A thermal separation process of low-grade hydromagnesite ore
A low-grade hydromagnesite technology, applied in solid separation, chemical instruments and methods, wet separation, etc., can solve the problems of poor sorting effect, poor dispersion, large dust, etc., and achieve good impurity removal effect, Easy drying and good dispersibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] Thermal separation process of low-grade hydromagnesite ore, 30g hydromagnesite sample is placed in a porcelain crucible and placed in a box-type resistance furnace, at a temperature of 900°C (850°C, 880°C, 900°C, 920°C, Corresponding tests were carried out at 950°C, and the effect of 900°C was the best for this sample), and the hydromagnesite was roasted and kept for 3 hours (160min, 190min, 200min were selected for the holding time between 160-200min, and the best effect was 3h) , to obtain 13.21g of hydromagnesite light-burned magnesium oxide powder, and the loss on ignition rate was 55.96%. The lightly burned magnesia powder after hydromagnesite roasting is placed in a 60-mesh (0.25mm) sieve, or a 65-mesh sieve, and sieved with absolute ethanol as a wet sieving medium. After the sieving is completed, the product on the sieve is dried, weighed, and sampled for testing. Finally, 9.36g of light-burned magnesia product was obtained, with a yield of 70.78%, and the purif...
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap