A polyurethane waterproof, waterproof and moisture-permeable membrane technology, which is applied in the field of waterproof and moisture-permeable membrane materials, can solve the problems of small pore size of waterproof and moisture-permeable membranes, and achieve the effects of improving mechanical strength, good compatibility, and enhancing moisture absorption performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0032] The preparation method of the titanium dioxide porous microspheres is as follows:
[0033] A certain amount of cellulose triacetate was dissolved in dimethylacetamide, and magnetically stirred at 60°C for 1 hour until uniform. A certain amount of tetrabutyl titanate is dissolved in a mixed solution of dimethylacetamide and glacial acetic acid, and magnetically stirred at 25°C for 1 hour until uniform. The above solutions were mixed, stirred at room temperature for 3 hours, and then placed in an oven at -10°C for 30 minutes. A large amount of ethanol was added to the solution to extract dimethylacetamide and glacial acetic acid, and the extraction was continued for 5 times. The remaining samples were freeze-dried for 48 hours to obtain cellulose triacetate / titanium dioxide composite porous microspheres. The composite porous microspheres were put into a certain amount of 0.5% NaOH ethanol solution to hydrolyze for 24 hours, then washed with distilled water to neutrality, a...
Example Embodiment
[0041] Example 1
[0042] The polyurethane waterproof and moisture-permeable membrane is mainly made of the following components: 25 parts of polyurethane resin, 72 parts of organic solvent, 2 parts of pore former, 1 part of inorganic filler.
[0043] The polyurethane resin adopts the JF-S-WV7025 model product of Zhejiang Huafeng Synthetic Resin Co., Ltd.;
[0044] The raw materials of the polyurethane resin include polypolyol, and polyethylene glycol accounts for 20% of the mass of the polypolyol;
[0045] The organic solvent is a mixed solution of N,N-dimethylformamide, ethyl acetate and dimethyl carbonate, and the mass ratio is 6:3:1;
[0046] The pore-forming agent is titanium dioxide, aluminum oxide, and zirconium oxide porous microspheres, the material ratio is 5:3:2, and the average pore diameter is 15 μm;
[0047] The inorganic filler is modified by a silane coupling agent, the inorganic filler is organic montmorillonite, kaolin, carbon nanotubes, and the mass ratio is 3:5:2, and...
Example Embodiment
[0052] Example 2
[0053] The polyurethane waterproof and moisture-permeable membrane is mainly made of the following components: 25 parts of polyurethane resin, 74 parts of organic solvent, 0.5 part of pore former, 0.5 part of inorganic filler.
[0054] The polyurethane resin adopts the JF-S-WV7025 model product of Zhejiang Huafeng Synthetic Resin Co., Ltd.;
[0055] The raw material of the polyurethane resin includes polypolyol, and polyethylene glycol accounts for 20% of the mass of the polypolyol;
[0056] The organic solvent is a mixed solution of N,N-dimethylformamide, ethyl acetate and dimethyl carbonate, and the mass ratio is 6:3:1;
[0057] The pore-forming agent is titanium dioxide, aluminum oxide, and zirconium oxide porous microspheres, the material ratio is 5:3:2, and the average pore diameter is 1 μm;
[0058] The inorganic filler is modified by a silane coupling agent, the inorganic filler is organic montmorillonite, kaolin, carbon nanotubes, and the mass ratio is 3:5:2, a...
PUM
Property | Measurement | Unit |
---|---|---|
Average pore size | aaaaa | aaaaa |
Average pore size | aaaaa | aaaaa |
Average pore size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap