Archaistic ivory white ceramic censer and preparation process thereof

A preparation process and ivory white technology, applied in the field of ceramic products, can solve the problems of easy blackening of incense burners, affecting use, etc., and achieve the effects of easy cleaning, fine ceramics, and convenient use.

Pending Publication Date: 2020-08-07
泉州市万虔堂艺术陶瓷有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The incense burner is one of the traditional shapes of Dehua white porcelain, but the surface of the white porcelain is smooth and clean. After the known incense burner is used, the incense ash will deposit on the surface of the incense burner, which will cause the incense burner to be easily blackened. Especially the ivory white surface has a high finish and needs to be cleaned frequently. Affect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation process of the above antique ivory white ceramic incense burner, the specific steps are as follows:

[0035] Step 1, weighing the ingredients according to the raw material formula of the green body to make the incense burner green body;

[0036] Step 2, the raw material formula of antique ivory white glaze is weighed batching, makes antique ivory white glaze;

[0037] Step 3, applying antique ivory white glaze on the surface of the incense burner body;

[0038] Step 4. Wait for the incense burner body with antique ivory white glaze to dry, put it into the kiln, and fire it through four-stage variable temperature control. The firing temperature is 1305-1310°C. The steps of four-stage variable temperature control firing are as follows :

[0039] In the low temperature stage, the temperature in the kiln rises from normal temperature to 300°C, and the kiln firing time is 1-2 hours;

[0040] In the uniform heating stage, the temperature in the kiln is rais...

specific Embodiment 1

[0049] The antique ivory white ceramic incense burner is characterized in that it includes an incense burner body, an antique ivory white glaze layer arranged outside the incense burner body, and a vacuum coating layer is arranged outside the ivory white glaze layer, and the thickness of the vacuum coating layer is 0.3mm;

[0050] The antique ivory white glaze has the following parts by weight: 42 parts of raw ore kaolin, 22 parts of feldspar, 13 parts of plant ash, 8 parts of quartz, 5 parts of clay, 7 parts of limestone, and 3 parts of nano water, wherein the raw ore kaolin includes Longyan kaolin 16 parts, 9 parts of Dehua kaolin, 18 parts of Brazilian kaolin, plant ash is a combination of pine ash and rice bran ash, the ratio of pine ash and rice bran ash is 3:7; nanometer water contains Al2 o 3 Nanoparticles, after the firing of this antique ivory white glaze, the addition of nanometer water makes the outer layer of the antique ivory white glaze layer form a layer of poro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of ceramic products, and particularly relates to an archaistic ivory white ceramic censer and a preparation process thereof. The archaistic ivory white ceramic censer comprises a censer green body and an archaistic ivory white glaze layer arranged outside the censer green body, and the archaistic ivory white glaze is prepared from strictly proportioned raw ore kaolin, feldspar, plant ash, quartz, clay, limestone powder, nano water and other raw materials. The use of the traditional Dehua kaolin is reduced through the combination of the raw materials; the traditional Dehua kaolin is replaced by the composition; and meanwhile, the effect closest to the antique ivory white ceramic is achieved by adding the plant ash, the ceramic is fine, smooth, compact, mild and light tooth yellow, the antique ivory white ceramic censer is not prone to adhering to oily soot, and therefore the antique ivory white ceramic censer has the performance of being not prone to contamination and easy to clean, and is durable and convenient to use.

Description

technical field [0001] The invention belongs to the field of ceramic products. Specifically, the invention relates to an antique ivory white ceramic incense burner and a preparation process thereof. Background technique [0002] Dehua white porcelain originated in the Song and Yuan Dynasties, became popular in the Ming Dynasty, and was extended to the early Qing Dynasty. It has a unique style in the white porcelain system in my country and occupies an important position in the history of ceramic development. Ivory white porcelain is one of the most distinctive and well-known varieties of Dehua white porcelain. It is a treasure that was widely used in Dehua white porcelain in the Ming Dynasty. Ivory, hence the name ivory white. The incense burner is one of the traditional shapes of Dehua white porcelain, but the surface of the white porcelain is smooth and clean. After the known incense burner is used, the incense ash will deposit on the surface of the incense burner, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C03C8/14C03C8/18C04B33/04C04B33/24C04B33/34C04B41/86C04B41/89A47G33/00
CPCC04B41/86C04B41/52C04B41/89C03C8/00C03C8/14C03C8/18C04B33/04C04B33/24C04B33/34A47G33/00C04B41/5022C04B41/5041C04B41/4529C04B41/4533
Inventor 苏跃进
Owner 泉州市万虔堂艺术陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com