Tea set as well as preparation method and application thereof

A tea set, press molding technology, applied in the application, home utensils, clay products and other directions, can solve the problems of inability to obtain effective and stable quality control, the improvement of taste is not obvious, affecting people's taste, etc., to achieve simple and easy preparation, and fragrant smell , the effect of increasing the number of brewing times

Inactive Publication Date: 2019-08-02
朱春棋
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional teapots and tea sets are produced by ceramic manufacturers according to their own raw material characteristics. The finished products are used to brew tea soup. The smell, taste, and quality of tea soup can only be left to chance, which is highly random, and effective and stable quality control cannot be obtained. affect people's taste
In order to solve this problem, the traditional method is to improve the processing method or brewing method of tea, but the improvement of its taste is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Get the following raw materials in parts by weight: 62 parts of the first mud material, 35 parts of the second mud material; wherein,

[0018] Take the Al in the first mud 2 o 3 , SiO 2 , CaO, Fe 2 o 3 and FeO, and K 2 O and Na 2 The mass ratio of O is 16:72:2.9:0.3:2.8;

[0019] Take the Al in the second mud 2 o 3 , SiO 2 , CaO, Fe 2 o 3 and FeO, and K 2 O and Na 2 The mass ratio of O is 14:67:4.8:11.8:2.2;

[0020] After adding water to the first mud material and the second mud material, carry out sieving treatment respectively, the particle fineness of the first mud material is 120 mesh, and the sieve residue is 0.2%-0.5%; the fineness of the second mud material particle is 60 mesh, 0.3%-0.8% remaining after sieving, then mix and grind the first mud and the second mud to obtain mud, and then spin the mud to dehydrate to a water content of 22%-24%;

[0021] Next, control the water content of the mud at 28% to 32%, then inject the above mud into the mold...

Embodiment 2

[0024] Get the following raw materials by mass percentage: 70 parts of the first mud material, 24 parts of the second mud material; wherein, take the Al in the first mud material 2 o 3 , SiO 2 , CaO, Fe 2 o 3 and FeO, and K 2 O and Na 2 The mass ratio of O is 22:62:2:0.5:3;

[0025] Take the Al in the second mud 2 o 3 , SiO 2 , CaO, Fe 2 o 3 and FeO, and K 2 O and Na 2 The mass ratio of O is 10:65:2.2:14:3.1;

[0026] After adding water to the first mud material and the second mud material, carry out sieving treatment respectively, the particle fineness of the first mud material is 120 mesh, and the sieve residue is 0.2%-0.5%; the fineness of the second mud material particle is 60 mesh, 0.3%-0.8% remaining after sieving, then mix and grind the first mud and the second mud to obtain mud, and then spin the mud to dehydrate to a water content of 22%-24%;

[0027] Next, control the water content of the mud at 28% to 32%, then inject the above mud into the mold, and u...

Embodiment 3

[0030] Get the following raw materials by mass percentage: 65 parts of the first mud material, 29 parts of the second mud material; wherein, take the Al in the first mud material 2 o 3 , SiO 2 , CaO, Fe 2 o 3 and FeO, and K 2 O and Na 2 The mass ratio of O is 18.2:74:1.8:0.6:3.5;

[0031] Take the Al in the second mud 2 o 3 , SiO 2 , CaO, Fe 2 o 3 and FeO, and K 2 O and Na 2 The mass ratio of O is 13:55:3:7:3.5;

[0032] After adding water to the first mud material and the second mud material, carry out sieving treatment respectively, the particle fineness of the first mud material is 120 mesh, and the sieve residue is 0.2%-0.5%; the fineness of the second mud material particle is 60 mesh, 0.3%-0.8% remaining after sieving, then mix and grind the first mud and the second mud to obtain mud, and then spin the mud to dehydrate to a water content of 22%-24%;

[0033] Next, control the water content of the mud at 28% to 32%, then inject the above mud into the mold, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tea set as well as a preparation method and an application thereof. The tea set is prepared from raw materials in parts by weight as follows: 62-70 parts of first pug and 24-35 parts of second pug, wherein the mass ratios of Al2O3, SiO2, CaO, Fe2O3 and FeO as well as K2O and Na2O in the first pug and the second pug are (16-22):(62-74):(1.8-3.2):(0.3-0.6):(2.8-3.8) and (10-14):(55-75):(2.2-4.8):(5-14):(2.2-3.5) respectively. Tea soup made by the tea set has pure taste, fragrant aroma and can refresh throats after drinking, is sweet after taste and has a significant taste improving effect.

Description

technical field [0001] The invention relates to a tea set and its preparation method and application. Background technique [0002] Traditional teapots and tea sets are produced by ceramic manufacturers according to their own raw material characteristics. The finished products are used to brew tea soup. The smell, taste, and quality of tea soup can only be left to chance, which is highly random and cannot be effectively controlled. affect people's taste for it. In order to solve this problem, the traditional methods all improve the processing method or brewing method of tea, but the improvement of its taste is not obvious. Contents of the invention [0003] In order to solve the above technical problems, the object of the present invention is to provide a tea set and its preparation method and application. [0004] The present invention is achieved through the following technical solutions: a tea set, made of the following raw materials: in parts by weight, 62-70 parts o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B33/24C04B33/32A47G19/22
CPCA47G19/22C04B33/04C04B33/24C04B33/32C04B2235/3201C04B2235/3208C04B2235/3217C04B2235/3272C04B2235/3418
Inventor 朱春棋
Owner 朱春棋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap