A metal-ceramic and porcelain-fused-to-metal technology, which is applied to dentures and other fields, can solve problems such as waste of manpower and materials, and a large number of air bubbles.

Active Publication Date: 2022-04-01
西安康泰健牙科技术有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, after the metal-fused-to-metal crown is piled with plastic-shading porcelain, it is directly put into the porcelain furnace for sintering. After cooling, it is taken out and dentin porcelain is piled up with plastic, and then it is directly put into the porcelain furnace for sintering. The process of finished metal porcelain teeth, plastic opaque porcelain and dentin porcelain is to apply the paste of plastic opaque porcelain and dentin porcelain on the surface of the tooth; the surface of the finished metal porcelain tooth is often A large number of air bubbles are generated, resulting in rework by blasting porcelain, wasting manpower and materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of metal porcelain tooth
  • A kind of preparation method of metal porcelain tooth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing metal-ceramic teeth, comprising the following steps:

[0024] Step 1: Prepare metal-ceramic inner crown;

[0025] Step 2: After plastic-shading porcelain is deposited on the surface of the inner crown, it is dried at 500°C for 8 minutes and then placed in a porcelain furnace. The furnace is heated from 500°C to 900°C at a heating rate of 60°C / min under vacuum. Vacuum sintering for 15 minutes to obtain metal-ceramic teeth treated at one time;

[0026] Step 3: After one-time treatment of metal-ceramic teeth with plastic dentin porcelain, dry at 500°C for 5 minutes and place in a porcelain furnace. Under vacuum, the furnace is heated from 500°C to 925°C at a rate of 50°C / min. Vacuum sintering at ℃ for 15 minutes to obtain secondary treated metal porcelain teeth;

[0027] Step 4: After trimming the shape of the metal porcelain fused to metal teeth for the second treatment, pile plastic enamel porcelain on the surface and color it. After drying at 50...

Embodiment 2

[0030] A method for preparing metal-ceramic teeth, comprising the following steps:

[0031] Step 1: Prepare metal-ceramic inner crown;

[0032] Step 2: After plastic-shading porcelain is deposited on the surface of the inner crown, it is dried at 515°C for 7 minutes and then placed in a porcelain furnace. The furnace is heated from 515°C to 910°C at a heating rate of 61°C / min under vacuum. Vacuum sintering for 13 minutes to obtain metal-ceramic teeth treated at one time;

[0033] Step 3: After one-time treatment of metal-ceramic-fused-to-metal teeth with plastic dentin porcelain, dry it at 515°C for 4.5 minutes and place it in a porcelain furnace. The furnace is heated from 515°C to Vacuum sintering at 935°C for 13 minutes to obtain secondary treated metal-ceramic teeth;

[0034] Step 4: After trimming the shape of the metal porcelain fused to metal tooth for the second treatment, pile plastic enamel porcelain on its surface and color it. After drying at 515°C for 4.5 minute...

Embodiment 3

[0036] A method for preparing metal-ceramic teeth, comprising the following steps:

[0037] Step 1: Prepare metal-ceramic inner crown;

[0038] Step 2: After plastic-shading porcelain is deposited on the surface of the inner crown, it is dried at 530°C for 6 minutes and then placed in a porcelain furnace. The furnace is heated from 530°C to 905°C at a heating rate of 63°C / min under vacuum. Vacuum sintering for 14 minutes to obtain metal-ceramic teeth treated at one time;

[0039] Step 3: After one-time treatment of metal-ceramic teeth with plastic dentin porcelain, dry at 530°C for 4 minutes and place in a porcelain furnace. Under vacuum, the furnace is heated from 530°C to 928°C at a rate of 52°C / min. Vacuum sintering at ℃ for 14 minutes to obtain secondary treated metal porcelain teeth;

[0040] Step 4: After trimming the shape of the metal porcelain fused to metal teeth for the second treatment, pile plastic enamel porcelain on its surface and color it. After drying at 53...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing metal-ceramic teeth: preparing metal-ceramic inner crowns; stacking plastic-shading porcelain on the surface of the inner crowns, drying and placing them in a porcelain furnace for vacuum sintering at 900-910°C to obtain One-time treatment of metal-ceramic teeth; for first-time treatment of metal-ceramic teeth, plastic dentin porcelain is dried and placed in a porcelain furnace for vacuum sintering at 925-935°C to obtain secondary-treatment metal-ceramic teeth; After the shape of the metal porcelain teeth is trimmed, the enamel porcelain is piled up on the surface and then dried after toning. The dried metal porcelain teeth are placed in a porcelain furnace and sintered at 900-910°C to obtain the metal porcelain teeth. ; It can prepare finished metal-ceramic teeth without air bubbles on the surface.

Description

technical field [0001] The invention belongs to the technical field of denture preparation, and relates to a method for preparing metal-ceramic teeth. Background technique [0002] With the continuous development of science and technology and the improvement of people's living standards, dental restoration materials have attracted more and more attention. Among them, metal-ceramic teeth are restorations made of low-melting porcelain and metal underlying materials, which combine the strength of metal and the beauty of porcelain. It is one of the most widely used restorations in dental fixed restorations today. The traditional preparation process of porcelain-fused-to-metal teeth is mainly as follows: making the inner crown → coating the inner crown with opaque porcelain and heat treatment → shape modification → sintering the ceramic outer crown → dyeing → obtaining the finished metal-ceramic tooth. At present, after the metal-fused-to-metal crown is piled with plastic-shadin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61C13/083C04B35/622C04B35/64
CPCA61C13/083C04B35/622C04B35/64C04B2235/606C04B2235/6581C04B2235/6562C04B2235/6567
Inventor 杨贤利
Owner 西安康泰健牙科技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap