High-strength steel plate and manufacturing method thereof

A technology of high-strength steel plate and manufacturing method, applied in the direction of manufacturing tools, furnaces, heat treatment equipment, etc., can solve problems such as high cost, and achieve the effect of excellent ductility and bendability

Active Publication Date: 2022-03-22
JFE STEEL CORP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The technology described in Patent Document 2 has the problem of having to perform rolling twice, resulting in high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength steel plate and manufacturing method thereof
  • High-strength steel plate and manufacturing method thereof
  • High-strength steel plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0082] Hereinafter, the action and effect of the high-strength steel sheet and its manufacturing method of the present invention will be described using examples.

[0083] Steels having the composition shown in Table 1 were melted to produce thin slabs with a thickness of 20 mm. These thin slabs were hot-rolled under the conditions shown in Table 2. The obtained hot-rolled sheets were pickled with hydrochloric acid and cold-rolled at the rolling ratio shown in Table 2 to manufacture cold-rolled steel sheets with a thickness of 0.2 mm. It should be noted that Ti: 0.001%, B: 0.0001%, and Nb: 0.001% in steel type O in Table 1 are unavoidable components mixed.

[0084] Next, the above-mentioned cold-rolled steel sheets were subjected to heating, annealing holding, cooling, and holding after cooling under the heat treatment conditions shown in Table 2 to obtain product steel sheets. The holding after cooling was stopped was performed in a temperature range from the cooling stop t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention provides a high-strength steel plate having excellent ductility and bendability and having a TS of 500 MPa or more, especially a high-strength thin steel plate for cans with a plate thickness ranging from 0.1 to 0.8 mm. The above-mentioned high-strength steel sheet has a composition containing C: 0.03% to 0.15%, Si: 0.01% to 0.05%, Mn: more than 0.6% to 1.5%, P: 0.025% or less, S: 0.02% or less, Al : 0.01% to 0.10%, N: 0.0005% to 0.0100%, Ti: 0.005% to 0.020%, B: 0.0005% to 0.0100%, and Nb: 0.0050% to 0.0200%, and the rest is iron and unavoidable impurities; It has a metal structure including 85% or more of ferrite and 1% to 10% of martensite in an area ratio, and the ratio of the grain size of the martensite is 5 μm or less and 2 μm or less is 80% or more.

Description

technical field [0001] The present invention relates to a high-strength steel sheet having excellent ductility and bendability, for example, a tensile strength (TS) of 500 MPa or more, which is particularly suitable for a container material, and a method for producing the same. Background technique [0002] In recent years, in order to reduce the cost of steel sheets for cans, thickness reduction of high-strength steel sheets has been progressing. Specifically, studies have been made on the use of high-strength thin steel sheets having a TS of 500 MPa or more for tanks. [0003] Here, generally, when the strength of the steel sheet is increased, there is a problem that the workability is lowered. For example, in a steel sheet used for a tab, it is necessary to have both the strength that the tab itself does not bend when the can is opened, and the workability, especially the bendability, when it is processed into a tab. In addition, the ring part of the pull tab is a part ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C21D9/46C22C38/14C22C38/54
CPCC21D9/46C22C38/00C22C38/14C22C38/54C22C38/02C22C38/12C22C38/04C21D8/0236C22C38/32C22C38/28C21D6/005C22C38/001C21D6/004C22C38/002C22C38/06C21D8/0205C22C38/26C21D8/0226C21D8/0263C21D6/008C21D2211/005C21D2211/008
Inventor 椎森芳惠斋藤勇人假屋房亮小岛克己
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com