Process for titanium alloy combined casting

A titanium alloy and process technology, which is applied in the process field of titanium alloy composite casting, can solve the problems of low service life of connecting parts and the like

Active Publication Date: 2019-11-22
LONGNAN XINJING TITANIUM IND CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a titanium alloy combined casting process, which solves the problem of low service life of the connecting part between the titanium alloy casting and the counterweight, and can also set the counterweight embedded in the integral molding The interior of the titanium alloy casting, and even if the casting and the insert are poorly fused, the strength and life of the titanium alloy casting will not be reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for titanium alloy combined casting
  • Process for titanium alloy combined casting
  • Process for titanium alloy combined casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0056] The technical solutions of the present invention will be further described below in conjunction with the accompanying drawings and through specific implementation methods.

[0057] Wherein, the accompanying drawings are only for illustrative purposes, showing only schematic diagrams, rather than physical drawings, and should not be construed as limitations on this patent; in order to better illustrate the embodiments of the present invention, some parts of the accompanying drawings will be omitted, Enlargement or reduction does not represent the size of the actual product; for those skilled in the art, it is understandable that certain known structures and their descriptions in the drawings may be omitted.

[0058] In the drawings of the embodiments of the present invention, the same or similar symbols correspond to the same or similar components; , "inner", "outer" and other indicated orientations or positional relationships are based on the orientations or positional ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of titanium alloy casting, in particular to a process for titanium alloy combined casting. The process includes the following steps of preparing of a balance weightpart; preparing of an insert; assembling of the insert; pressing of a wax pattern; preparing of a shell; pouring; and cutting. According to the process, the problem that the service life of the connecting portion between a titanium alloy casting and a balance weight is short is solved, the balance weight can be arranged in the integrally-formed titanium alloy casting in an embedded manner, and even though the casting and the insert are in incomplete fusion, the strength of the titanium alloy casting cannot be reduced and the service life of the titanium alloy casting cannot be shortened.

Description

technical field [0001] The invention relates to the field of titanium alloy casting, in particular to a titanium alloy combined casting process. Background technique [0002] Casting refers to the liquid forming process of metal materials. The molten metal is poured, injected or sucked into the cavity of the mold, and after solidification, it becomes a casting with a certain shape and performance. Cast titanium alloy refers to the titanium alloy used to cast into castings of a certain shape, and most of the deformed titanium alloys have good casting properties. [0003] Titanium castings are mostly used in vacuum shell solidification furnaces and graphite castings. Compared with deformed alloys of the same composition, their strengths are basically equal, but their plasticity and fatigue properties are about 40% to 50% lower, while the fracture toughness is slightly better. Most titanium castings are stabilized annealed. [0004] Due to the light specific gravity of titan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C9/04B22C7/02B22D19/16
CPCB22C7/02B22C9/04B22D19/16
Inventor 谢建周建林谢宝山王康
Owner LONGNAN XINJING TITANIUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com