Soft tissue adhesive with antibacterial and hemostatic functions
An adhesive and soft tissue technology, used in surgical adhesives, applications, medical science, etc., can solve the problems of insufficient adhesive strength and single function, and achieve the effect of rapid hemostasis, convenient and safe application, and good fluidity.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] An adhesive for soft tissue with antibacterial and hemostatic effects based on polysaccharide and hyperbranched polypeptide, which is composed of the following raw materials by mass percentage: oxidized carboxymethyl cellulose 25% and hyperbranched polypeptide polyethylene glycol graft copolymer 25%, the balance is phosphate buffered saline.
[0032] The molecular weight of the oxidized carboxymethyl cellulose is 250,000, and the degree of deacetylation is 90%.
[0033] The hyperbranched polypeptide in the hyperbranched polypeptide polyethylene glycol graft copolymer is a lysine three-generation peptide dendrimer, and the molecular weight of the polyethylene glycol terminated by amino groups at both ends is 2000.
[0034] The mass ratio of the oxidized carboxymethyl cellulose and the hyperbranched polypeptide polyethylene glycol graft copolymer is 1:1.
[0035] The use temperature of the adhesive for soft tissue is room temperature, and the use pH is 7.2-7.5.
Embodiment 2
[0037] An adhesive for soft tissue with antibacterial and hemostatic effects based on polysaccharide and hyperbranched polypeptide, which is composed of the following raw materials by mass percentage: oxidized carboxymethyl cellulose 25% and hyperbranched polypeptide polyethylene glycol graft copolymer 25%, the balance is phosphate buffered saline.
[0038] The molecular weight of the oxidized carboxymethyl cellulose is 250,000, and the degree of deacetylation is 90%.
[0039] The hyperbranched polypeptide in the hyperbranched polypeptide polyethylene glycol graft copolymer is a lysine three-generation peptide dendrimer, and the molecular weight of the polyethylene glycol terminated by amino groups at both ends is 2000.
[0040] The mass ratio of the oxidized carboxymethyl cellulose and the hyperbranched polypeptide polyethylene glycol graft copolymer is 1:2.
[0041] The use temperature of the adhesive for soft tissue is room temperature, and the use pH is 7.2-7.5.
Embodiment 3
[0043] The present embodiment is the preparation method of the adhesive for soft tissue of embodiment 1, comprising the following steps:
[0044] (1) at room temperature, the oxidized carboxymethyl cellulose and the hyperbranched polypeptide polyethylene glycol graft copolymer are respectively dissolved in the phosphate buffered saline of pH 7.2-7.5 to prepare a solution of 25g / L;
[0045] (2) The oxidized carboxymethyl cellulose and the hyperbranched polypeptide polyethylene glycol graft copolymer solution obtained in step (1) were loaded into a double-barreled syringe respectively, uniformly mixed with a mass ratio of 1:1, and then applied to the wound At room temperature, through the Schiff base reaction, a soft tissue adhesive with both antibacterial and hemostatic effects is obtained at room temperature, which firmly and lastingly adheres to the wound surface.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com