A kind of bamboo fiber lunch box uses environment-friendly leak-proof sealing method
A bamboo fiber and lunch box technology, applied in the direction of bonding method, starch adhesive, adhesive type, etc., can solve the problems of environmental pollution, spillage and other problems of disposable lunch box waste, and achieve large-scale promotion and use Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] The bamboo fiber lunch box of the present embodiment comprises the following steps with the environmental protection leak-proof sealing method:
[0020] The bamboo fiber lunch box includes a box body processed from bamboo and a lid matched with the box body;
[0021] Step 1. Mix and stir the potato starch and water to form a starch emulsion, then add the starch emulsion into the gelatinization tank, and then feed steam into the gelatinization tank to heat the starch emulsion to a temperature of 60°C, and keep it warm while stirring 2.5h to obtain starch slurry; the mass content of potato starch in the starch emulsion is 40%;
[0022] Step 2, apply the starch slurry obtained in step 1 on the surrounding edges of the inner surface of the lid, the thickness of the coated starch slurry is 0.15mm, and then the lid is processed under the condition of 165 ° C. The drying process of 2min forms the pregelatinized starch film on the inner surface of lid then;
[0023] Step 3. A...
Embodiment 2
[0025] The bamboo fiber lunch box of the present embodiment comprises the following steps with the environmental protection leak-proof sealing method:
[0026] The bamboo fiber lunch box includes a box body processed from bamboo and a lid matched with the box body;
[0027] Step 1. Mix potato starch and water to form a starch emulsion, then add the starch emulsion into the gelatinization tank, and then feed steam into the gelatinization tank to heat the starch emulsion to a temperature of 55°C, and keep it warm while stirring 3h, obtain starch slurry; the mass content of potato starch in the starch emulsion is 30%;
[0028] Step 2, apply the starch slurry obtained in step 1 to the surrounding edges of the inner surface of the lid, the thickness of the coated starch slurry is 0.3mm, and then the lid is subjected to 3min under the condition of 150°C. drying process, then form a pregelatinized starch film around the edge of the inner surface of the lid;
[0029] Step 3. After t...
Embodiment 3
[0031] The bamboo fiber lunch box of the present embodiment comprises the following steps with the environmental protection leak-proof sealing method:
[0032] The bamboo fiber lunch box includes a box body processed from bamboo and a lid matched with the box body;
[0033] Step 1. Mix and stir the potato starch and water to form a starch emulsion, then add the starch emulsion into the gelatinization tank, and then feed steam into the gelatinization tank to heat the starch emulsion to a temperature of 65°C, and keep it warm while stirring 2h, obtain starch slurry; the mass content of potato starch in the starch emulsion is 50%;
[0034] Step 2, apply the starch slurry obtained in step 1 on the inner surface of the box cover, the thickness of the coated starch slurry is 0.01mm, and then cover the box cover at 180 ° C for 1 min Drying, then forming a pregelatinized starch film at the periphery of the inner surface of the lid;
[0035] Step 3. After the food is installed in the...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com