Steel slag grinding aid enhancer and preparation method thereof

A grinding aid and steel slag technology, applied in the field of steel slag grinding aid and preparation, can solve the problems of poor economy, poor wearability of steel slag, high energy consumption, etc., achieve excellent overall performance and improve overall utilization rate effect

Inactive Publication Date: 2020-04-28
杭州斯曼特建材科技有限公司
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with limestone, fly ash and slag, the grindability of steel slag is very poor, the energy consumption required for grinding is large, and the economy is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A preparation method of a steel slag grinding aid, comprising the steps of:

[0020] (1) Put an appropriate amount of glacial acetic acid into the reaction kettle, put triethanolamine and glycerin into the kettle at a ratio of 1:1, heat to 100°C, and prepare the binary core component.

[0021] (2) Take 20 parts of binary core components, 10 parts of triisopropanolamine, 5 parts of ethylene glycol, 25 parts of urea, 40 parts of deionized water, and 2 parts of calcium hydroxide, and put them into the stirring tank and stir evenly That is the finished product.

Embodiment 2

[0023] A preparation method of a steel slag grinding aid, comprising the steps of:

[0024] (1) Put an appropriate amount of glacial acetic acid into the reaction kettle, put triethanolamine and glycerin into the kettle at a ratio of 2:1, heat to 100°C, and prepare the binary core component.

[0025] (2) Take 20 parts of binary core components, 10 parts of triisopropanolamine, 5 parts of ethylene glycol, 25 parts of urea, 40 parts of deionized water, and 2 parts of calcium hydroxide, and put them into the stirring tank and stir evenly That is the finished product.

Embodiment 3

[0027] A preparation method of a steel slag grinding aid, comprising the steps of:

[0028] (1) Put an appropriate amount of glacial acetic acid into the reaction kettle, put triethanolamine and glycerin into the kettle at a ratio of 1:2, heat to 100°C, and prepare the binary core component.

[0029] (2) Take 20 parts of binary core components, 10 parts of triisopropanolamine, 5 parts of ethylene glycol, 25 parts of urea, 40 parts of deionized water, and 2 parts of calcium hydroxide, and put them into the stirring tank and stir evenly That is the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a steel slag grinding aid enhancer and a preparation method thereof. According to the technical scheme, the steel slag grinding aid enhancer is characterized by comprising thefollowing raw materials in parts by weight: 10-20 parts of a binary core component, 10-20 parts of triisopropanolamine, 5-10 parts of ethylene glycol, 10-25 parts of urea, 25-50 parts of deionized water and 1-3 parts of calcium hydroxide, wherein the binary core component is prepared from triethanolamine and glycerol in a ratio of (1-9): 3. The steel slag grinding aid enhancer can improve the grindability of steel slag, effectively improve the steel slag grinding efficiency, save energy and reduce consumption; therefore, the preparation method provided by the invention has the characteristicsof simple process and convenience in manufacturing.

Description

technical field [0001] The invention relates to a steel slag grinding aid enhancer and a preparation method thereof. Background technique [0002] At present, my country's iron and steel industry is developing at a high speed, and has become the world's largest steel production and consumption country, with steel output accounting for about 1 / 5 of the world's steel output. Like granulated blast furnace slag, steel slag is also a waste slag produced in the steelmaking process, and its emission is about 15%-20% of steel production. Statistics show that the steel slag accumulated in my country over the years has reached more than 300 million tons. If it is not treated and comprehensively utilized, steel slag will occupy more and more land, pollute the environment, cause waste of resources, and affect the sustainable development of the iron and steel industry. therefore. How to improve the utilization rate of steel slag has become a hot issue of common concern in the iron and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/12C04B103/52
CPCC04B40/0039C04B2103/52C04B24/122C04B24/02C04B24/126C04B22/064
Inventor 柳玉强甘丽华
Owner 杭州斯曼特建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com