A kind of high temperature pin-pht piezoelectric ceramics and preparation method thereof
A technology of PIN-PHT and piezoelectric ceramics, applied in the field of high-temperature PIN-PHT piezoelectric ceramics and its preparation, can solve the problems of low Curie temperature, limited working temperature range, weak piezoelectric performance, etc., and achieve low preparation cost , Facilitate the effect of mass production
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0033] A preparation method of high-temperature PIN-PHT piezoelectric ceramics, comprising the following steps:
[0034] Step 1, put In 2 o 3 Powder and Nb 2 o 5 The powder is ball milled, dried, and calcined in sequence to obtain InNbO 4 Precursor powder;
[0035] Specifically follow the steps below:
[0036] Step 1.1, put In 2 o 3 Powder and Nb 2 o 5 The powder is weighed and mixed according to the molar ratio of 1:1 to form a mixed powder;
[0037] Step 1.2, the mixed powder obtained in step 1.1 is subjected to ball milling and drying in turn to obtain a mixed dry powder; the mixed powder and zirconia balls are added to the ball milling tank together and absolute ethanol is added to the ball milling tank as The ball milling medium is used for ball milling treatment. Wherein, the time of ball milling is 10h; the consumption of dehydrated alcohol is: every gram of powder material to be ball milled will add 1ml of dehydrated ethanol, the mass ratio of ball to materi...
Embodiment 2
[0054] A preparation method of high-temperature PIN-PHT piezoelectric ceramics, comprising the following steps:
[0055] Step 1, put In 2 o 3 Powder and Nb 2 o 5 The powder is ball milled, dried, and calcined in sequence to obtain InNbO 4 Precursor powder;
[0056] Specifically follow the steps below:
[0057] Step 1.1, put In 2 o 3 Powder and Nb 2 o 5 The powder is weighed and mixed according to the molar ratio of 1:1 to form a mixed powder;
[0058] Step 1.2, the mixed powder obtained in step 1.1 is subjected to ball milling and drying in turn to obtain a mixed dry powder; the mixed powder and zirconia balls are added to the ball milling tank together and absolute ethanol is added to the ball milling tank as The ball milling medium is used for ball milling treatment. Wherein, the time of ball milling is 10h; the consumption of dehydrated alcohol is: every gram of powder material to be ball milled will add 1ml of dehydrated ethanol, the mass ratio of ball to materi...
Embodiment 3
[0075] A preparation method of high-temperature PIN-PHT piezoelectric ceramics, comprising the following steps:
[0076] Step 1, put In 2 o 3 Powder and Nb 2 o 5 The powder is ball milled, dried, and calcined in sequence to obtain InNbO 4 Precursor powder;
[0077] Specifically follow the steps below:
[0078] Step 1.1, put In 2 o 3 Powder and Nb 2 o 5 The powder is weighed and mixed according to the molar ratio of 1:1 to form a mixed powder;
[0079] Step 1.2, the mixed powder obtained in step 1.1 is subjected to ball milling and drying in turn to obtain a mixed dry powder; the mixed powder and zirconia balls are added to the ball milling tank together and absolute ethanol is added to the ball milling tank as The ball milling medium is used for ball milling treatment. Wherein, the time of ball milling is 10h; the consumption of dehydrated alcohol is: every gram of powder material to be ball milled will add 1ml of dehydrated ethanol, the mass ratio of ball to materi...
PUM
Property | Measurement | Unit |
---|---|---|
piezoelectric charge coefficient | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Curie point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com