Lyocell/secondary cellulose acetate fiber blended fabric and weaving method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of diacetate fiber and blended fabrics, applied in the field of textile fabrics, can solve the problems of fabric loss of luster, poor alkali resistance, low strength of diacetate fibers, etc., and achieve low price, high loom weaving efficiency and wide application Effect
Inactive Publication Date: 2019-07-19
YUYUE HOME TEXTILE +1
View PDF6 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, on the one hand, the strength of diacetate fiber is quite low, and the dry strength is only 1.1~1.2cN / dtex; on the other hand, diacetate fiber has poor alkali resistance, and it is easy to make the fabric lose luster after being compounded and interwoven with other fibers.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] In the weaving method of the Tencel / diecetate fiber blended fabric provided in this embodiment, the warp and weft yarns of the fabric are Tencel Saisen A100 produced by Austrian company and diacetate fiber blended yarn produced by Eastman Company of the United States.
[0033] Specifications of gray fabric: Saisen A100 ten70 / two vinegar 30 60*60s 182*116 106〞4 / 1.
[0038] In order to ensure that the two kinds of fiber raw materials with different characteristics can be fully mixed, to avoid color flowers due to different fiber dyeing properties, to alleviate the accumulation of diacetate fibers, and to prevent excessive short fibers in the post-production process, the two fibers are mixed together. Proportional portioning, weighing, layering, manual direct feeding and...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a lyocell / secondary cellulose acetate fiber blended fabric and a weaving method thereof. The weaving method includes the following processing steps of spinning, warping, sizing, weaving and after-finish scouring and dyeing; the spinning step includes raw material premixing, a blowing-carding procedure, a drawing procedure, a roving procedure, a spinning procedure and a spooling procedure; the after-finish scouring and dyeing step includes scouring, dyeing, washing and after-finish. According to the lyocell / secondary cellulose acetate fiber blended fabric, lyocell fibersand secondary cellulose acetate fibers serve as warp and weft respectively, and the two fibers are mutually reinforced; the produced lyocell / secondary cellulose acetate fiber blended fabric has the advantages of the lyocell fibers and the secondary cellulose acetate fibers, has the advantages of being low in price and wide in application range and can be applied to the markets of garments, home textiles, auxiliary materials and the like.
Description
technical field [0001] The invention relates to the technical field of textile fabrics, in particular to a Tencel / diecetate fiber blended fabric and a weaving method thereof. Background technique [0002] Diacetate fiber is a semi-synthetic fiber prepared from natural high-quality wood pulp as the main raw material, which has the excellent characteristics of both natural fiber and synthetic fiber. The raw material of the fiber is renewable, and has excellent characteristics such as low toxicity, low flammability, good optics and smoothness; at the same time, the fiber is close to real silk, with elegant luster, bright dyeing, strong dyeing fastness, soft and smooth hand feeling, Light texture, low moisture regain, good elasticity, not easy to wrinkle, good drapability, thermoplasticity, dimensional stability, its fabric has moderate hygroscopicity, quick drying, stable anti-pilling, anti-static, stain Easy to shed and easy to wash. However, on the one hand, the strength of...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more