A carbon dioxide, heterojunction technology, applied in chemical instruments and methods, electrodes, chemical/physical processes, etc., can solve the problems of catalysis efficiency limitation, ineffective use of sunlight, etc., to reduce the recombination rate and promote high efficiency and rapidity. Effect of geomigration, excellent photoelectrochemical (PEC) performance

Active Publication Date: 2019-07-12
ANHUI UNIVERSITY
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to WO 3 It cannot effectively utilize sunlight, and it is easy to quickly...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heterojunction photo-anode for driving reduction of carbon dioxide and preparation method and application of heterojunction photo-anode
  • Heterojunction photo-anode for driving reduction of carbon dioxide and preparation method and application of heterojunction photo-anode
  • Heterojunction photo-anode for driving reduction of carbon dioxide and preparation method and application of heterojunction photo-anode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1, WO 3 / Bi 2 S 3 Fabrication of Heterojunction Photoanodes

[0026] This example prepares relevant photoanode nanomaterials according to the following steps:

[0027] 1) The hydrothermal method of the prior art is used to prepare WO 3 Nanosheet array (Du Ronggui et al., preparation method of tungsten trioxide nanosheet composite photoanode, Chinese patent application number: 201810115207.1), the specific steps are as follows:

[0028] Weigh 0.231g of sodium tungstate dihydrate and stir in 30mL of deionized water until dissolved, add dropwise 10mL of hydrochloric acid (3M) and stir for about 10min, then add 0.2g of ammonium oxalate and 35mL of deionized water and continue stirring for 30min, then place the solution in water In the thermal reaction kettle, after sealing, the hydrothermal reaction was carried out at a temperature of 120 ° C for 6 hours, that is, the vertical growth of WO was prepared on the conductive glass (FTO). 3 ·H 2 O nanosheet array...

Embodiment 2

[0035] Example 2, WO 3 / Bi 2 S 3 Photoelectrochemical performance of heterojunction photoanodes

[0036] With the WO prepared in Example 1 3 Nanosheet photoanodes and WO 3 / Bi 2 S 3 A series of photoelectrochemical performance tests such as photocurrent and impedance were performed on the heterojunction photoanode. The photoelectrochemical performance test is carried out in the electrochemical workstation of the three-electrode system. The prepared photoanode material is the working electrode, the platinum sheet is the counter electrode, the saturated calomel electrode is the reference electrode, and the electrolyte is 0.5M anhydrous sodium sulfate. solution. A xenon lamp was used as the light source during the photoelectric test, and the optical power density of the light source was calibrated to 100mW cm -2 . Test the current density-time curve (I-T) of the sample electrode at a bias voltage of 1.0V; at a bias voltage of 0.8V, the frequency range is 10 -1 to 10 4 ...

Embodiment 3

[0039] Example 3, WO 3 / Bi 2 S 3 Photoelectrocatalytic CO with heterojunction photoanodes 2 Reduction experiment

[0040] With the WO prepared in Example 1 3 Nanosheet photoanodes and WO 3 / Bi 2 S 3 Heterojunction photoanode for photoelectrocatalytic reduction of CO in a photoanode-driven photoelectrochemical system 2 experiment.

[0041] Photoanode-driven photoelectrocatalytic CO 2 The reduction test was carried out in an electrochemical workstation with a three-electrode system. The prepared photoanode material was used as the working electrode, the 1cm×2cm foamed copper was used as the counter electrode, and the saturated calomel electrode was used as the reference electrode. Photocatalytic CO in an H-type electrolytic cell equipped with a quartz window 2 Reduction experiments, the electrolytic cell consists of two separate compartments, the cathode and the anode, and the anode compartment is filled with 0.2M Na 2 SO 4 solution, while 0.5M KHCO in the cathode co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Photocurrent densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a heterojunction photo-anode for driving reduction of carbon dioxide and a preparation method and application of the heterojunction photo-anode. The preparation method comprises the steps that firstly, a WO3 nano-sheet array is synthesized through a hydrothermal method, then by adopting a secondary hydrothermal method, a Bi2S3 nano-material grows on the surface of a WO3 nano-sheet, and therefore the WO3/Bi2S3 heterojunction photo-anode used for driving the reduction of CO2 is obtained. Compared with an original WO3 photo-anode, the constructed WO3/Bi2S3 heterojunction photo-anode expresses a more excellent photoelectrochemical property and more excellent photoelectrocatalysis capacity.

Description

technical field [0001] The invention belongs to the technical field of photoelectric catalysis, and in particular relates to a WO 3 / Bi 2 S 3 Heterojunction photoanode and its preparation method. Background technique [0002] Photoelectrocatalytic technology can effectively utilize solar energy. It realizes energy conversion by converting light energy into electrical energy or chemical energy, thereby alleviating the energy crisis and realizing the degradation of pollutants. Among them, photocatalytic reduction of CO 2 Technology can convert carbon dioxide in the air and make good use of it. It can convert carbon dioxide into energy-dense and higher value liquid fuels or other chemicals, such as formic acid, methane and carbon monoxide. [0003] Tungsten trioxide (WO 3 ) has a relatively appropriate optical band gap (~2.6eV), good chemical stability and photocorrosion resistance in acidic solutions, and it also has great potential in the oxidation of water and the degra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25B3/04C25B1/00C25B11/06B01J27/047C25B3/25
CPCB01J35/0033B01J35/004B01J27/047C25B1/55C25B3/25C25B11/091Y02P20/133
Inventor 李国华李婉青陈志成项曙光胡鑫
Owner ANHUI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap