Liquid metal material for noise reduction in nuclear reactor environment and processing technology thereof

A liquid metal and nuclear reactor technology, applied in the field of alloys, can solve the problems of increasing the leakage of nuclear products, achieve the effects of attenuating rays, realizing degrees of freedom, and excellent shielding materials

Inactive Publication Date: 2019-08-30
深圳市兴荣晟物业管理有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, vibration will also increase the possibility of nuclear prod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid metal material for noise reduction in nuclear reactor environment and processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A liquid metal material for reducing noise in a nuclear reactor environment and a processing technology thereof. In terms of weight percentage, the alloy composition is: Se: 0.1wt.%, Sb: 8.0wt.%, In: 21.0wt.%, V: 0.5wt.%, Ag: 1.5wt.%, Pb: 12.0wt. %, Cd: 5.0wt.%, the balance is tin.

[0019]The above-mentioned liquid metal material for noise reduction in a nuclear reactor environment and its processing technology include the following processing and use steps: (a) After the alloy is configured according to the required composition, it is put into an induction furnace for smelting, and magnesium oxide is used to Or the alumina crucible is smelted under the protection of argon; after 10 minutes of heat preservation at 500 degrees, the alloy melt is fully stirred evenly by electromagnetic stirring, and the dross on the surface of the melted alloy melt is scraped off, poured into an iron mold and cast into a Rod shape (about 200 mm in length, 8 mm in width, and about 3 mm i...

Embodiment 2

[0022] A liquid metal material for reducing noise in a nuclear reactor environment and a processing technology thereof. In terms of weight percentage, the alloy composition is: Se: 0.2wt.%, Sb: 15.0wt.%, In: 25.0wt.%, V: 1.0wt.%, Ag: 2.0wt.%, Pb: 15.0wt. %, Cd: 10.0wt.%, the balance is tin.

[0023] The above-mentioned liquid metal material for noise reduction in a nuclear reactor environment and its processing technology include the following processing and use steps: (a) After the alloy is configured according to the required composition, it is put into an induction furnace for smelting, and magnesium oxide is used to Or melt the alumina crucible under the protection of argon; heat the alloy melt at 520 degrees for 10 minutes and use electromagnetic stirring to fully stir the alloy melt evenly, scrape off the dross on the surface of the melted alloy melt, pour it into an iron mold and cast it into a Rod shape (about 300 mm in length, 10 mm in width, and about 5 mm in thickn...

Embodiment 3

[0026] A liquid metal material for reducing noise in a nuclear reactor environment and a processing technology thereof. In terms of weight percentage, the alloy composition is: Se: 0.2wt.%, Sb: 12.0wt.%, In: 22.0wt.%, V: 0.8wt.%, Ag: 1.8wt.%, Pb: 13.0wt. %, Cd: 6.0wt.%, the balance is tin.

[0027] The above-mentioned liquid metal material for noise reduction in a nuclear reactor environment and its processing technology include the following processing and use steps: (a) After the alloy is configured according to the required composition, it is put into an induction furnace for smelting, and magnesium oxide is used to Or melt the alumina crucible under the protection of argon gas; heat the alloy melt at 530 degrees for 10 minutes and use electromagnetic stirring to fully stir the alloy melt evenly, scrape off the dross on the surface of the melted alloy melt, pour it into an iron mold and cast it into a Rod shape (about 250 mm in length, 9 mm in width, and about 4 mm in thic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Elastic modulusaaaaaaaaaa
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a liquid metal material for noise reduction in nuclear reactor environment and a processing technology thereof. The liquid metal material comprises, by weight, 0.1%-0.2% of Se,5.0%-15.0% of Sb, 20.0%-25.0% of In, 0.5%-1.0% of V, 1.5%-2.0% of Ag, 10.0%-15.0% of Pb, 5.0%-10.0% of Cd, and the balance Sn. The liquid metal type vibration reduction alloy material can be coated in a gap for vibration reduction through a simple heat source. The liquid metal material is characterized in that technology equipment is simple, the operation technology is easy to grasp, the construction cost is low, and the vibration reduction effect is remarkable.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a lead alloy. Background technique [0002] The use and research and development of nuclear energy is an important symbol to measure a country's national defense strength and national economic level. Nuclear power has become a clean, efficient and reliable energy source in the 21st century when energy is very scarce. Therefore, the research and industrialization of nuclear energy is an area of ​​widespread concern in various countries. During the normal production process of the reactor, a lot of mechanical facilities are needed to cooperate. Therefore, in the modern nuclear industry, the pollution and hazards caused by mechanical vibration are becoming more and more serious. [0003] The catastrophic consequences of vibration and noise on equipment and human health are manifold. For instruments and equipment, vibration can significantly reduce the accuracy of the instrument a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C13/00C22C30/04C22C1/02B23K35/26
CPCB23K35/262C22C1/02C22C13/00C22C30/04
Inventor 王金辉
Owner 深圳市兴荣晟物业管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap