Liquid crystal alignment agent, liquid crystal alignment film, and liquid crystal display element

A technology of liquid crystal aligning agent and liquid crystal aligning film, applied in the directions of liquid crystal materials, instruments, chemical instruments and methods, etc., can solve the problems of lack of liquid crystal alignment, small anisotropy of polymer films, and generation of afterimages, etc. Good afterimage characteristics, no poor expression, suppressing bright spots

Active Publication Date: 2022-03-22
NISSAN CHEM CORP
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, compared with the liquid crystal aligning film obtained by rubbing treatment, the liquid crystal aligning film obtained by the photo-alignment method has a problem that the anisotropy with respect to the orientation direction of the polymer film is small.
If the anisotropy is small, sufficient liquid crystal orientation cannot be obtained, and when forming a liquid crystal display element, there are problems such as image sticking.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid crystal alignment agent, liquid crystal alignment film, and liquid crystal display element
  • Liquid crystal alignment agent, liquid crystal alignment film, and liquid crystal display element
  • Liquid crystal alignment agent, liquid crystal alignment film, and liquid crystal display element

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0144] The following examples are given to describe the present invention in more detail, but the present invention is not limited or interpreted by them.

[0145] The abbreviations and measurement methods of the compounds used in the following are as follows.

[0146] NMP: N-methyl-2-pyrrolidone

[0147] BCS: Butyl Cellosolve

[0148] DA-1: 1,2-bis(4-aminophenoxy)ethane

[0149] DA-2: 1,3-bis(4-aminophenoxy)propane

[0150] DA-3: p-phenylenediamine

[0151] DA-6: 4-(2-(Methylamino)ethyl)aniline

[0152]

[0153] [viscosity]

[0154] For the viscosity of polyamic acid ester and polyamic acid solution, using E-type viscometer TVE-22H (manufactured by Toki Sangyo Co., Ltd.), the sample volume is 1.1mL, and the cone rotor TE-1 (1 ° 34', R24) , Measured at a temperature of 25°C.

[0155] [molecular weight]

[0156] The molecular weight of the polyamic acid ester is measured using a GPC (normal temperature gel permeation chromatography) device, and the number average mol...

Synthetic example 1

[0182]Take DA-1 0.81g (3.30mmol), DA-20.57g (2.20mmol), DA-3 0.36g (3.30mmol), DA-4 0.88 g (2.20 mmol), NMP29.99g was added, and stirring and dissolution were carried out while feeding nitrogen gas. While stirring this diamine solution, 2.35 g (10.51 mmol) of 1,3-dimethyl-1,2,3,4-cyclobutanetetracarboxylic dianhydride was added so that the solid content concentration became 12 mass % to add NMP 6.40g and stir at room temperature for 24 hours to obtain a polyamic acid solution (A). The viscosity of this polyamic acid solution at a temperature of 25° C. was 316 mPa·s. In addition, the molecular weight of this polyamic acid was Mn=13230, Mw=29550.

Synthetic example 2

[0184] Take DA-1 0.54g (2.20mmol), DA-20.85g (3.30mmol), DA-3 0.36g (3.30mmol), DA-4 0.88 g (2.20 mmol), NMP30.17g was added, and stirring and dissolution were carried out while feeding nitrogen gas. While stirring this diamine solution, 2.35 g (10.51 mmol) of 1,3-dimethyl-1,2,3,4-cyclobutanetetracarboxylic dianhydride was added so that the solid content concentration became 12 mass % to add NMP 6.34g and stir at room temperature for 24 hours to obtain a polyamic acid solution (B). The viscosity of this polyamic acid solution at a temperature of 25° C. was 356 mPa·s. In addition, the molecular weight of this polyamic acid was Mn=14120, Mw=31210.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

To provide a liquid crystal aligning agent, a liquid crystal aligning film, and a liquid crystal display element for obtaining an alignment film suitable for photo-alignment, which does not generate bright spots even in negative type liquid crystals and can obtain good image sticking characteristics. A liquid crystal aligning agent, which contains a polyimide precursor selected from a structural unit represented by formula (1) and a structural unit represented by formula (2) and the imidization of the polyimide precursor At least one polymer (A) in the group consisting of polymers. The definitions of the symbols in the formula are as described in the specification.

Description

technical field [0001] The present invention relates to a liquid crystal aligning agent suitable for photo-alignment treatment, a liquid crystal aligning film obtained from the liquid crystal aligning agent, and a liquid crystal display element using the liquid crystal aligning film. Background technique [0002] In liquid crystal display elements used in liquid crystal televisions, liquid crystal displays, etc., a liquid crystal aligning film for controlling the alignment state of liquid crystals is usually provided in the element. As the liquid crystal aligning film, a liquid crystal aligning agent mainly composed of a polyimide precursor such as polyamide acid and a solution of soluble polyimide is applied to a glass substrate and fired. Polyimide-based liquid crystal alignment film. According to the most popular method in the industry, the liquid crystal aligning film is formed on the surface of the polyimide-based liquid crystal aligning film on the electrode substrate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02F1/1337
CPCG02F1/1337C09K19/56C08L79/08C08G73/1046
Inventor 松本欣也桥本淳作本直树
Owner NISSAN CHEM CORP