent-resistant elastic coating

An elastic coating, chameleon technology, applied in coatings, polyurea/polyurethane coatings, etc., to achieve the effect of good fullness, good wetting, and increased scratch resistance

Active Publication Date: 2019-06-04
湖北双键精细化工有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are no water-based chameleon pigments in the market at present, mainly because of the constraints of related technical problems. One is to solve the problem of wetting and encapsulation of pigments by water-based resins, and the other is that due to the limitation of applicable fields, it has a certain impact on its wear-resistant and scratch-resistant performance. High requirements, and this is the shortcoming of traditional water-based coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The water-based chameleon solvent-resistant elastic coating provided in this example is prepared by the following method, (1), at a stirring speed of 600-1000rpm, add each component in order according to the following parts by mass, and prepare a water-based semi- Matte chameleon solvent-resistant coating: U355 water-based resin 30 parts, U3700 water-based resin 15 parts, deionized water 10 parts, BYK-180 dispersant 0.3 parts, BYK-346 wetting agent 0.5 parts, BYK-3720 leveling agent 0.8 parts , 2 parts of Tosoh E220A matting powder, 1 part of Fuji 256NF matting powder, 3 parts of BCS film-forming aid, 0.2 part of Dego 902W defoamer, 1 part of Zuo Ronggong R-089 hand feeling additive, BYK 535 water-based wax 2 parts, 0.2 parts of Dow AMP-95pH regulator, 4 parts of Dongguan Longmei 2232 chameleon pigment, 4 parts of Dongguan Longmei 3202 chameleon pigment, 1 part of double bond DB7650 modified polyurethane (the DB7650 special modified polyurethane is made of poly Aqueous ...

Embodiment 2

[0024] The water-based chameleon solvent-resistant elastic coating provided in this example is prepared by the following method, (1), at a stirring speed of 600-1000rpm, add each component in order according to the following parts by mass, and prepare a water-based semi- Matt chameleon solvent-resistant paint: 25 parts of U355 water-based resin, 25 parts of U3700 water-based resin, 13 parts of deionized water, 0.4 part of BYK-180 dispersant, 0.4 part of BYK-346 wetting agent, 1.0 part of BYK-3720 leveling agent , 2.5 parts of Tosoh E220A matting powder, 1.5 parts of Fuji 256NF matting powder, 3.5 parts of BCS film-forming aid, 0.1 part of Dego 902W defoamer, 1.5 parts of Zuo Ronggong R-089 hand feeling additive, BYK 535 water-based wax 1.5 parts, Dow AMP-95pH regulator 0.1 part, Dongguan Longmei 2232 chameleon pigment 3 parts, Dongguan Longmei 3202 chameleon pigment 3 parts, double bond DB7650 modified polyurethane 2 parts.

[0025] (2) Mix and dilute 6 parts of double bond 83...

Embodiment 3

[0028]The water-based chameleon solvent-resistant elastic coating provided in this example is prepared by the following method, (1), at a stirring speed of 600-1000rpm, add each component in order according to the following parts by mass, and prepare a water-based semi- Matte chameleon solvent-resistant paint: 35 parts of U355 water-based resin, 25 parts of U3700 water-based resin, 15 parts of deionized water, 0.5 parts of BYK-180 dispersant, 0.3 parts of BYK-346 wetting agent, 1.2 parts of BYK-3720 leveling agent , 3 parts of Tosoh E220A matting powder, 2 parts of Fuji 256NF matting powder, 4 parts of BCS film-forming aid, 0.2 part of Tego 902W defoamer, 1 part of Zuo Ronggong R-089 hand feeling additive, BYK 535 water-based wax 2 parts, 0.3 parts of Dow AMP-95pH regulator, 5 parts of Dongguan Longmei 2232 chameleon pigment, 5 parts of Dongguan Longmei 3202 chameleon pigment, 3 parts of double bond DB7650 modified polyurethane.

[0029] (2) Mix and dilute 5 parts of double bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-based chameleon solvent-resistant elastic coating, which comprises the following ingredients (by weight): 10-15 parts of deionized water, 40-60 parts of waterborne resin, 6-10 parts of chameleon pigment, 8-10 parts of a water-based curing agent, 2.5-5 parts of water-based matting powder, 0.3-0.5 part of a dispersant, 0.3-0.5 part of a wetting agent, 0.8-1.2 parts ofa leveling agent, 3-4 parts of a coalescing agent, 1-2 parts of a hand feeling agent, 1-2 parts of water-based wax, 0.1-0.3 part of an antifoaming agent, 0.1-0.3 part of a pH regulator, 0.2-0.4 part of a thickening agent, 2-3 parts of propylene glycol methyl ether acetate, and 1-3 parts of DB7650 special modified polyurethane. The coating is safe and environmentally-friendly, and has good solventresistance, film fullness, scratch resistance and wear resistance. In addition, hand feeling and application property are also greatly enhanced.

Description

technical field [0001] The invention provides a water-based solvent-resistant coating with a chameleon effect, which belongs to an environment-friendly water-based coating in the field of high-end decoration. Background technique [0002] There are mainly two types of coatings on the market, water-based coatings and solvent-based coatings (oil-based coatings). Solvent-based coatings do not have high requirements for painting conditions, and can be applied in a wide range of temperature and humidity. Solvent-based coatings have a thicker consistency and are not easy to flow; solvent-based coatings have good leveling properties, smooth paint films, and less brush or reel lines. The surface permeability of solvent-based paint is strong, especially for open-air wood, which can increase its adhesion and surface protection; the adhesion of oil-based paint is better on a smooth surface; solvent-based paint has a brighter and more eye-catching luster. However, with the implementat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D201/00C09D7/40
Inventor 马世凯雷木生田军胡勇军柴广高州游仁国
Owner 湖北双键精细化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com