Low-cost production method of low-carbon glassed steel

A production method and technology for enamel steel are applied in the low-cost production field of low-carbon enamel steel, which can solve the problem of high production cost, and achieve the effects of simplifying production process, reducing production cost, and easy to control production rhythm.

Active Publication Date: 2019-10-11
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a low-cost production method of low-carbon enamelled steel, which mainly solves the technical problem that low-carbon enameled steel must adopt RH furnace vacuum refining process and high production cost in the prior art; the method of the present invention solves the current It is difficult to produce qualified low-carbon enamelled steel with the LF furnace refining process, which reduces the cost of low-carbon enameled steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1, the steel output of the converter is 271.9t, the weight content of carbon in the steel is 355ppm, and the weight content of oxygen is 639ppm; %, blow argon at the bottom of the ladle, heat up to the target temperature; then feed aluminum wire, add 362kg of ferrotitanium, switch the gas blowing at the bottom of the ladle from argon to nitrogen, blow nitrogen and stir for 10 minutes to obtain the finished molten steel, and the carbon in the finished steel The weight content of nitrogen is 301ppm, and the weight content of nitrogen is 36.4ppm.

Embodiment 2

[0018] Example 2, the steel output of the converter is 272.6t, the weight content of carbon in the steel is 326ppm, and the weight content of oxygen is 780ppm; the weight content of nitrogen in the molten steel entering the LF furnace is 17.9ppm, and the weight percentage of Alt is 0.0079% , heated up to the target temperature; then feed the aluminum wire, add 361kg of ferrotitanium, blow nitrogen and stir for 8 minutes to obtain the finished molten steel, the weight content of carbon in the finished steel is 360ppm, and the weight content of nitrogen is 43.8ppm.

[0019] See Table 1 for the nitrogen content (by weight percentage) in molten steel in the examples of the present invention.

[0020] Table 1 Nitrogen content in molten steel of the embodiment of the present invention, unit: weight percent.

[0021] category Nitrogen in molten steel at the end of converter smelting Nitrogen in LF in molten steel Nitrogen in finished steel Example 1 0.0011 0.001...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-cost production method of low-carbon glassed steel, and mainly solves the technical problems that in the prior art, low-carbon glassed steel has to adopt an RH furnace vacuum refining process, and is high in production cost. The technical scheme adopted by the invention is that the low-cost production method comprises the following steps: smelting by a top-bottom combined blowing converter, wherein the low-carbon glassed steel comprises the following main metal raw materials in percentage by mass: 75%-100% of molten iron and the balance of steel scrap; controllingthe converter smelting final point, and detecting w[C] in molten iron and the temperature of the molten iron at the converter blowing final point; immediately tapping after completing the converter blowing; and transporting molten iron in a steel ladle in an LF furnace to perform molten iron temperature control and molten iron component control. The low-carbon glassed steel produced by the low-cost production method is low in cost, and compared with an existing RH furnace vacuum refining process, the low-carbon glassed steel, produced by the low-cost production method, each ton is lower than20 yuan.

Description

technical field [0001] The present invention relates to a production method of low-carbon enamel steel, in particular to a low-cost production method of low-carbon enamel steel; in particular, it relates to a production method for regulating carbon and nitrogen elements in low-carbon enamel steel by adopting LF furnace technology , belongs to the technical field of steel smelting and continuous casting. Background technique [0002] Low-carbon enamel steel is enamel enamel on the surface of the steel plate to prevent the steel plate from rusting, so that the steel plate will not form an oxide layer on the surface when it is heated and resist various liquids. It is widely used in eating utensils and washing utensils used in daily life. In order to prevent defects such as pinholes, bubbles, "lin burst" and product deformation of low-carbon enamelled steel at high temperatures, it is necessary to precisely control the carbon content of the finished product; at the same time, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C5/35C21C7/00C21C7/06C21C7/072C22C38/02C22C38/04C22C38/14
CPCC21C5/35C21C7/0006C21C7/06C21C7/072C22C38/001C22C38/02C22C38/04C22C38/14Y02P10/20
Inventor 刘相林夏富春孙玉军
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com