Stainless steel vacuum container surface treatment method with three-dimensional fabric sense

A vacuum container and surface treatment technology, which is applied to special surfaces, pretreatment surfaces, and devices for coating liquids on surfaces. , Good dust removal effect, fast volatile effect

Active Publication Date: 2019-06-07
浙江飞剑科技有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention provides a new surface treatment method for stainless steel vacuum containers aiming at the defects in the prior art that the surface of the stainless steel vacuum containers has a single color and cannot meet people’s living needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel vacuum container surface treatment method with three-dimensional fabric sense
  • Stainless steel vacuum container surface treatment method with three-dimensional fabric sense

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A method for treating the surface of a stainless steel vacuum container with a sense of three-dimensional cloth, comprising the following steps:

[0051] a. take a stainless steel vacuum container, and carry out surface treatment to the stainless steel vacuum container;

[0052] b. Weigh the following components by weight:

[0053] 100 parts of polyester resin,

[0054] 10 parts of color pigment,

[0055] Filling 8 parts,

[0056] 2 parts crack crack additive,

[0057] Thoroughly stir and mix the above proportioned components with a disperser, then extrude into cakes and grind them into powder coatings;

[0058] c. Spray the powder coating on the surface of the stainless steel vacuum container with electrostatic powder spraying equipment. The powder spraying electrostatic voltage is 50kv, the compressed air pressure is 1.0kg, the electrostatic current is 10μa, the atomization pressure is 0.30mpa, and the powder spraying is over. Finally, a powder coating with a fil...

Embodiment 2

[0074] A method for treating the surface of a stainless steel vacuum container with a sense of three-dimensional cloth, comprising the following steps:

[0075] a. take a stainless steel vacuum container, and carry out surface treatment to the stainless steel vacuum container;

[0076] b. Weigh the following components by weight:

[0077] 100 parts of polyester resin,

[0078] 100 parts of colored pigments,

[0079] Filling 100 parts,

[0080] Crack crack additive 100 parts,

[0081] Thoroughly stir and mix the above proportioned components with a disperser, then extrude into cakes and grind them into powder coatings;

[0082] c. Spray the powder coating on the surface of the stainless steel vacuum container with electrostatic powder spraying equipment. The powder spraying electrostatic voltage is 60kv, the compressed air pressure is 2.0kg, the electrostatic current is 15μa, the atomization pressure is 0.45mpa, and the powder spraying is over. Finally, a powder coating wi...

Embodiment 3

[0098] A method for treating the surface of a stainless steel vacuum container with a sense of three-dimensional cloth, comprising the following steps:

[0099] a. take a stainless steel vacuum container, and carry out surface treatment to the stainless steel vacuum container;

[0100] b. Weigh the following components by weight:

[0101] 100 parts of polyester resin,

[0102] 55 parts of colored pigments,

[0103] Filling 54 parts,

[0104] 51 parts of tortoise crack assistant,

[0105] Thoroughly stir and mix the above proportioned components with a disperser, then extrude into cakes and grind them into powder coatings;

[0106] c. Spray the powder coating on the surface of the stainless steel vacuum container with electrostatic powder spraying equipment. The powder spraying electrostatic voltage is 55kv, the compressed air pressure is 1.5kg, the electrostatic current is 13μa, the atomization pressure is 0.35mpa, and the powder spraying is over. Finally, a powder coatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a stainless steel vacuum container surface treatment method with a three-dimensional fabric sense. The stainless steel vacuum container surface treatment method comprises the following steps of a, taking the stainless steel vacuum container and carrying out surface treatment; b, weighing polyester resin, colored pigment, filler and turtle crack promoter, and then extrudingand grinding the mixture into powder coating; c, carrying out powder spraying operation on the powder coating, forming a cracking texture layer after curing; d, carrying out air spraying operation oncolored acrylic resin coating, and forming a color texture layer after curing; e, carrying out air spraying operation on transparent bright acrylic resin coating, and forming a bright color layer after curing; and f, carrying out air spraying operation on transparent matte acrylic resin coating, and forming a matte color layer after curing to finish the surface treatment of the stainless steel vacuum container. Through the above steps, the three-dimensional distribution grid effect with different shapes, sizes and thicknesses can be finally formed on the surface of the stainless steel vacuum container, the color is soft, the surface effect is vivid, and the living requirements of people can be better met.

Description

technical field [0001] The invention relates to a stainless steel vacuum container, in particular to a method for treating the surface of the stainless steel vacuum container with a sense of three-dimensional cloth. Background technique [0002] Stainless steel vacuum containers are one of the most commonly used containers, such as stainless steel vacuum insulation cups, stainless steel vacuum insulation pots, etc. The surface of the stainless steel vacuum container generally presents the inherent color of stainless steel, which is similar to silver, but this color is relatively single, so some manufacturers will spray or paint on the surface of the stainless steel vacuum container to change the color of the surface of the stainless steel vacuum container. Make it present a variety of different colors, thereby enriching the appearance of stainless steel vacuum containers. [0003] However, for the current process of spraying plastic on the surface of stainless steel vacuum ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D1/06B05D3/00B05D3/02B05D5/06B05D7/14B05D7/24C09D167/00C09D5/03C09D7/61
Inventor 程海崴夏飞剑
Owner 浙江飞剑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com