A kind of modified asphalt material and preparation method thereof
A modified asphalt and modified technology, applied in building thermal insulation materials, building components, buildings, etc., can solve problems such as poor performance of modified asphalt materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] First, prepare KH-550 modified stone powder for later use.
[0034] Heat stone powder with a particle size of less than 0.2mm to 200°C, add KH-550, stir at a speed of 70rpm, and stir for 0.5h. The weight ratio of stone powder to KH-550 is 20, and it is used after drying.
[0035] Second, prepare the modified asphalt material:
[0036] (1) Take raw materials by weight, 100 parts of matrix pitch, 5 parts of rock pitch, 5 parts of epoxy resin, 24 parts of rubber powder, for subsequent use;
[0037] (2) Heat the base asphalt to a fluid state, raise the temperature to 180°C, and maintain a constant temperature state;
[0038] (3) Add rock asphalt, rubber powder, and epoxy resin to the base asphalt in a constant temperature state, keep the temperature of the system constant, and perform high-speed shearing with a shearing speed of 4000r / min and a shearing time of 2h to obtain a shear mixture material;
[0039] (4) Add 10 parts of KH-550 modified stone powder to the shearin...
Embodiment 2
[0041] First, prepare KH-550 modified stone powder for later use.
[0042] Heat stone powder with particle size less than 0.2mm to 100°C, add KH-550, stirring speed 40rpm, stirring time 1h, weight ratio of stone powder to KH-550 is 15, and use after drying.
[0043] Second, prepare the modified asphalt material:
[0044] (1) raw materials are taken by weight, 140 parts of matrix pitch, 18 parts of rock pitch, 10 parts of epoxy resin, 30 parts of rubber, for subsequent use;
[0045] (2) Heat the base asphalt to a fluid state, raise the temperature to 190°C, and maintain a constant temperature state;
[0046] (3) Add rock asphalt, rubber powder, and epoxy resin to the base asphalt in a constant temperature state, keep the temperature of the system constant, and perform high-speed shearing with a shearing speed of 4000r / min and a shearing time of 2h to obtain a shear mixture material;
[0047] (4) Add 30 parts of KH-550 modified stone powder to the shear mixture, keep the temp...
Embodiment 3
[0049] First, prepare KH-550 modified stone powder for later use.
[0050] Heat stone powder with a particle size of less than 0.2mm to 150°C, add KH-550, stir at a speed of 70rpm, and stir for 1h. The weight ratio of stone powder to KH-550 is 20, and it is used after drying.
[0051] Second, prepare the modified asphalt material:
[0052] (1) Take raw materials by weight, 130 parts of matrix pitch, 12 parts of rock pitch, 6 parts of epoxy resin, 24 parts of rubber powder, for subsequent use;
[0053] (2) Heat the base asphalt to a fluid state, raise the temperature to 180°C, and maintain a constant temperature state;
[0054] (3) Add rock asphalt, rubber powder, and epoxy resin to the base asphalt in a constant temperature state, keep the temperature of the system constant, and perform high-speed shearing with a shearing speed of 4000r / min and a shearing time of 2h to obtain a shear mixture material;
[0055] (4) Add 30 parts of KH-550 modified stone powder to the shear mi...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com