A kind of 125ksi steel grade anti-sulfur oil well pipe and its manufacturing method

A manufacturing method and technology for oil well pipes, which are used in manufacturing tools, furnaces, heat treatment equipment, etc., can solve the problems of lack of sulfur resistance and guarantee, achieve excellent resistance to hydrogen sulfide stress corrosion, reduce manufacturing costs, and high strength. Effect

Active Publication Date: 2021-07-16
BAOSHAN IRON & STEEL CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The publication number is CN103160752A, and the publication date is June 19, 2013. The Chinese patent document entitled "A High-Strength Seamless Steel Tube with Excellent Low-Temperature Toughness and Its Manufacturing Method" discloses a high-strength seamless steel tube with excellent low-temperature toughness. Its composition is: C: 0.15% ~ 0.20%, Si: 0.20% ~ 0.30%, Mn: 0.20% ~ 0.50%, P: ≤0.010%, S: ≤0.003%, Cr: 0.6% ~ 0.8%, Mo: 0.4%~0.7%, Ni: 1.0%~1.4%, Nb: 0.01%~0.035%, Als: 0.01%~0.05%, the Cr-Mo-Ni system is used to obtain the 125ksi steel grade oil well pipe, although the toughness is obtained Significantly improved, the impact energy at -60°C reaches over 40J, but there is no guarantee of sulfur resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 125ksi steel grade anti-sulfur oil well pipe and its manufacturing method
  • A kind of 125ksi steel grade anti-sulfur oil well pipe and its manufacturing method
  • A kind of 125ksi steel grade anti-sulfur oil well pipe and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-6 and comparative example 1-10

[0047] Table 1-1 and Table 1-2 list the mass percent of each chemical element in the 125ksi steel-grade sulfur-resistant oil well pipe of Examples 1-6 and Comparative Examples 1-10.

[0048] Table 1-1. (wt%, the balance is Fe and unavoidable impurities other than P, S, O)

[0049]

[0050]

[0051] Table 1-2. (wt%, the balance is Fe and unavoidable impurities other than P, S, O)

[0052] serial number Ti W Al O N [Cr%]+3[Mo%] Example 1 0.022 0.45 0.06 0.009 0.006 2.7 Example 2 0.032 0.58 0.09 0.005 0.005 2.52 Example 3 0.015 0.21 0.04 0.002 0.007 3.16 Example 4 0.033 0.36 0.07 0.004 0.006 2.92 Example 5 0.019 0.25 0.06 0.007 0.005 3.48 Example 6 0.034 0.41 0.08 0.008 0.002 2.84 Comparative example 1 0.031 0.17

0.06 0.003 0.004 2.7 Comparative example 2 0.028 0.32 0.04 0.002 0.003 2.58 Comparative example 3 0.032 0.36 0.06 0.008 0.006 2.27

Compar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a 125ksi steel grade sulfur-resistant oil well pipe, the mass percentage of chemical elements is: C: 0.20-0.30%, Si: 0.1-0.5%, Mn: 0.2-0.6%, Cr: 0.30-0.70%, Mo : 0.60~1.00%, V: 0.10~0.20%, Nb: 0.01~0.06%, Ti: 0.015~0.035%, W: 0.20~0.60%, Al≤0.1%, N≤0.008%, the balance is Fe and others unavoidable impurities. The invention also discloses a method for manufacturing the above-mentioned 125ksi steel grade sulfur-resistant oil well pipe, which includes the steps of: (1) preparing the pipe blank; (2) piercing and hot rolling the pipe blank to obtain a blank pipe; Controlled cooling; (4) Quenching+tempering: the quenching temperature in the quenching step is Ac3+(30~50°C), where Ac3(°C)=910‑203[C%] 1 / 2 +44.7[Si%]+104[V%]+31.5[Mo%]+13.1[W%], then water quenching, the water quenching speed is ≥30℃ / s; the tempering temperature in the tempering step is 680~700℃ , then air cool.

Description

technical field [0001] The invention relates to an oil well pipe and a manufacturing method thereof, in particular to a sulfur-resistant oil well pipe and a manufacturing method thereof. Background technique [0002] With the increasing depletion of oil and natural gas, the exploitation and development of oil and gas are developing towards deep wells and ultra-deep wells. Correspondingly, the environment of oil and gas wells has higher pressure, higher temperature and higher corrosiveness, especially the Hydrogen sulfide corrodes the medium, which puts forward higher requirements for the strength and hydrogen sulfide stress corrosion resistance of oil well pipe materials. [0003] In the American Petroleum Institute Standard Casing and Tubing Specifications (API Spec 5CT), the existing standardized sulfur-resistant pipe steel grades have yield strengths of 80ksi (that is, 551MPa), 90ksi (that is, 620MPa), and 95ksi (that is, 655MPa) And 110ksi (that is, 758MPa), and the sul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/22C22C38/24C22C38/26C22C38/28C22C38/06C21D8/10
CPCC22C38/02C22C38/04C22C38/22C22C38/24C22C38/26C22C38/28C22C38/06C21D8/105C21D8/10C21D9/08
Inventor 罗明刘耀恒张忠铧齐亚猛
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap