Film coating material for skin affinity electrode plate

An electrode sheet and coating technology, which is applied in the field of skin-friendly electrode sheet coating materials, can solve the problems of affecting the use effect, redness and swelling of the fit, and skin irritation, so as to improve the moisturizing effect and touch feeling, avoid redness and swelling, and avoid irritation. Effect

Inactive Publication Date: 2019-08-16
淄博鲁泰正隆医疗器械有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, existing coating materials still have some disadvantages in actual use, such as poor affinity with the skin. In actual use, after a long time of bonding with the skin, it is easy to cause irritation to the skin at the bonding place. This will lead to redness and swelling at the joint, and itching, especially when the user has allergic skin, the above situation is more obvious, which seriously affects the use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Film coating material for skin affinity electrode plate
  • Film coating material for skin affinity electrode plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The present invention provides figure 1 The shown skin-affinity electrode sheet coating material includes a main material and an auxiliary material, in parts by mass, the main material includes 20 parts of polyvinyl alcohol, 0.7 parts of plant essential oil and 2 parts of plant nano powder. Including 3 parts of glycerol, 0.2 part of antibacterial agent, 1 part of crosslinking agent and 60 parts of solvent, 20 parts of said polyvinyl alcohol is set as medical polyvinyl alcohol, the degree of polymerization of said medical polyvinyl alcohol is set to 1200, and alcoholysis The degree is set to 95%, 0.7 part of the plant essential oil is set as geranium essential oil, 2 parts of the plant nano powder is set as aloe nano powder, and 0.2 part of the antibacterial agent is set as octanediamine, butanediamine, and xylylenediamine Or hexamethylene diamine, one part of the crosslinking agent is set to epichlorohydrin, ethylene glycol diglycidyl ether, glutaraldehyde, allyl glycidy...

Embodiment 2

[0037] The present invention provides figure 1 A skin-affinity electrode sheet coating material shown includes a main material and an auxiliary material, in parts by mass, the main material includes 29 parts of polyvinyl alcohol, 1 part of plant essential oil, and 2.5 parts of plant nano powder. Including 5 parts of glycerol, 0.4 parts of antibacterial agent, 2 parts of crosslinking agent and 75 parts of solvent, 29 parts of the polyvinyl alcohol is set as medical polyvinyl alcohol, the degree of polymerization of the medical polyvinyl alcohol is set to 5600, and alcoholysis The degree is set to 97%, 1 part of the plant essential oil is set as geranium essential oil, 2.5 parts of the plant nano powder is set as aloe nano powder, and 0.4 part of the antibacterial agent is set as octanediamine, butanediamine, and xylylenediamine Or hexamethylene diamine, 2 parts of the crosslinking agent is set as epichlorohydrin, ethylene glycol diglycidyl ether, glutaraldehyde, allyl glycidyl e...

Embodiment 3

[0047] The present invention provides figure 1 A skin-affinity electrode sheet coating material is shown, comprising a main material and an auxiliary material, in parts by mass, the main material includes 36 parts of polyvinyl alcohol, 1.3 parts of plant essential oils and 3 parts of plant nano powder. Including 7 parts of glycerol, 0.6 parts of antibacterial agent, 3 parts of crosslinking agent and 90 parts of solvent, 36 parts of the polyvinyl alcohol is set as medical polyvinyl alcohol, the degree of polymerization of the medical polyvinyl alcohol is set to 10000, and alcoholysis The degree is set to 100%, 1.3 parts of the plant essential oil is set as geranium essential oil, 3 parts of the plant nano powder is set as aloe nano powder, and 0.6 part of the antibacterial agent is set as octanediamine, butanediamine, and xylylenediamine Or hexamethylene diamine, 3 parts of the crosslinking agent is set to epichlorohydrin, ethylene glycol diglycidyl ether, glutaraldehyde, allyl ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a film coating material for a skin affinity electrode plate, and in particular relates to the field of electrode plates. The film coating material is prepared from a main material and an auxiliary material, wherein the main material is prepared from 20-36 parts of polyvinyl alcohol, 0.7-1.3 parts of plant essential oil and 2-3 parts of plant nanometer fine powder; the auxiliary material is prepared from 3-7 parts of glycerol, 0.2-0.6 part of an antibacterial agent, 1-3 parts of a cross-linking agent and 60-90 parts of a solvent. The film coating material for the skin affinity electrode plate can effectively avoid irritation to the skin, thereby effectively avoiding the redness and swelling of the bonded part and the generation of itching sensation, and being good inactual use effect; furthermore, the geranium essential oil also has functions of sterilization and disinfection, and the aloe nanometer fine powder has a function of moisturizing the skin, so that the film coating material not only does not cause irritation to the skin, but also provides better care for the skin.

Description

Technical field [0001] The present invention relates to the technical field of electrode sheets, and more specifically, the present invention relates to a skin-friendly electrode sheet coating material. Background technique [0002] There are many kinds of electrode pads, including massage electrode pads, physiotherapy electrode pads, conductive electrode pads, self-adhesive electrode pads, viscose electrode pads, non-woven electrode pads, ECG electrode pads, medical electrode pads, silicone electrode pads, heating electrodes The heating electrode sheet includes conductive sheet, insulating sheet, heating device, and wire connected to the outside, and a temperature sensor is installed between the insulating sheet and the conductive sheet, and the two ends of the temperature sensor are connected to the terminal through the wire Connected, the heating electrode sheet has a temperature control function, and the inner side has a heat dissipation mesh, which can fully dissipate local ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L31/10A61L31/08A61L31/14A61L31/16
CPCA61L31/08A61L31/10A61L31/14A61L31/16A61L2300/30A61L2300/404C08L29/04
Inventor 李健
Owner 淄博鲁泰正隆医疗器械有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com